Q235-304L电偶对在Na2S溶液中的电偶腐蚀行为研究

李君;李晓刚;董超芳

北京科技大学材料学院

GALVANIC CORROSION BEHAVIORS OF Q235-304L COUPLE IN Na2S SOLUTION

;;

北京科技大学材料学院

全文: PDF(362 KB)

摘要: 用电化学法和浸泡法研究了Q235-304L电偶对在3种不同浓度的Na2S溶液中的电偶腐蚀行为，用SEM观察试样的表面形貌.结果表明：在3种溶液中Q235钢的阳极过程均为混合控制，而304L的阴阳极过程均为电化学控制；偶接后Q235钢表面阳极金属的溶解过程与阴极过程同时进行，其阳极溶解电流大于电偶电流值；电偶腐蚀效应随阴阳极面积比的增大而增大；随着S2－浓度的升高，电偶对中Q235钢的腐蚀速率减小，电偶腐蚀效应也随之降低.

关键词 ：电偶腐蚀, Q235钢, 304L不锈钢, 阴阳极面积比

Abstract：Galvanic corrosion behaviors of Q235-304L couple with various cathode/anode area ratios in three different concentrations of Na2S solutions were studied by the potentiodynamic polarization curves,galvanic method and immersion test.Surface morphologies of the samples were also analyzed by SEM after rust cleaning.The results showed that:both the cathodic and anodic processes of 304L were controlled by the electrochemical step,while the anodic process of Q235 exhibited an apparent characteristics of activation-diffusion mixed contro l;a cathodic process as well as an anodic process took place on the surface of Q235 after coupled and the dissolution current of Q235 was much more above the galvanic current got by galvanic corrosion method;as the area ratio increases,the galvanic effect increases;and with the elevation of the concentration of S2-,the corrosion rate of Q235 creased,so did the galvanic effect.

Key words： galvanic corrosion Q235 carbon steel 304L stainless steel cathode/anode area ratio

收稿日期: 2004-07-26

ZTFLH:

TG172.2

通讯作者: 李君 E-mail: kylinjune@sina.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李君
	李晓刚
	董超芳
44.8K

引用本文:

李君; 李晓刚; 董超芳 . Q235-304L电偶对在Na2S溶液中的电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2006, 26(5): 308-314 .

链接本文:

