外加电位对X70管线钢在近中性PH溶液中的应力腐蚀破损的影响

中国腐蚀与防护学报

2004, Vol. 24

Issue (4): 208-212

研究报告

本期目录 | 过刊浏览

外加电位对X70管线钢在近中性PH溶液中的应力腐蚀破损的影响

郭浩

Effect of Applied Potentials on Stress Corrosin Cracking of X70 Pipeline Steel in Near-Neutral-pH Solutions

全文: PDF(228 KB)

摘要: 采用慢应变速率试验（SSRT）研究了不同电位下X70管线钢在近中性pH溶液中的应力腐蚀破裂（SCC）行为，同时研究了溶液中通往不同含量CO2对SCC的影响。结果表明，X70管线钢在近中性pH溶液中的开裂方式是穿晶型的，具有准解理特征，并且随着外加阴极电位的降低，SCC敏感性增加，随CO2含量的增加，pH值降低，SCC敏感性增加，均表现为氢致开裂占主导。

关键词 ：管线钢, 应力腐蚀破裂, 近中性pH, 电位, CO2含

Abstract：The stress corrosion cracking(SCC) behaviior of X70pipeline steel in near-neutral-pH solutions at different applied potentials and the effect of different levels of CO2 on SCC were studied with slow strain rate testing (SSRT). The results showed that the cracking mode of X70pipeline steel in near-neutral-pH solutions was transgranular, with the features of quasi-cleavage. The susceptibilit to SCC increased as the applied potential moved towards the cathodic direction The value of pH decreased with the increased addition of CO2 in the solution, which increased the susceptibitlity to SCC. Hydroge induced cracking(HIC) dominated the process.

Key words： pipeling steel stress corrosion cracking near-neutral pH potential carbon dioxide

收稿日期: 2003-05-12

ZTFLH:

TG172.8

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	郭浩
44.8K

引用本文:

郭浩 . 外加电位对X70管线钢在近中性PH溶液中的应力腐蚀破损的影响[J]. 中国腐蚀与防护学报, 2004, 24(4): 208-212 .

链接本文:

https://www.jcscp.org/CN/Y2004/V24/I4/208

[1]GuoH ,CaiX ,YangW .Thefactorsofmechanicsandmaterialsinfluenc ingstresscorrosioncrackingofpipelinesteels[J].Mater.MechanicalEng.,2002,26(4):1-5(郭浩,蔡,杨武.影响管线钢应力腐蚀破裂的力学和材料因素[J].机械工程材料,2002,26(4):1-5)
[2]Gonzalez-RodriguezJG ,CasalesM ,Salinas-BravoVM ,AlbarranJL ,MartinezL .EffectofmicrostructureonthestresscorrosioncrackingofX -80pipelinesteelindilutedsodiumbicarbonatesolutions[J].Corro sion,2002,58(7):584-590
[3]RebakRB ,XiaZ ,SafruddinR ,Szklarska-SmialowskaZ .Effectofso lutioncompositionandelectrochemicalpotentialonstresscorrosioncrackingofX -52pipelinesteel[J].Corrosion,1996,52(5):396-405
[4]KushidaT ,NoseK ,AsahiH ,etal.EffectsofmetallurgicalfactorsandtestconditionsonnearneutralpHSCCofpipelinesteels[A].Corrosion/2001[C].Houston,NACEInternationalTX ,2001,PaperNo.01213
[5]ChenW ,KingF ,VokesE .CharacteristicsofnearneutralpHstresscor rosioncracksinanX65pipeline[J].Corrosion,2002,58(3):267-275
[6]ParkinsRN ,BlanchardWKJr,DelantyBS .Transgranularstresscorro sioncrackingofhigh-pressurepipelinesincontactwithsolutionsofnearneutralpH[J].Corrosion,1994,50(5):394-408
[7]GuB ,LuoJ,MaoX .Hydrogenfacilitatedanodicdissolutiontypestresscorrosioncrackingofpipelinesteelsinnear-neutralpHsolution[J].Corrosion,1999,55(1):96-106
[8]PuiggaliM ,RousserieS ,TouzetM .Fatiguecrackinitiationonlow-car bonsteelpipesinanear-neutral-pHenvironmentunderpotentialcontrolconditions[J].Corrosion,2002,58(11):961-970
[9]GuB ,YuWZ ,LuoJL ,MaoX .TransgranularstresscorrosioncrackingofX -80andX -52pipelinesteelsindiluteaqueoussolutionwithnear-neutralpH[J].Corrosion,1999,55(3):312-319
[10]ChenWX ,WangSH ,KingFraser,JackTomR ,WilmottMartynJ.Hy drogenpermeationbehaviorofX -70pipelinesteelinanear-neutralpHsoilenvironment[A].2000InternationalPipelineConference-Vol ume2[C].ASME 2000:953-960

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[4]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[5]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[6]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[7]	王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[10]	袁玮,黄峰,甘丽君,戈方宇,刘静. 显微组织对X100管线钢氢致开裂及氢捕获行为影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 536-542.
[11]	丁国清,李向阳,张波,杨朝晖,黄桂桥,杨海洋,刘凯吉. 金属材料在天然海水中的腐蚀电位及其变化规律[J]. 中国腐蚀与防护学报, 2019, 39(6): 543-549.
[12]	王标,杜楠,张浩,王帅星,赵晴. 304不锈钢点蚀产物对亚稳态点蚀萌生和稳态蚀孔生长的加速作用[J]. 中国腐蚀与防护学报, 2019, 39(4): 338-344.
[13]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[14]	王贵容,邵亚薇,王艳秋,孟国哲,刘斌. 阴极保护电位对破损环氧涂层阴极剥离的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 235-244.
[15]	施远,金洙吉,姜冠楠,刘作涛,周忠正,王泽北. YG15硬质合金电化学腐蚀机理研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 253-259.

Viewed

Full text

Abstract

Cited

Shared

Discussed