中国腐蚀与防护学报  2004, Vol. 24 Issue (3): 135-142     
  研究报告 本期目录 | 过刊浏览 |
T6态峰时效AA2090及AA8090铝-理合金晶间腐蚀与剥蚀性能
李劲风
中南大学材料科学与工程学院
Intergraular Corrosion and Exfoliation Behaviors of Peak-Aged AA2090 and AA8090 Al-Li Alloys
中南大学材料科学与工程学院
全文: PDF(289 KB)  
摘要: 研究了峰时效AA2090及AA8090 Al-Li合金的晶间腐蚀与剥蚀敏感性。结果表明,AA2090合金峰时效时晶内析出大量T1相,晶内T1相的优先溶解导致晶间腐蚀的电化学动力较低。合金晶间腐蚀程度较弱;而AA8090合金峰时效时由于T2相在晶界呈粗链状析出,其阳极溶解导致严重的晶间腐蚀。由于晶间腐蚀敏感性的差异,AA8090合金的剥蚀敏感性较大,而AA2090合金则出现只是小薄片状的轻微剥蚀。
关键词 Al-Li合金峰时效晶间腐蚀剥蚀    
Abstract:Intergranular corrosion and exfoliation of peak-aged AA2090 and AA8090 Al-Li alloys were studied.For peak-aged AA2090 alloy,due tonumerousT1 precipitations within grains and the selective dissolution of T1,the electrochemical dynamic of intergranular corrosion is determined.For peak-aged AA8090 alloy,because of selective dissolution of thick continuous T2 precipitates at grain boundary,severe intergranular corrosion occurs.Owing to the difference of microstructure and intergranular orrosion,AA8090 alloy is very susceptible to exfoliation corrosion,while only superficial exfoliation w ith tiny flakes appears in AA2090 alloy.
Key wordsAl-Li alloy    peak-aging    intergranular corrosion    exfoliation corrosion
收稿日期: 2002-09-16     
ZTFLH:  TG174.3  
通讯作者: 李劲风     E-mail: jfli2000@163.net

引用本文:

李劲风 . T6态峰时效AA2090及AA8090铝-理合金晶间腐蚀与剥蚀性能[J]. 中国腐蚀与防护学报, 2004, 24(3): 135-142 .

链接本文:

