中国腐蚀与防护学报  2005, Vol. 25 Issue (6): 373-379     
  综述 本期目录 | 过刊浏览 |
锌及其合金的大气腐蚀研究现状
施彦彦;张昭;张鉴清;曹楚南
浙江大学化学系电化所
Review of Atmospheric Corrosion of Zinc and Zinc alloy
Yanyan Shi;Zhao Zhang;Jianjing Zhang;Chunan Cao
浙江大学化学系电化所
全文: PDF(255 KB)  
摘要: 综述了大气中常见侵蚀性粒子对锌及其合金大气腐蚀的影响机制,重点介绍了几种常用的大气腐蚀研究方法,并比较了各种研究方法的优缺点.同时展望了锌及其合金大气腐蚀研究的方向.
关键词 锌合金大气腐蚀    
Abstract:Electrodeposited zinc and zinc-based alloys are widely used as the protective coatings of metals,and the nature of their atmospheric deterioration is their electrochemical corrsion under thin elecrolyte film.This paper reviews the influence mechnism of several important aggressive particles on the corrosion process of zinc and its alloys,and the main measuremerts usually used in the atmospheric corrosion study and their corresponding merits and limitation.Meanwhile,the prospetive points in future atmospheric corrosion study of zinc and its alloys are brought forward.
Key wordsZinc    Zinc alloy    Atmospheric corrosion
收稿日期: 2004-06-22     
ZTFLH:  TG172  
通讯作者: 施彦彦   
Corresponding author: Yanyan Shi   

引用本文:

施彦彦; 张昭; 张鉴清; 曹楚南 . 锌及其合金的大气腐蚀研究现状[J]. 中国腐蚀与防护学报, 2005, 25(6): 373-379 .
Yanyan Shi, Zhao Zhang, Jianjing Zhang, Chunan Cao. Review of Atmospheric Corrosion of Zinc and Zinc alloy. J Chin Soc Corr Pro, 2005, 25(6): 373-379 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2005/V25/I6/373

[1]Assaf F H,Abd S S,El-Rehiem,et al.PQu Q,Yan C W,Zhang L,et al.Synergismof NaCl and SO2inini-tial atmospheric corrosion of zinc[J].Chin.J.Nonferr.Metal.,2002,12(6):1272-1275(屈庆,严川伟,张蕾等.Zn初期大气腐蚀中NaCl和SO2的协同效应[J].中国有色金属学报,2002,12(6):1272-1275)
[3]El-Mahdy G A.Advanced laboratory study on the atmosphericcorrosion of zinc under thin electrolyte layers[J].Corrosion,2003,59(6):505-510
[4]Baugh L M.Corrosion and polarization characteristics of zinc inneutral-acid media-I.pure zinc in solutions of various sodiumsalts[J].Electrochi m.Acta,1979,24:657-667
[5]Lindstr m R,Svensson J E,Johansson L G.The atmospheric corro-sion of zincinthe presence of NaCl-theinfluence of carbon dioxideandtemperature[J].J.Electrochem.Soc.,2000,147(5):1751-1757
[6]Cramer S D,Carter J P,Linstrom P J,Flinn D R.Environmentaleffects on metallic corrosion products formedin short-termatmo-spheric exposures[J].ACS SymposiumSeries,1986:119-151
[7]Mattsson E.Corrosion:an electrochemical problem[J].Chem.Tech.,1985,15:234-243
[8]Ailor WH.Atmospheric Corrosion[M].New York:John Wiley&Sons Inc.,1982,529-552
[9]German G.Atomspheric Factors Affecting the Corrosion of Engi-neering Metals[M].ASTM,USA:Philadelphia,1978:74-82
[10]Ramanauskas R,Muleshkova L,Maldonado L,Dobrovolskis P.Characterization of the corrosion behaviour of Zn and Zn alloyelectrodeposits:atmospheric and accelerated tests[J].Corros.Sci.,1998,40:401-410
[11]Haynie F H,UphamJ B.Effects of atmospheric sulfur dioxide onthe corrosion of zinc[J].Mater.Perf.,1986,9(8):35-40
[12]Friel J J.Atmospheric corrosion products on Al,Zn and AlZnmetallic coatings[J].Corrosion,1986,42(7):422-426
[13]Munier G B,Psota L A,Reagor B T,et al.Contamination of elec-tronic equipment after an extended urban exposure[J].J.Elec-trochem.Soc.,1980,127(2):265-272
[14]Biestek T,Drys M,Sokolov,et al.Atmospheric corrosion of metal-lic systems.V.Identification of the chemical compoundsinthe cor-rosion products of zinc[J].Prot.Met.,1983,19(5):612-615
[15]Flinn D R,Cramer S D,Carter J P,et al.Materials degradationcaused by acid rain[A].Washington.R.Baboian,Editor.ACSSymposiumSeries,1986:119-151
[16]Falk T,Svensson J E,Johansson L G.The role of carbon dioxideinthe atmospheric corrosion of zinc:a laboratory study[J].J.Elec-trochem.Soc.,1998,145(1):39-44
[17]Lindstr m R,Svensson J E,Johansson L G.The atmospheric cor-rosion of zinc in the presence of NaCl-the influence of carbondioxide and temperature[J].J.Electrochem.Soc.,2000,147(5):1751-1757
