金属材料大气腐蚀破坏的剂量响应函数研究

叶堤;赵大为;张冬保

重庆市环境科学研究院

Dose-response functions for atmospheric corrosion on meatls

;;

重庆市环境科学研究院

全文: PDF(289 KB)

摘要: 利用RAPIDC（发展中国家区域大气污染）腐蚀子项目的最新试验结果，结合灰色关联分析和非线性回归方法，建立了基于大气腐蚀机理的碳钢、Zn、Cu的腐蚀剂量响应函数。结果表明，获得的剂量响应函数能较好的拟合原始试验数据且形式相对简练，适用于区域性的材料大气腐蚀经济损失核算。

关键词 ：金属, 大气腐蚀, 剂量响应函数, 干沉降, 湿沉降

Abstract：Baesd on the database of a corrosion project，which was a sub-project of the international cooperation programme RAPIDC（Regional Air Pollution in Developing Country）， Dose-Response Functions（DRFs） of carbon steel，zinc and copper were set up by the combined methods of grey relation analysis and non-liner regression. The DRFs could reflect the mechanism of atmospheic corrosion by some extent. The results showed that the obtained DRFs well fitted the experimental data and had relative simple expression，therefore they could be used to calculate the economincal loss of material corrosion at regional scale.

Key words： metals atmospheric corrosion Dose-Response Functions dry deposition wet deposition

收稿日期: 2005-07-18

ZTFLH:

TG172.3

通讯作者: 叶堤 E-mail: david0672_cn@sina.com.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	叶堤
	赵大为
	张冬保
44.8K

引用本文:

叶堤; 赵大为; 张冬保 . 金属材料大气腐蚀破坏的剂量响应函数研究[J]. 中国腐蚀与防护学报, 2006, 26(6): 351-354 .

链接本文:

https://www.jcscp.org/CN/Y2006/V26/I6/351

[1]Zhang H X,Guo J L,Zhu J Y,et al.Methods of Multi-Analysis ofSmall Sample Data and Its Application[M].Xi′an:NorthwesternPoly-Technical University Press,2002(张恒喜,郭基联,朱家元等.小样本多元数据分析方法及应用[M].西安:西北工业大学出版社,2002)
[2]Yan C W,He Y F,Lin H C,et al.Atmospheric corrosion of copperat initial stage in air containing sulfur dioxide[J].Chin.J.Nonferr.Met.,2000,10(5):645-648(严川伟,何毓番,林海潮等.铜在含SO2大气中的腐蚀初期规律和机理[J].中国有色金属学报,2000,10(5):645-648)
[3]Han W,Jia W,Wang J,et al.Effect of SO2on corrosion mechanismof A3 steel at dewing environment[J].J.Chin.Soc.Corros.Prot.,2002,22(6):355-358(韩薇,贾薇,汪俊等.凝露状态下SO2对A3钢腐蚀机理的影响[J].中国腐蚀与防护学报,2002,22(6):355-358)
[4]Baedecker P A,Edney E O,Moran P J,et al.Effects of acidic depo-sition on materials[A].NAPAP.SOS/T Report[C].U.S.ASTMNo.19,1989
[5]ISO 9223.Corrosion of Metals and Alloys—Corrosivity of Atmo-spheres—Classification[S].1992
[6]Tidblad J,Mikhailov A A,Kucera V.Model for the prediction ofthe time of wetness from average annual data on relative air humidi-ty and air temperature[J].Protection of Metals,2000,36(6):584-591
[7]Mikhailov A A.Dose-response functions as estimates of the effectsof acid precipitates on materials[J].Protection of Metals,2001,37(4):357-36
[8]Tidblad J,Mikhailov A A,Kucera V.Unified Dose-response func-tions after 8 years of exposure[A].Proceedings of the UN ECEWorkshop on Quantification of Effect of Air Pollutants on Materials[C].Berlin:Umweltbundesamt,1999
[9]Hong N.SPSS for Windows:Windows Tutorial of Statistical Prod-uct and Service Solutions[M].Beijing:Northern Jiaotong Universi-ty Press,2003(洪楠.SPSS for Windows统计产品和服务解决方案教程[M].北京:北方交通大学出版社,2003)
[10]Arrovave C,Morcillo M.The effect of nitrogen oxides in atmo-spheric corrosion of metals[J].Corros.Sci.,1995,37(2):293-305
[11]Sun-Tae Kim,Yasuaki Maeda,Yoshio Tsujino.Assessment of theeffect of air pollution on materials damages in Northeast Asia[J].Atmospheric Environment,2004,38:37-49

[1]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[2]	蒋旭光, 刘晓博. 垃圾焚烧锅炉关键受热面腐蚀研究进展及方向思考[J]. 中国腐蚀与防护学报, 2020, 40(3): 205-214.
[3]	伊红伟, 胡慧慧, 陈长风, 贾小兰, 胡丽华. CO₂环境下油酸咪唑啉对X65钢异种金属焊缝电偶腐蚀的抑制作用研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[4]	刘威, 杜开发, 胡晓宏, 汪的华. 液态金属储能电池中常用液态金属腐蚀研究进展[J]. 中国腐蚀与防护学报, 2020, 40(2): 81-86.
[5]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[6]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[7]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[8]	丁国清,李向阳,张波,杨朝晖,黄桂桥,杨海洋,刘凯吉. 金属材料在天然海水中的腐蚀电位及其变化规律[J]. 中国腐蚀与防护学报, 2019, 39(6): 543-549.
[9]	邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[10]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[11]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[12]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[13]	周勇, 左禹, 闫福安. 缓蚀性组分对金属小孔腐蚀的缓蚀作用与机制[J]. 中国腐蚀与防护学报, 2017, 37(6): 487-494.
[14]	夏大海, 宋诗哲, 王吉会, 高志明, 胡文彬. 食品包装用镀锡薄钢板的腐蚀机理研究进展[J]. 中国腐蚀与防护学报, 2017, 37(6): 513-518.
[15]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.

Viewed

Full text

Abstract

Cited

Shared

Discussed