https://www.jcscp.org/CN/Y2006/V26/I5/308

[1]Mansfeld F.The relationship between galvanic current and dissolu-tion rates[J].Corrosion,1973,29(10):403-405
[2]Akid R,Mills D J.A comparison between conventional macroscopicand novel microscopic scanning electrochemical methods to evaluategalvanic corrosion[J].Corros.Sci.,2001,43:1203-1216
[3]Abreu C M,Cristoóbal M J,Montemor M F.Galvanic coupling be-tween carbon steel and austenitic stainless steel in alkaline media[J].Electrochi.Acta,2002,47:2271-2279
[4]Tahara Akira,Kodama Toshiaki.Potential distribution measure-ment in galvanic corrosion of Zn/Fe couple by means of Kelvinprobe[J].Corros.Sci.,2000,42:655-673
[5]Varela F E,Kurata Y,Sanada N.The influence of temperature onthe galvanic corrosion of a cast iron-stainless steel couple(predic-tion by boundary element method)[J].Corros.Sci.,1997,39(4):775-788
[6]Zahran R P,Sedahmed F H.Galvanic corrosion of zinc in turbulent-ly moving saline water containing drag reducing polymers[J].Mater.Lett.,1997,31(5):29-33
[7]Huang G Q,Yu C J,Li L S.Study on galvanic corrosion of steelcouples in seawater[J].J.Chin.Soc.Corros.Prot.,2001,21(1):46-53(黄桂桥,郁春娟,李兰生.海水中钢的电偶腐蚀研究[J].中国腐蚀与防护学报,2001,21(1):46-53)
[8]Sun D B,Li T,Yu H Y.Formation and effect of tribo-cell for Fe-Cr alloy[J].Electrochemistry,1998,4(3):307-312(孙冬柏,李涛,俞宏英.铁铬合金摩擦破损微电偶的形成及作用[J].电化学,1998,4(3):307-312)
[9]Zhang X Y,Du Y L.Effect of iron sulfide scale on corrosion behav-ior of UNS G11180 steel in 5%NaCl solution containing H2S[J].Corros.Sci.Prot.Technol.,1997,9(1):19-23(张学元,杜元龙.Fe的硫化物膜对UNS G11180钢在含H2S的NaCl溶液中的腐蚀行为的影响[J].腐蚀科学与防护技术,1997,9(1):19-23)
[10]Mansfeld F.Galvanic interaction between active and passive titani-um[J].Corrosion,1973,29(2):56-58
[11]Mansfeld F.Area relationships in galvanic corrosion[J].Corrosion,1971,27(10):436-442
[12]Bellucci F.Galvanic corrosion between nonmetallic composites andmetals:ⅠEffects of metal and of temperature[J].Corrosion,1991,47(10):808-819
[13]Jiang T,Zuo Y,Xiong J P.Effect of several sulfur containing an-ions on pitting mild steel[J].Corros.Sci.Prot.Technol.,2001,13(5):249-253(姜涛,左禹,熊金平.含S阴离子对低碳钢孔蚀的影响[J].腐蚀科学与防护技术,2001,13(5):249-253)
[14]Ke W,Chen J W.Development of corrosion research for petroleumprocessing industry[J].Petrochem.Corros.Prot.,1997,14(2):1-11(柯伟,陈进伟.炼油工业中腐蚀研究的进展[J].石油化工腐蚀与防护,1997,14(2):1-11)

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	丁清苗, 秦永祥, 崔艳雨. 大气环境中飞机构件的电偶腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 455-462.
[3]	伊红伟, 胡慧慧, 陈长风, 贾小兰, 胡丽华. CO₂环境下油酸咪唑啉对X65钢异种金属焊缝电偶腐蚀的抑制作用研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[4]	白苗苗, 白子恒, 蒋立, 张东玖, 姚琼, 魏丹, 董超芳, 肖葵. H62黄铜/TC4钛合金焊接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 159-166.
[5]	黄宸,黄峰,张宇,刘海霞,刘静. 高强耐候钢焊接接头电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 527-535.
[6]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[7]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[8]	王振华, 白杨, 马晓, 邢少华. 钛合金和铜合金管路电偶腐蚀数值仿真[J]. 中国腐蚀与防护学报, 2018, 38(4): 403-408.
[9]	张新新,高志明,胡文彬,伍志鹏,韩连恒,卢丽花,修妍,夏大海. Q235钢在薄液膜下腐蚀行为与图像信息的相关性研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[10]	刘艳洁,王振尧,王彬彬,曹岩,霍阳,柯伟. 实时监测技术研究薄液膜下电偶腐蚀的机理[J]. 中国腐蚀与防护学报, 2017, 37(3): 261-266.
[11]	赵欣,胡裕龙,董赋,张晓东,王智峤. 湿态电绝缘对电偶腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 175-182.
[12]	郑珉,黄彦良,西方笃,路东柱,张杰,王秀通,温娟,李玉红,刘月妙. Q235钢在甘肃北山地区地下水模拟液及高压实膨润土环境下的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(5): 398-406.
[13]	李阳恒,左禹,唐聿明,赵旭辉. 应变作用下Q235碳钢在NaHCO₃+NaCl溶液中的孔蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(3): 238-244.
[14]	陈文,管春平,杨申明,胡小安. 节节草提取物在盐酸介质中对碳钢的缓蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(2): 177-184.
[15]	黄涛,陈小平,王向东,米丰毅,刘芮,李向阳. pH值对Q235钢在模拟土壤中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(1): 31-38.

Viewed

Full text

Abstract

Cited

Shared

Discussed