[18]Bernard MC,Hugot L A,Philips N.Underpaint corrosion of zinc-coated steel sheet studied by in situ Raman spectroscopy[J].Corros.Sci.,1993,35(5-8):13社,2002,210)
[20]Anderson E A.The Atmospheric Corrosion of Rolled Zinc,in Sym-posiumon Atmospheric Corrosion of Nonferrous Metals[M].STP175,American Society for Testing and Materials,1955,126-134
[21]Sun C,Wu WT,Huang C X,et al.Atmospheric corrosion of zincin Liaoning rural area[J].Mater.Sci.Prog.,1992,6(4):312-314(孙成,吴维,黄春晓等.Zn的乡村大气腐蚀[J].材料科学进展,1992,6(4):312-314)
[22]Svensson J E,Johansson L G.Alaboratory study of the effect of o-zone,nitrogen dioxide and sulfur dioxide on the atmospheric corr-sion of zinc[J].J.Electrochem.Soc.,1993,140(8):2210-2216
[23]Deakin MR,Melroy O R.Monitoring the growth of an oxide fil mon aluminumin situ with the quartz crystal microbalance[J].J.Electrochem.Soc.,1989,136(2):349-352
[24]Qu Q,Yan C W,Zhang L,et al.Initial atmospheric corrosion ofzinc sprayed with NaCl[J].Trans.Nonferrous Met.Soc.China,2003,13(5):1243-1246
[25]Szir偄ki L,Sz cs E,Pilb偄th Z,et al.Study of the initial stage ofwhite rust formation onzinc single crystal by EIS,STM/AFMandSEM/EDS techniques[J].Electrochi mica Acta,2001,(46):3743-3754
[26]Kleber C,Schreiner M.Multianalytical in-situ investigations ofthe early stages of corrosion of copper,zinc and binary copper/zincalloys[J].Corros.Sci.,2003,45(8):2851-2866
[27]Bernard MC,Hugot-Le A,Massinon D,et al.Underpaint corro-sion of zinc-coated steel sheet studied by in situ Raman spec-troscopy[J].Corros.Sci.,1993,35(Nos5-8):1339-1349
[28]L櫣tzenkipchen D,Waligura C U,Strehblow H.An in situ EXAFS-study of corrosion products[J].Corros.Sci.,1998,40(6):1037-1041
[29]Suzukia,S,Suzukia T,Ki muraa M,et al.EXAFS characterizationof ferric oxyhydroxides[J].Appl.Surf.Sci.,2001,169-170:109-112
[30]Chung S C,Lin AS,Chang J R,et al.EXAFSstudy of atmospher-ic corrosion products on zinc at the initial stage[J].Corros.Sci.,2000,42,1599-1610
[31]Tomashov N D.Development of the electrochemical theory ofmetallic corrosion science[J].Corrosion,1964,20:7t-14t
[32]Rozenfeld I L.Atmospheric corrosion of metals[J].NACE,Hous-ton,TX,1972
[33]Stratmann M,Streckel H,Ki m K T,Crockett S.On the atmo-spheric corrosion of polarization curves on metal surfaces whichcovered by thin electrolyte layers[J].Corros.Sci.,1990,30(6/7):715-734
[34]Cox A,Lyon S.An electrochemical study of the atmospheric corro-sion of mild steel-I,experi mental[J].Corros.Sci.,1994,36(7):1167-1176
[35]Fiaud C,Keddam M,Kadri A,Takenouti H.Electrochemicali mpedancein a thin surface electrolyte layer influence of the po-tential probe location[J].Electrochi m.Acta,1987,32(6):445-448
[36]Abayarathna D,Hale E B,O’Keefe T J,et al.Effects of sampleorientation on the corrosion of zinc ammoniumsulfate and sodiumhydroxide solutions[J].Corros.Sci.,1991,32(7):755-768
[37]Fratesi R,Roventi G,Brance C,Si moncini S.Corrosion resistanceof Zn-Co alloy coatings[J].Sur.Coat.Technol.,1994,63:97-103
[38]Nishikata A,Ichihara Y,Hayashi Y,Tsuru T.Influence of elec-trolytelayer thickness and pHontheinitial stage of the atmospher-ic corrosion of iron[J].J.Electrochem.Soc.,1997,144(4):1244-1252
[39]Cao C N,Zhang J Q.An Introduction to ElectrochemicalI mpedance Spectroscopy[M].Beijing:Science Press,2002(曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002)
[40]Nishikata A,Ichihara Y,Tsuru T.An application of electrochemi-cal i mpedance spectroscopy to atmospheric corrosion study[J].Corros.Sci.,1995,37(6):897-911
[41]Nishikata A,Ichihara Y,Tsuru T.Electrochemical i mpedancespectroscopy of metals covered with a thin electrolyte layer[J].Electrochi mica Acta,1996,41(7/8):1057-1062
[42]EL-Mahdy G A,Ki m K B.AC i mpedance study on the atmo-spheric corrosion of aluminumunder periodic wet-dry conditions[J].Electrochi mica Acta,2004,49:1937-1948
