海水环境微生物附着对钝性金属开路电位的影响

王佳;李相波;王伟1

中科院青岛海洋研究所

The Effect of Microorganism Attachmenet on the Open-circuit-potential of Passive Metals in Seawater

;;;

中科院青岛海洋研究所

全文: PDF(186 KB)

摘要: 彩电化学技术和荧光显微技术研究了微生物附着对钝性金属在海水中开路电位的影响。研究中发现，在自然海水中，钝性金属的开路电位逐渐正移达300mV。显微镜原位观察表明，浸入海水后，微生物在金属表面逐渐寄居附着，形成微生物膜。微生物的数量与开路电位按相同方式增加。但在来菌海水中以及铜电极情况下，开路电位保持不变，微生物也很少附着在表面上。此外，钝性金属界面双层电容在自然海水中逐渐减少，但在来菌海水中，由于没有微生物膜存在，电容值保持不变。这些结果证实，微生物在表面的附着和寄居生长是导致钝性金属开路电位正移的主要原因。

关键词 ：微生物附着, 开路电位, 电化学

Abstract：An investigation on the changes in open-circuit-potentials of passive metals in seawater was made with electrochemical technology and epifluoresence microscopy. It was found that in natural seawater, the open-circuit-potentials of passive metals shifted in noble direction gradually. The in-situ microscope observation showed that biofilm gradually formed on the metal surfaces with the increase of open-circuit-potentials and the change in bacteria number on metal surface was in the same manner with the ennoblement of the open-circuit=potentials. However, compared that in natural sea water, both open-circuit-potentials and bacteria number are not changed in sterile seawater. In addition, open-circuit-potentials and bacteria number for coppper clectrode were almost not changed no matter in natural or in sterile seawater. Moreover, the double capacitance of passive metals decreased woth time when immersed in natural seawater, while it remained almost unchanged in sterile seawater due to the decrease in dielectric constant with the formation of bilfilm in natural seawater. Above results strongly supported that bacteria attachment and growth of bilfilms were the cause for the ennoblement of open-circuit-potentials of the passive metal.

Key words： microorganism open-circuit-potential electrochemistry

收稿日期: 2003-04-28

ZTFLH:

TG172.5

通讯作者: 王佳 E-mail: jwang@ms.qdio.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王佳
	李相波
	王伟
44.8K

引用本文:

王佳; 李相波; 王伟 . 海水环境微生物附着对钝性金属开路电位的影响[J]. 中国腐蚀与防护学报, 2004, 24(5): 262-266 .
. The Effect of Microorganism Attachmenet on the Open-circuit-potential of Passive Metals in Seawater. J Chin Soc Corr Pro, 2004, 24(5): 262-266 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I5/262

[1]ClaudeE ,Zobell,etal.Thesignificanceofmarinebacteriainthefoulingofsubmergedsurface[J].J .Bacterial,1935,29:239-251
[2]ColwellRR .Microbialecologyofbiofouling.biotechnologyinthemarinesciences[M ].NewYork:JohnWileyandSonsInc.,1984:221-231
[3]DharHP ,HowellDW ,etal.Theuseofinsituelectrochemicalreductionofoxygeninthediminutionofadsorptionbacteriaonmetalsinseawater[J].J .Electrochem.Soc.,1982,129(10):2178-2182
[4]DharHP ,LewisDH ,etal.Theelectrochemicaldiminutionofsurfacebacterialconcentration[J].CAN .J.Microbiol,1981,27:998-1010
[5]TadshiMatsunaga,Tae-KyuLIM .Electrochemicalpreventionofbiofouling[J].Electrochemisty,2000,68(11):847-852
[6]BurdeLittle,etal.Microbiologicallyinfluencedcorrosion[A].NACEInternational5[C].Houston,Texas,1997:4-7
[7]YoungLY ,etal.Theroleofmicroorganismsinmarinefouling[J].InternationalBiodeterBull,1973,9:105-109
[8]CostertonJW ,etal.Microbialbiofilms[J].Annu.Rev.Microbial,1995,49:711-745
[9]XuK ,DexterSC ,LutherGW .Voltammetricmicroelectrodesforbiocorrosionstudies[J].Corrosion,1998,54(10):814-823
[10]MollicaA ,TrevisA .Correlationbetweentheformationofapri maryfilmandthemodificationofthecathodicsurfacesteelinsea water[A].Proc.4thInt.Cong.ManneCorrosionandFouling[C].Juan-Les-Prins.Antibes,1976,351
[11]DexterSC ,GaoGY .Effectofseawaterbiofilmsoncorrosionpo tentialandoxygenreductionofstainlesssteel[J].Corrosion,1988,44(10):717-723
[12]ScottoV ,LaiME .Theennoblementofstainlesssteelsinseawa ter:alikelyexplanationcomingfromthefield[J].Corros.Sci.,1998,40(6):1007-1018
[13]SalvagoG ,MagagninL .Biofilmeffectonthecathodicandanodicprocessesonstainlesssteelinseawaternearthecorrosionpoten tial:part1-corrosionpotential[J].Corrosion,2001,57(8):680-692
[14]JohnR ,BardalE .Cathodicpropertiesofdifferentstainlesssteelsinnaturalseawater[J].Corrosion,1985,41(5):296-302
[15]BelasMR ,etal.Adsorptionkineticsofpollarlyflagellatedvibrio[J].J .Bacteriol,1982,151(3):1568-1580
[16]LiHuirong,FuYubin,LiYun,etal.Compositionofmarinebacte riainmicro-biofilmformedonfourdifferentartificialsubstrata[J].JournalofOceanUniversityofQingdao,2001,31(3):32(李会荣,付玉滨,李筠等.海洋细菌在不同基质表面微生物粘膜中的组成[J].青岛海洋大学学报,2001,31(3):32
[17]JiWS ,XuB ,XuHS ,ColwellRR .Studiesonattachmentofma rinebacteriatobioticandabioticsurfaces[J].JournalofOceanU niversityofmarinebacteriatobioticandabioticsurfaces[J].Jour nalofOceanUniversityofQingdao,1991,21(2):61-68(纪伟尚,许兵,徐怀恕,R .R .Colwell.海洋细菌在生物和非生物表面附着的研究[J].青岛海洋大学学报,1991,21(2):61-68)
[18]ScottoV ,LaiME .Analyticalcharacterizationofnaturalmarinebiofilms[A].10 thInternat.CongressonMarineCorrosionandFouling[C].Melbourne,Australia,Feb.,1999

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[4]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[5]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[6]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[7]	翟思昕, 杨幸运, 杨继兰, 顾剑锋. 淬火-配分-回火钢在模拟海水环境中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[8]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[9]	付海波, 刘晓茹, 孙媛, 曹大力. 环氧树脂/重结晶碳化硅复合材料的抗腐蚀性能[J]. 中国腐蚀与防护学报, 2020, 40(4): 373-380.
[10]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[11]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[12]	王廷勇, 董如意, 许实, 王辉. 石墨烯改性Ti/IrTaSnSb-G金属氧化物阳极在低温和低盐NaCl溶液中的电化学性能[J]. 中国腐蚀与防护学报, 2020, 40(3): 289-294.
[13]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[14]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[15]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.

Viewed

Full text

Abstract

Cited

Shared

Discussed