Zn-Fe-SiO2复合镀层的性能研究

范云鹰; 张英杰; 陈阵;董鹏;罗少林

昆明 650093）昆明理工大学昆明 650093）昆明理工大学

Study on Properties of Zn-Fe-SiO2 Composite Coatings

;;;;

昆明 650093）昆明理工大学昆明 650093）昆明理工大学

全文: PDF(125 KB)

摘要: 分别采用硫酸盐体系和氯化物体系的最佳工艺条件电沉积制备了高铁(Fe mass%>1%)和低铁(Fe mass%<1%)的Zn-Fe-SiO2复合镀层，并系统测试了不同厚度Zn-Fe-SiO2复合镀层的耐蚀性、结合力、孔隙率和氢脆性等综合性能，同时与电镀Zn及Zn-Fe合金进行了对比.实验结果表明：Zn-Fe-SiO2复合镀层的耐蚀性及其它综合性能均优于Zn-Fe合金镀层和Zn镀层.因此，相对于电镀Zn及Zn-Fe合金，电沉积Zn-Fe-SiO2复合镀层技术具有先进性，应用前景良好.

关键词 ：复合镀层, 耐蚀性, 结合力, 孔隙率, 氢脆性

Abstract：High-iron(Fe mass%>1%)and low-iron(Fe mass%<1%)Zn-Fe-SiO2 composite coatings have been obtained from sulfate bath and chloride bath with optimum technics.Corrosion resistance,adhesion,porosity and hydrogen embrittlement of Zn-Fe-SiO2 composite coatings with different thickness have been tested systematically,and these data have been compared with the properties of Zn and Zn-Fe alloy.The results show that corrosion resistance and all other properties of Zn-Fe-SiO2 composite coatings are better than that of Zn and Zn-Fe alloy.Therefore,the Zn-Fe-SiO2 composite electrodepositing technique is superior to Zn and Zn-Fe alloy electroplating,with a great prospect in application.

Key words： composite coating corrosion resistance adhesive porosity hydrogen embrittlement

收稿日期: 2005-05-13

ZTFLH:

TG174.4

通讯作者: 范云鹰*

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	范云鹰
	张英杰
	陈阵
	董鹏
	罗少林
44.8K

引用本文:

范云鹰; 张英杰; 陈阵; 董鹏; 罗少林 . Zn-Fe-SiO2复合镀层的性能研究[J]. 中国腐蚀与防护学报, 2005, 25(5): 317-320 .

链接本文:

https://www.jcscp.org/CN/Y2005/V25/I5/317

[1]Ke W.Chinese Corrosion Survey Report[M].Beijing:Chemical In-dustry Press,2003(柯伟.中国腐蚀调查报告[M].北京:化学工业出版社,2003)
[2]Xiao Y D,Wang G Y,Li X G,et al.Corrosion behavior of atmo-sphere environment and corrosion feature of materials in our west-ern area[J].J.Chin.Soc.Corros.Prot.,2003,23(4):248-255(萧以德,王光雍,李晓刚等.我国西部地区大气环境腐蚀性及材料腐蚀特征[J].中国腐蚀与防护学报,2003,23(4):248-255)
[3]Xu B S,Ma S N,Liu S S,et al.Application of surface engineeringand remanufacturing engineering[J].Mater.Prot.,2000,33(1):1-4(徐滨士,马世宁,刘世参等.表面工程的应用和再制造工程[J].材料保护,2000,33(1):1-4)
[4]Abayarathna D,Hale E B,O’Keefe T J,et al.Effects of sample ori-entation on the corrosion of zinc in ammonium sulfate and sodiumhydroxide solutions[J].Corros.Sci.,1991,33(7):755-768
[5]Rizzi K W.New zinc electroplate fights both wear and corrosion[J].Metal Progress,1986,129(2):51-54
[6]Guo R,Weinberger F.Pitting corrosion of passivated zincmonocrystals[J].Corrosion,1995,51(5):356-366
[7]Qu Q,Yan C W,Zhang L,et al.Initial atmospheric corrosion ofzinc sprayed with NaCl[J].Trans.Nonferrous Met.Soc.China,2003,13(5):1243-1246
[8]Ramanauskas R,Muleshiova L,Maldonado L,et al.Characterizationof the corrosion behavior of Zn and Zn alloy electrodeposits;atomo-spheric and accelerated tests[J].Corros.Sci.,1998,40(2):401-410
[9]Shen P H,Tu Z M.Zinc and Zinc Alloy Plating[M].Beijing:Me-chanical Industry Press,2002(沈品华,屠振密.电镀锌及锌合金[M].北京:机械工业出版社,2002)
[10]Wilcox G D,Gabe D R.Electrodeposited zinc alloy coatings[J].Corros.Sci.,1993,35(5):1251-1258
[11]Zeng X D.A full bright Zn-Fe alloy plating process[J].Electro-plating and Finishing,1992,11(3):24-30(曾祥德.全光亮锌铁合金电镀工艺[J].电镀与涂饰,1992,11(3):24-30)
[12]Fan Y Y,Zhang Y J,Yang X W,et al.Corrosion resistance of elec-trodeposited Zn-Fe-SiO2composite coatings[J].Corros.Sci.Prot.Technol.,2004,16(4):245-246(范云鹰,张英杰,杨显万等.Zn-Fe-SiO2复合镀层的耐蚀性[J].腐蚀科学与防护技术,2004,16(4):245-246)
[13]Fan Y Y,Zhang Y J,Yang X W,et al.Influence of composition ofelectro-solution on the component of Zn-Fe-SiO2compositecoating[J].Surf.Technol.,2003,32(5):53-55(范云鹰,张英杰,杨显万等.镀液组成对Zn-Fe-SiO2合金复合镀层成分的影响[J].表面技术,2004,16(4):245-246)
[14]Zhang Y J,Fan Y Y,Yang X W,et al.Influence of technics ofelectrodepositing on the component of Zn-Fe-SiO2compositecoatings[J].Mater.Prot.,2004,37(5):26-27(张英杰,范云鹰,杨显万等.工艺条件对Zn-Fe-SiO2复合镀层成分的影响[J].材料保护,2004,37(5):26-27)

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[3]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[4]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[5]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[6]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[7]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[8]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[9]	杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al₂O₃复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[10]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[11]	程多云,赵晋斌,刘波,姜城,付小倩,程学群. 高镍钢和传统耐候钢在马尔代夫严酷海洋大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 29-35.
[12]	蓝秀玲,刘光明,周街胜,刘志雷,彭叔森,李茂东. 有机硅/SiO₂杂化溶胶改性丙烯酸树脂及性能研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 601-606.
[13]	王志虎, 张菊梅, 白力静, 张国君. AZ91镁合金表面微弧氧化与化学镀铜复合处理层的微观组织与性能[J]. 中国腐蚀与防护学报, 2018, 38(4): 391-396.
[14]	杨钊, 时惠英, 蒋百灵, 葛延峰, 张静, 张曼玉, 李研. 脉冲电流对1050铝合金微弧氧化过程的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 283-288.
[15]	黄勇, 王善林, 王帅星, 龚玉兵, 柯黎明. 含硫化物夹杂铁基块体非晶合金在HCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(2): 203-209.

Viewed

Full text

Abstract

Cited

Shared

Discussed