[43]Yadav AP,Nishikata A,Tsuru T.Degradation mechanismof gal-vanized steel in wet-dry cyclic environment containing chlorideions[J].Corros.Sci.,2004,46:361-367
[44]Chung S C,Lin AS,Chang J R,Shih HC.EXAFSstudy of atmo-spheric corrosion products on zinc at the initial stage[J].Corros.Sci.,2000,42:1599-1610
[45]Budevski E,Obretenov W,Bostanov W,Staikov G.Noise analysisin metal deposition-expectation andli mits[J].Electrochi mica Ac-ta,1989,34(8):1023-1029
[46]Bertocci U,Huet F.Noise analysis applied to electrochemical sys-tems[J].Corrosion,1995,51(2):131-144
[47]Magaino S I,Kawaguchi A,Hirata A,Osaka T.Spectrumanalysisof corrosion potential fluctuationfor localized corrosion of type 304stainless steel[J].J.Electrochem.Soc.,1987,134(12):2993-2997
[48]Leoal A,Doleoek V.Corrosion monitoring system based on mea-surement and analysis of electrochemical noise[J].Corrosion,1995,51(4):295-300
[49]Riberge P R.Analysis of electrochemical noise by the stochasticprocess detector method[J].Corrosion,1994,50(7):502-512
[50]Chen J F,Bogaerts WF.Electrochemical emissionspectroscopyformonitoring uniformandlocalized corrosion[J].Corrosion,1996,52(10):753-785
[51]Pistorius P C.Design aspects of electrochemical noise for uncoatedmetals:electrode size and sampled rate[J].Corrosion,1997,53(4):273-283
[52]Xiao H,Han L T,Lee G C,Mansfeld F.Collection of electrochemi-cal i mpedance and noise data for polymet-coated steel fromre-mote test sites[J].Corrosion,1997,53(5):412-422
[53]Flis J,Dawson J L,Gill J,Wood G C.I mpedance and electrochemi-cal noise measurements on iron and iron-carbon alloys in hotcaustic soda[J].Corros.Sci.,1991,32(8):877-892
[54]Cheng Y L.The electrochemical studies of the corrosion of alu-miniumalloyin bulk solution and the atmospheric corrosion underthin electrolyte layers[D].Zhejiang University,2003(程英亮.铝合金在本体溶液以及薄层液膜下的腐蚀电化学研究[D].浙江大学,2003)
[55]Yee S,Oriam R A,Stratmann MJ.Application of a Kelvin micro-probe to the corrosion of metal in humid atmospheres[J].J.Elec-trochem.Soc.,1991,138(1):55-60
[56]Wang J,Tsuru T.Aninvestigation on oxygen reduction under thinelectrolyte layer using Kelvin probe reference electrode[J].J.Chin.Soc.Corros.Prot.,1995,15(3):180-188(王佳,水流彻.使用Kelvin探头参比电极技术研究液层厚度对氧还原速度的影响[J].中国腐蚀与防护学报,1995,15(3):180-188)
[57]Wang J,Tsuru T.Electrochemical measurements under thin elec-trolytelayer using Kelvin probe reference electrode[J].J.Chin.Soc.Corros.Prot.,1995,15(3):173-178(王佳,水流彻.使用Kelvin探头参比电极技术进行薄液层下电化学测量[J].中国腐蚀与防护学报,1995,15(3):173-178)
[58]Zhang X Y,Ke k,Du Y L.Research on the electrochemical corro-sion cell for metal under different thin layer electrolytes[J].J.Chin.Soc.Corros.Prot.,2001,21(2):117-122(张学元,柯克,杜元龙.金属在薄液膜下电化学腐蚀电池的设计[J].中国腐蚀与防护学报,2001,21(2):117-122)
[1] 范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[2] 师超,邵亚薇,熊义,刘光明,俞跃龙,杨志广,许传钦. 硅烷偶联剂改性磷酸锌对环氧涂层防腐性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 38-44.
[3] 潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[4] 赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[5] 赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[6] 邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[7] 孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[8] 赖德林,孔纲,车淳山. 硅酸盐封闭对TiO2转化膜耐蚀性的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 607-614.
[9] 王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[10] 严寒, 赵晴, 杜楠, 胡彦卿, 王力强, 王帅星. 镀锌层三价铬钝化成膜过程及耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 547-553.
[11] 王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO3溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[12] 张新新,高志明,胡文彬,伍志鹏,韩连恒,卢丽花,修妍,夏大海. Q235钢在薄液膜下腐蚀行为与图像信息的相关性研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[13] 张鑫,戴念维,杨燕,张俊喜. 模拟工业环境下直流电场对金属Zn腐蚀机理的影响[J]. 中国腐蚀与防护学报, 2017, 37(5): 451-459.
[14] 孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[15] 牛振国, 郭浦山, 叶宏, 杨丽景, 许赪, 宋振纶. Zn-7Mg合金热处理显微组织演变及耐蚀性能研究[J]. 中国腐蚀与防护学报, 2017, 37(4): 347-353.