炔氧甲基季胺盐和咪唑啉对N80在饱和CO2的3%NaCl溶液中的缓蚀性能研究

中国腐蚀与防护学报

2004, Vol. 24

Issue (1): 10-15

研究报告

本期目录 | 过刊浏览

炔氧甲基季胺盐和咪唑啉对N80在饱和CO2的3%NaCl溶液中的缓蚀性能研究

蒋秀;骆素珍;郑玉贵;柯伟

中国科学院金属所金属腐蚀与防护国家重点实验室

Study on Inhibitor properties of Quaternary Alkynoxymethyl Amine and Imidazoline for N80 Seamless Steel in 3% NaCl Saturated by CO2

Xiu Jiang;Suzhen Luo;YUgui Zheng;Wei Ke

全文: PDF(252 KB)

摘要: 利用交流阻抗（EIS）、线性极化、动电位极化和拉曼光谱等方法对炔氧甲基季胺盐和咪唑啉在常温常压CO2饱和的模拟油田产出水中的电化学行为和缓蚀性能进行了研究.结果表明:随两种缓蚀剂的加入,体系的阳极电流都明显减小,自腐蚀电位都明显正移,都存在阳极脱附现象和浓度极值现象,炔氧甲基季胺盐的极值浓度为150mg/L，而咪唑啉的极值浓度为100mg/L。并且咪唑啉缓蚀剂的缓蚀效果更佳。但在7m/s时直至缓蚀剂浓度为300mg/L时也没有发现静态下的浓度极值现象。

关键词 ： CO2, 腐蚀, 无缝钢N80, 缓蚀剂, 浓度极值, 阳极

Abstract：A study on the effect of IMC-80-Q(quaternary alkynoxymethyl amine) and IMC-871-W(imidazoline) on the electrochemical behavior and inhibitor properties of N80 steel in 3% NaCl saturated by CO2 at 25±10C was carried out by means of weight loss and electrochemistry techniques including EIS, potentiodynamic polarization and linear polarization. The sharp decrease of anodic current density ia, positive shift of corrosion potential (Ecorr) and anodic desorption were observed in inhibited solutions.The electrochemical parameters Rp,Cd and Rt exhibited extreme values at certain concentrations of two inhibitors,150mg/L for IMC-80-Q and 100mg/L for IMC-871-W ,respectively.IMC-871-W had better inhibitor properties than IMC-80-Q.The weight loss test at 7m/s showed that the cumulative mass loss was decreased sharply for solutions containing IMC-80-Q, compared with inhibitor-free brine, and extreme-value-phenomena of concentration was not observed up to 300mg/L.

Key words： CO2 corrosion N80 seamless steel inhibitor extreme-value-phenomena of concentration anodic desorptio

收稿日期: 2003-02-13

ZTFLH:

TG174.42

通讯作者: 蒋秀 E-mail: xjiang@imr.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	蒋秀
	骆素珍
	郑玉贵
	柯伟
44.8K

引用本文:

蒋秀; 骆素珍; 郑玉贵; 柯伟 . 炔氧甲基季胺盐和咪唑啉对N80在饱和CO2的3%NaCl溶液中的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2004, 24(1): 10-15 .
Xiu Jiang, Suzhen Luo, YUgui Zheng, Wei Ke. Study on Inhibitor properties of Quaternary Alkynoxymethyl Amine and Imidazoline for N80 Seamless Steel in 3% NaCl Saturated by CO2. J Chin Soc Corr Pro, 2004, 24(1): 10-15 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I1/10

[1]JiangXiu,ZhengYugui.Researchprogressofinhibitorinoilandgaswell[J].Corros.Sci.Prot.Technol.,2003,15(3):164-168(蒋秀,郑玉贵.油气井缓蚀剂研究进展[J].腐蚀科学与防护技术,2003,15(3):164-168)
[2]GuoXingpeng,FuChaoyang.InteractionbetweeninhibitorandCO2 cor rosionproductionfilm[D].Qingdao:InhibitorCommitteeofChineseCor rosionandProtection,2001,7-12(郭兴蓬,付朝阳.缓蚀剂和CO2腐蚀产物膜的相互作用[D].青岛:中国腐蚀与防护学会缓蚀剂专业委员会,2001,7-12)
[3]DoughertyJA ,StergmannDW .Theeffectsofflowoncorrosionin hibitorsperformance[J].MaterialPerformance,1996,35(4):47-53
[4]LiuXiaowu,PengFangming,ZhengJiashen,etal.Studyofinhibitorforpipelineinoilfields[J].Mater.Prot.,2000,33(8):3-5(刘小武,彭芳明,郑家焱木等.输油管线缓蚀剂的研究[J].材料保护,2000,33(8):3-5)
[5]ChenY ,JepsonWP .EISmeasurementforcorrosionmonitoringundermultiphaseflowcondition[J].Electrochem.Acta,1999,(44):4453-4464
[6]WangHB ,HongT ,JepsonWP ,etal,Characterizationofinhibitorandcorrosionproductfilmusingelectrochemicalimpedancespectroscopy(EIS)[A].Corrosion2001[C].Houston,2001,01023
[7]SmartJS .Themeaningoftheapi-rp-14-eformulaforerosioncor rosioninoilandgasproduction[A].Corrosion91[C].1991,468
[8]WangJia,CaoChu′nan.Astudyofanodicdesorptiononinhibitor,partⅣextremevaluephenomenaofconcentration[J].J.Chin.Soc.Corros.Prot.,1996,16(1):15-19(王佳,曹楚南.缓蚀剂阳极脱附现象的研究,Ⅳ缓蚀剂浓度极值现象[J].中国腐蚀与防护学报,1996,16(1):15-19)
[9]TanYJ,BaileyS ,KinsellaB .Aninvestigationoftheformationandde structionofcorrosioninhibitorfilmsusingelectrochemicalimpedancespectroscopy(EIS)[J].Corros.Sci.,1996,38(9):1545-1561
[10]XuHaibo.SERSandelectrochemicalstudyontheinhibitionmechanismofadsorbedinhibitor[D].Shenyang:InstituteofCorrosionandProtec tion,TheChineseAcademyofSciences,1997.47-56(徐海波.吸附型缓蚀剂作用机制的电化学和表面增强拉曼光谱研究[D].沈阳:中国科学院金属腐蚀与防护研究所,1997.47-56)

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[4]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[5]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[6]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[7]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[8]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[9]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[10]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[11]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[12]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[13]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[14]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[15]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.

Viewed

Full text

Abstract

Cited

Shared

Discussed