https://www.jcscp.org/CN/Y2004/V24/I3/135

[1]TanCY ,ZhengZQ ,PanY ,etal.EffectofexfoliationcorrosiononmechanicalpropertiesofAl-Lialloy[A].ZhengZQ .Proceedingsofthe2 ndNationalSymposiumonAl-LiAlloys[C].Changsha:PublicationPressofCentralSouthUniversityofTechnology,1993.154-157(谭澄宇,郑子樵,潘颖等.剥落腐蚀对铝锂合金力学性能的影响[A].郑子樵主编.第二届全国铝锂合金研讨会论文集[C].长沙:中南工业大学出版社,1993.154-157)
[2]HeJP ,ChenWL ,XuW ,etal.EffectofexfoliationonstructureandtensilestrengthofLC4CSaluminiumalloyatconstanttempera ture[J].J .NanjingUniversityofAeronauticsandAstronautics,1999,31(5):575-579(何建平,陈文理,许玮等.恒温剥蚀对LC4CS铝合金结构和力学性能的影响[J].南京航空航天大学学报,1999,31(5):575-579)
[3]HeB ,SunYC ,FanWX .Influenceofexfoliationcorrosiononthefatigueofaluminiumalloy[J].JNanjingUniversityofAeronauticsandAstronautics,1998,30(3):306-310(贺斌,孙有朝,樊蔚勋.剥蚀对铝合金疲劳性能的影响[J].南京航空航天大学学报,1998,30(3):306-310)
[4]WangBR ,ZhangWJ ,GaoSM .Effectofquenchingcraftsonin tergranularcorrosionof2024alloytubes[J].LightAlloysFabrica tionTechnology,1996,24(9):23-26(王本仁,张万金,高叔明.淬火工艺对2024管材晶间腐蚀的影响[J].轻合金加工技术,1996,24(9):23-26)
[5]HeLZ ,ZhangXB ,SunQX ,etal.EffectsofCuandagetreatmentonsusceptibilitytointergranularcorrosionofAl-Mg-Sialloys[J].Chin.J .NonferrousMetals,2001,11(2):231-235(何立子,张晓博,孙秋霞等.Cu及热处理制度对Al-Mg-Si系合金晶间腐蚀敏感性的影响[J].中国有色金属学报,2001,11(2):231-235)
[6]DuHZ ,XuJX ,LiuQC .Experimentalresearchintocorrosionre sistantperformanceofanewtypeofagingprocesstoaluminiumal loy2024[J].J.CivilAviationUniversityofChina,1999,17(6):1-4(杜洪增,徐建新,刘奇才.新时效制度处理的2024铝合金耐蚀性能的研究.中国民航学院学报,1999,17(6):1-4)
[7]LiD ,ZuoSZ ,GuoBL .StudyonexfoliationcorrosionbehaviorofLY12aluminiumalloy[J].J .Chin.Soc.Corros.Prot.,1995,15(3):203-208(李荻,左尚志,郭宝兰.LY12铝合金剥蚀行为的研究[J].中国腐蚀与防护学报,1995,15(3):203-208)
[8]ZhangY ,ZhuZY ,WangZF ,etal.IntergranularandexfoliationcorrosionbehaviorofAl-Lialloy[J].J.Chin.Soc.Corros.Prot.,1992,12(2):180-184(张匀,朱自勇,王政富等.铝锂合金晶间腐蚀和剥蚀行为.中国腐蚀与防护学报,1992,12(2):180-184)
[9]HB 5225-83.TestofIntergranularcorrosionsusceptibilityinalu miniumalloy[S].(HB 5225-83.铝合金晶间腐蚀试验方法[S].)
[10]ASTMG34-79.Standardtestmethodforexfoliationcorrosionsusceptibilityin2×××and7×××seriesaluminiumalloys(EXCOtest)[S].
[11]BuchheitRG ,MoranJP ,StonerGE .ElectrochemicalbehavioroftheT1(Al2CuLi)intermetalliccompoundanditsroleinlocalizedcorrosionofAl-2%Li-3%Cualloys[J].Corrosion,1994,50(2):120-130
[12]TostenMH ,VasudvanAK ,HowellPR .TheagingcharacteristicsofanAl-2 pctLi-3pctCu-0.12 pctZralloyat190℃[J].Metall.Trans.A ,1988,19A(1):51-66
[13]GaberA ,AfifyN .CharacterizationoftheprecipitatesinAl-Li(8090)alloyusingthermalmeasurementsandTEMexaminations[J].PhysicaB ,2002,315(1-3):315-316
[14]StarinkMJ ,WangP ,SinclairI ,etal.Microstructureandstrength eningofAl-Li-Cu-MgalloysandMMCs:1,Analysisandmodelingofmicrostructurechanges[J].ActaMater.,1997,47(14):3841-3853
[15]ZhangY ,LiuYL ,ZhaoHE ,HuZQ .Intergranularandexfolia tioncorrosionbehaviourof8090Al-Lialloy[J].ActaMetall.Sin.,1991,21(4):B271-B277(张匀,刘玉林,赵洪恩,胡壮麒.8090Al-Li合金晶间腐蚀与剥落腐蚀性能研究[J].金属学报,1991,21(4):B271-B277)
[1] 刘辉,邱玮,冷滨,俞国军. 304和316H不锈钢在LiF-NaF-KF熔盐中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 51-58.
[2] 刘希武,赵小燕,崔新安,许兰飞,李晓炜,程荣奇. 304L不锈钢在硝酸-硝酸钠环境中的腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 543-550.
[3] 赵小燕, 刘希武, 崔新安, 于凤昌. 304L不锈钢在稀硝酸环境下的腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 455-462.
[4] 刘丹阳, 汪洁霞, 李劲风, 陈永来, 张绪虎, 许秀芝, 郑子樵. Mg,Ag,Zn微合金化Al-Cu-Li系铝锂合金T6态时效的晶间腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(2): 183-190.
[5] 刘德强,柯黎明,徐卫平,邢丽,毛育青. 7075厚板铝合金搅拌摩擦焊接头晶间腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 293-299.
[6] 彭新元,周贤良,华小珍. 晶粒尺寸对316LN不锈钢晶间腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2016, 36(1): 25-30.
[7] 许龙, 姚希, 李劲风, 蔡超. 2099铝锂合金晶间腐蚀行为与时效制度的相关性[J]. 中国腐蚀与防护学报, 2014, 34(5): 419-425.
[8] 俞树荣,何燕妮,李淑欣,王璐. 晶粒尺寸对奥氏体不锈钢晶间腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2013, 33(1): 70-74.
[9] 冯万里,张乐福,马明娟. 轧制变形对690合金特殊晶界比例及耐晶间腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(4): 296-299.
[10] 饶思贤,万章,宋光雄,张铮,钟群鹏. 基于规则的晶间腐蚀和氢致开裂的失效模式诊断[J]. 中国腐蚀与防护学报, 2011, 31(4): 260-264.
[11] 黄昌龙,万小朋,赵美英,徐海蓉. 正应力对7150铝合金剥蚀行为的影响[J]. 中国腐蚀与防护学报, 2011, 31(2): 135-138.
[12] 黄昌龙,徐海蓉. 不同时效态对7150铝合金剥蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(6): 487-490.
[13] 胡轶嵩,王俭秋,柯伟,韩恩厚. 690TT合金在高温含铅碱液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2010, 30(6): 427-432.
[14] 孙涛,邓博, 徐菊良,李劲,蒋益明. 氮、铌添加对304奥氏体不锈钢电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(6): 421-426.
[15] 李朝兴;李劲风;BIRBILIS Nick;贾志强;郑子樵. Mg2Si及Si粒子在Al-Mg-Si合金晶间腐蚀中协同作用机理的多电极偶合研究[J]. 中国腐蚀与防护学报, 2010, 30(2): 107-113.