冷轧低碳钢板表面形貌与其耐大气腐蚀性能的关系

钟庆东

上海市上海电力学院电化学室

STUDY ON ATMOSPHERIC CORROSION OF LOW ALLOY STEELS

Qingdong Zhong

上海市上海电力学院电化学室

全文: PDF(133 KB)

摘要: 采用薄层电化学测试技术，并结合结露试验和表面粗糙度测量研究了冷轧低碳钢板的耐大气腐蚀性能.研究表明，薄层电化学测试技术可以评价冷轧低碳钢板耐大气腐蚀性能，且评价结果与钢板的实际使用情况基本一致.冷轧低碳钢板表面结露行为与钢板表面粗糙度分布有关，但与钢板的耐大气腐蚀性能并无直接关系.

关键词 ：粗糙度, 结露, 电化学

Abstract：The corrosion of 7 kinds of mild steel and low alloy steel in immersion-wet-dry cycle test environment and the electrochemical feature of rusted metals after test were studied by using EIS and SEM et al.The solution containing HSO-3 and Cl-,was used for wetting and immersion specimens at circumstance temperature 40℃ for 4 min respectively.The drying cycle was maintained for 12 min at temperature 12℃.The results indicated that,the weight loss all followed exponential decay function:Y=Y0+Ae-t/B.The corrosion rate of mild steel was 2.49 times than that of the most corrosion resistant low alloy after 120 h test.The results of electrochemical measurement showed that,the further corrosion rate would be controlled by cathodic diffusion process.The impedance of 7 kinds of steels after corrosion test was linear with the annual corrosion rate.

Key words： steel low alloy steel atmospheric corrosion

收稿日期: 2002-11-25

ZTFLH:

TG172.3

通讯作者: 钟庆东

Corresponding author: Qingdong Zhong

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	钟庆东
44.8K

引用本文:

钟庆东 . 冷轧低碳钢板表面形貌与其耐大气腐蚀性能的关系[J]. 中国腐蚀与防护学报, 2004, 24(3): 151-154 .
Qingdong Zhong. STUDY ON ATMOSPHERIC CORROSION OF LOW ALLOY STEELS. J Chin Soc Corr Pro, 2004, 24(3): 151-154 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I3/151

[1]CorvoF ,BetancourtN ,MendozaAR .Theinfluenceofairbornesalinityontheatmosphericcorrosionofsteel[J].Corros.Sci.,1995,37(12):1889
[2]CorvoF ,MendozaAR ,AutieM ,etal.Roleofwateradsorptionandsaltcontentinatmosphericcorrosionproductsofsteel[J].Corros.Sci.,1997,39(4):815
[3]MendozaAR ,CorvoF .Outdoorandindooratmosphericcorrosionofcarbonsteel[J].Corros.Sci.,1998,41(1):75
[4]OhSJ,CookDC ,TownsendHE .Atmosphericcorrosionofdiffer entsteelsinmarine,ruralandindustrialenvironments[J].Corros.Sci.,1999,41(9):1687
[5]MorcilloM ,ChicoB ,MariacaL ,etal.Salinityinmarineatmospher iccorrosion:itsdependenceonthewindregimeexistinginthesite[J].Corros.Sci.,2000,42(1):91
[6]ChungKW ,KimKB .Astudyoftheeffectofconcentrationbuild-upofelectrolyteontheatmosphericcorrosionofcarbonsteeldur ingdrying[J].Corros.Sci.,2000,42(3):517
[7]WeiBM .TheoryofMetalCorrosionandApplication[M ].Beijing:ChemicalIndustryPress,1991(魏宝明.金属腐蚀理论及应用[M ].北京:化学工业出版社,1991)
[8]XuNX ,ZhaoLY ,DingCH ,etal.Somefactorsaffectingdewingbehavioronmildsteelsurfaceduringatmosphericcorrosion[J].Corros.Prot.,2001,22(12):522(徐乃欣,赵灵源,丁翠红等.碳钢大气腐蚀时表面结露行为的某些影响因素[J].腐蚀与防护,2001,22(12):522)
[9]XuNX ,ZhaoLY ,DingCH ,etal.Anovellaboratorytechniqueforobservingdewformationatearlystageinatmosphericcorrosion[J].J .Chin.Soc.Corros.Prot.,2001,21(5):301(徐乃欣,赵灵源,丁翠红等.研究大气腐蚀金属表面结露行为的新技术[J].中国腐蚀与防护学报,2001,21(5):301)
[10]ZhangCD ,XuNX ,DingCH ,etal.Electrochemicaltechniqueforinvestigatingthinfilmrustpreventiveoil[J].J .Chin.Soc.Corros.Prot.,1991,11(2):263(张承典,徐乃欣,丁翠红等.研究薄层防锈油的电化学技术[J].中国腐蚀与防护学报,1991,11(2):263)
[11]ZouMP ,LiX ,ZhongQD ,etal.Influenceofsurfacecontamina tiononatmosphericcorrosionperformanceofcold-rolledsteelplates[J].Corros.Prot.,2002,23(5):196(邹美平,郦希,钟庆东等.表面污染物对冷轧低碳钢板耐大气腐蚀性能的影响[J].腐蚀与防护,2002,23(5):196)

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[4]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[5]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[6]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[7]	翟思昕, 杨幸运, 杨继兰, 顾剑锋. 淬火-配分-回火钢在模拟海水环境中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[8]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[9]	付海波, 刘晓茹, 孙媛, 曹大力. 环氧树脂/重结晶碳化硅复合材料的抗腐蚀性能[J]. 中国腐蚀与防护学报, 2020, 40(4): 373-380.
[10]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[11]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[12]	王廷勇, 董如意, 许实, 王辉. 石墨烯改性Ti/IrTaSnSb-G金属氧化物阳极在低温和低盐NaCl溶液中的电化学性能[J]. 中国腐蚀与防护学报, 2020, 40(3): 289-294.
[13]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[14]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[15]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.

Viewed

Full text

Abstract

Cited

Shared

Discussed