EPR法评价奥氏体不锈钢晶间腐蚀敏感性的研究

金维松;郎宇平;荣凡;孙力军

钢铁研究总院

RESEARCH OF EPR ON THE SUSCEPTIBILITY TO INTERGRANULAR ATTACK OF AUSTENITIC STAINLESS STEEL

;;;

钢铁研究总院

全文: PDF(2513 KB)

摘要: 利用电化学动电位再活化（即EPR）法检测了奥氏体不锈钢晶间腐蚀敏感性的程度.研究了不同条件对敏化度的影响，特别是不同敏化时间、敏化温度、扫描速度、溶液温度对奥氏体不锈钢晶间腐蚀性能的影响，并与草酸电解浸蚀实验结果进行对比.结果表明：双环EPR法能定量、定性的检测不锈钢的晶间腐蚀敏感性.对304LNSS而言，敏化时间越长，温度越高，其晶间腐蚀敏感性越强.扫描速度越快，溶液温度越低，同一材料的Ra值越小.EPR法与草酸电解浸蚀试验结果相吻合.

关键词 ：奥氏体不锈钢, EPR, 晶间腐蚀

Abstract：The susceptibility to intergranular attack (IGA) of austenitic stainless steel were studied by electrochemical potentiokinetic reactivation(EPR).The influences to IGA under different condition were analyzed,especially,through changing the sensitization time and temperature,scan rate and solution temperature.The results were compared with the result of the oxalic acid etching test.The study shows that the double loop EPR (DL-EPR) method is appropriate for evaluating the susceptibility to IGA.For 304LNSS the longer the sensitization time or the higher the sensitization temperature,the more serious the IGA.The faster the scan rate or the lower the solution temperature,the less the Ra of same material.EPR method is consistent with the oxalic acid etching test.

Key words： austenitic stainless steel EPR intergranular attack

收稿日期: 2006-08-24

ZTFLH:

O646

通讯作者: 郎宇平 E-mail: langyuping@nercast.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	金维松
	郎宇平
	荣凡
	孙力军
44.8K

引用本文:

金维松; 郎宇平; 荣凡; 孙力军 . EPR法评价奥氏体不锈钢晶间腐蚀敏感性的研究[J]. 中国腐蚀与防护学报, 2007, 27(1): 54-59 .
. RESEARCH OF EPR ON THE SUSCEPTIBILITY TO INTERGRANULAR ATTACK OF AUSTENITIC STAINLESS STEEL. J Chin Soc Corr Pro, 2007, 27(1): 54-59 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2007/V27/I1/54

[1]Chinese Metal Institute.Iron and Steel Thesaurus[M].Hebei:Chi-nese Price Publishing Company,1995(中国金属学会.钢铁辞典[M].河北:中国物价出版社,1995)
[2]Gao Z P,Chen F C,Zhao C J.Various criterion of evaluating suscep-tibility of intergranular corrosion by electrochemical potentiokineticreactivation[J].Sichuan Chemical Engineering and Corrosive Con-trol,1999,2(3):40-44(高中平,陈范才,赵常就.动电位再活化法评价晶间腐蚀敏感性的各种判据[J].四川化工与腐蚀控制,1999,2(3):40-44)
[3]Taboada A,Frank L.Intergranular corrosion in nuclear systems.In-tergranular corrosion in stainless alloys[A].ASTM STP 656[C].Steigerwald R F,Ed.,American Society for Testing and Materials,Philadelphia,Pennsylvania,1978,85
[4]Azar P Majidi,Michael A Streicher.The double loop reactivationmethod for detecting sensitization in AISI 304 stainless steels[J].Corrosion,1984,40(11):584-593
[5]Li S S.Examination of sensitization of austenitic stainless steels bydouble-loop EPR test method[J].Corros.Sci.Prot.Technol.,2000,12(5):288-291(李神速.双回路EPR法测定奥氏体不锈钢的敏化[J].腐蚀科学与防护技术,2000,12(5):288-291)
[6]Wu Y S,Fang Z,et al.The Experimental Method of Corrosion andthe Examinatorial Technology of Corrosion Resistance[M].Beijing:Chemical Industry Press,1996(吴荫顺,方智等.腐蚀试验方法与防腐蚀检测技术[M].北京:化学工业出版社,1996)
[7]Lu S Y,Zhang TK,Kang X F.Stainless Steels[M].Beijing:AtomicEnergy Press,1995(陆世英,张廷凯,康喜范.不锈钢[M].北京:原子能出版社,1995)
[8]Azar P Majidi,Michael A Streicher.Potentiodynamic reactivationmethod for detecting sensitization in AISI 304 and 304L stainlesssteels[J].Corrosion,1984,40(8):393-408
[9]Gang Y M.Corrosion Notebook of Stainless Steels[M].Beijing:Met-allurgy Industry Press,1992(冈毅民.中国不锈钢腐蚀手册[M].北京:冶金工业出版社,1992)
[10]Institute of Chinese Society for Corrosion and Protection.Metal Lo-calized Corrosion[M].Beijing:Chemical Industry Press,1995(中国腐蚀与防护学会.金属的局部腐蚀[M].北京:化学工业出版社,1995)

[1]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[2]	刘辉,邱玮,冷滨,俞国军. 304和316H不锈钢在LiF-NaF-KF熔盐中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 51-58.
[3]	刘希武,赵小燕,崔新安,许兰飞,李晓炜,程荣奇. 304L不锈钢在硝酸-硝酸钠环境中的腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 543-550.
[4]	赵小燕, 刘希武, 崔新安, 于凤昌. 304L不锈钢在稀硝酸环境下的腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 455-462.
[5]	刘丹阳, 汪洁霞, 李劲风, 陈永来, 张绪虎, 许秀芝, 郑子樵. Mg,Ag,Zn微合金化Al-Cu-Li系铝锂合金T6态时效的晶间腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(2): 183-190.
[6]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[7]	刘德强,柯黎明,徐卫平,邢丽,毛育青. 7075厚板铝合金搅拌摩擦焊接头晶间腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 293-299.
[8]	彭新元,周贤良,华小珍. 晶粒尺寸对316LN不锈钢晶间腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2016, 36(1): 25-30.
[9]	许龙, 姚希, 李劲风, 蔡超. 2099铝锂合金晶间腐蚀行为与时效制度的相关性[J]. 中国腐蚀与防护学报, 2014, 34(5): 419-425.
[10]	段振刚, 张乐福, 王力, 徐雪莲, 石秀强. 注锌对316L奥氏体不锈钢氧化膜成分的影响[J]. 中国腐蚀与防护学报, 2014, 34(3): 249-252.
[11]	易雪庆陆永浩陈迎锋. 敏化和固溶处理对核级不锈钢Z3CN20-09M相间腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2013, 33(2): 141-147.
[12]	俞树荣,何燕妮,李淑欣,王璐. 晶粒尺寸对奥氏体不锈钢晶间腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2013, 33(1): 70-74.
[13]	尹开锯，邱绍宇，唐睿，洪晓峰，张乐福，张强. 超级奥氏体不锈钢AL-6XN在超临界水中的腐蚀行为[J]. 中国腐蚀与防护学报, 2012, 32(5): 375-380.
[14]	冯万里,张乐福,马明娟. 轧制变形对690合金特殊晶界比例及耐晶间腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(4): 296-299.
[15]	江克,陈学东,杨铁成,张玮,梁春雷. 典型奥氏体不锈钢高温环烷酸腐蚀行为研究[J]. 中国腐蚀与防护学报, 2012, 32(1): 59-63.

Viewed

Full text

Abstract

Cited

Shared

Discussed