储罐底板外侧阴极保护电位分布的数值模拟

杜艳霞;张国忠

中国石油大学（华东）油气储运专业

Numerical modeling of Cathodic Protection Potential Distribution on the Exterior of Tank Bottom

;

中国石油大学（华东）油气储运专业

全文: PDF(262 KB)

摘要: 建立了储罐底板外侧阴极保护电位分布的数学模型，利用FLUENT软件模拟了罐底外侧的阴极保护电位分布；研究了土壤电阻率、罐底的极化特性、阳极的埋深、与罐距离及数量等因素对罐底外侧阴极保护电位分布的影响，并将模拟结果与实测数据进行了对比。结果吻合较好。

关键词 ：罐底, 阴极保护, 电位分布, 数值模拟, 影响因素

Abstract：The mathematical nodel of cathodic protection potential distribution on the exterior of tank bottom is established and calculated by using FLUENT software. the effects of soil resistivity, polarization characteristic of tank bottom, depth of anode, distance between anode and tank on cathodic protection potential distribution of tank bottom are studied. Calculated results are compared with measured data and there is good agreement between them.

Key words： tank bottom cathodic protection potential distribution numerical simulation contributing factors

收稿日期: 2005-06-15

ZTFLH:

TE988

通讯作者: 杜艳霞 E-mail: duyanxia0216@sina.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	杜艳霞
	张国忠
44.8K

引用本文:

杜艳霞; 张国忠 . 储罐底板外侧阴极保护电位分布的数值模拟[J]. 中国腐蚀与防护学报, 2006, 26(6): 346-350 .
. Numerical modeling of Cathodic Protection Potential Distribution on the Exterior of Tank Bottom. J Chin Soc Corr Pro, 2006, 26(6): 346-350 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I6/346

[1]Qiu F,Xu N X.Potential distribution on cathodically protected ex-ternal tank bottom[J].J.Chin.Soc.Corros.Prot.,1996,16(1):29-36(邱枫,徐乃欣.钢质贮罐底板外侧阴极保护时的电位分布[J].中国腐蚀与防护学报,1996,16(1):29-36)
[2]Chin D T,Sabde G M.Current distribution and electrochemical en-vironment in a cathodically protected crevice[J].Corrosion,2000,56(3):229-237
[3]Kranc S C,Sagues A A.Detailed modeling of corrosion macrocells onsteel reinforcing in concrete[J].Corros.Sci.,2001,43:1355-1372
[4]DeGiorgi V G,Wimmer S A.Geometric details and modeling accu-racy requirements for shipboard impressed current cathodic protec-tion system modeling[J].Engineering Analysis with Boundary Ele-ments,2005,29:15-28
[5]Riemer D P,Orazem M E.A mathematical model for the cathodicprotection of tank bottoms[J].Corros.Sci.,2005,47:849-868
[6]Sun J B.CP test and results analysis on 20000 m3oil tank[J].Oil&Gas Storage and Transportation,2001,20(1):23-24(孙建斌.20000 m3金属储罐阴极保护试验及效果分析[J].油气储运,2001,20(1):23-24)
[7]Sun J B.Cathodic protection test by Yizheng pump station and theeffects of protection[J].Oil Depot and Gas Station,2001,10(1):31-32(孙建斌.仪征泵站大罐阴极保护试验及保护效果分析[J].石油库与加油站,2001,10(1):31-32)

[1]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[2]	梁毅, 杜艳霞. 交流干扰和阴极保护协同作用下的腐蚀评判标准与机理研究进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 215-222.
[3]	解璇, 刘莉, 王福会. TiO₂的制备及表面修饰工艺对其光电化学阴极保护性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 123-130.
[4]	赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[5]	王贵容,邵亚薇,王艳秋,孟国哲,刘斌. 阴极保护电位对破损环氧涂层阴极剥离的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 235-244.
[6]	廖彤,马峥,李蕾蕾,马秀敏,王秀通,侯保荣. Fe₂O₃/TiO₂纳米复合材料对304不锈钢的光生阴极保护性能[J]. 中国腐蚀与防护学报, 2019, 39(1): 36-42.
[7]	邱萍, 杨连捷, 宋玉, 杨鸿飞. 添加DMF对TiO₂薄膜光生阴极保护性能影响研究[J]. 中国腐蚀与防护学报, 2018, 38(3): 289-295.
[8]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[9]	寇杰, 张新策, 崔淦, 杨宝安. 储罐底板阴极保护电位分布研究进展[J]. 中国腐蚀与防护学报, 2017, 37(4): 305-314.
[10]	王晓霖, 闫茂成, 舒韵, 孙成, 柯伟. 破损涂层下管线钢的交流电干扰腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(4): 341-346.
[11]	王廷勇,马兰英,汪相辰,张海兵,陈凯,闫永贵. 某核电站凝汽器在海水中阴极保护参数的研究及应用[J]. 中国腐蚀与防护学报, 2016, 36(6): 624-630.
[12]	魏木孟,杨博均,刘洋洋,王孝平,姚敬华,高灵清. Cu-Ni合金管海水冲刷腐蚀研究现状及展望[J]. 中国腐蚀与防护学报, 2016, 36(6): 513-521.
[13]	林翠,赵晓斌,张翼飞. 金属材料的空化腐蚀行为及影响因素研究进展[J]. 中国腐蚀与防护学报, 2016, 36(1): 11-19.
[14]	杨霜,唐囡,闫茂成,赵康文,孙成,许进,于长坤. 温度对X80管线钢酸性红壤腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2015, 35(3): 227-232.
[15]	刘在健,王佳,张彭辉,王燕华,张源. 5083铝合金在海水中的腐蚀行为及其阴极保护研究[J]. 中国腐蚀与防护学报, 2015, 35(3): 239-244.

Viewed

Full text

Abstract

Cited

Shared

Discussed