气相环境中无机盐微粒沉积金属表面的电位分布

王佳

中科院青岛海洋研究所

Potential Distribution Over the Metal with Salt Particle Deposition in Atmosphere

Jia WANG

中科院青岛海洋研究所

全文: PDF(285 KB)

摘要: 使用扫描Kelvin探头参比电极技术研究了气相环境中无机盐微粒沉积诱发金属腐蚀过程的电位分布特征。结果表明，金属电位分布的变化与无机盐的种类和环境相对湿度有密切关系。在较低相对湿度下，无机盐的沉积不会改变金属表面均匀的电位分布；在较高相对湿度下，沉积无机盐位置的电位首先会形成电位深谷，然后深谷周围区域的电位逐渐升高，形成火山型不均匀电位分布。Na2SO4、NaCl和KCl等无机盐在Zn和钢表面沉积均可观察到这种电位分布的变化。无机盐的沉积诱发的不均匀电位分布在金属表面形成了阴极区和阳极区，构成了腐蚀原电池，从而开始了大气腐蚀过程。

关键词 ：电位分布, 大气腐蚀, Kelvin, 探头

Abstract：Potential distributions of atmospheric corrosion caused by salt particle deposition were investigated using scanning Kelvin probe technique. The results indicate that the changes in potential distribution depended on the type of the salts and the relative humidity of the environment. At lower relative humidity, the potential distribution over the metal with salt particl deposition remained uniform. When relative humidity is higher than RHoss(Relative Humidity over Saturated Solution),however, the potentials around the salt particle deposition shifted negatively, forming a lower potential valley , and then the potentials outside the valley gradually moved positively, leading to volcano type of the heterogeneous potential distribution. This phenomenon can be observed on zinc and steel with the salt particle deposition such as sodium sulfate, sodium chloride and potassium chloride. The nonuniform potential distribution caused by the deposition of salt particle built-up anode and cathode which forms corrosion battery on the metal surface. Then, the atmospheric corrosion was initiated and propagated.

Key words： potential distribution atmospheric corrosion Kelvin probe

收稿日期: 2003-02-20

ZTFLH:

TG172.6

通讯作者: 王佳 E-mail: jwang@ms.qdio.ac.cn

Corresponding author: Jia WANG E-mail: jwang@ms.qdio.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王佳
44.8K

引用本文:

王佳 . 气相环境中无机盐微粒沉积金属表面的电位分布[J]. 中国腐蚀与防护学报, 2004, 24(1): 1-5 .
Jia WANG. Potential Distribution Over the Metal with Salt Particle Deposition in Atmosphere. J Chin Soc Corr Pro, 2004, 24(1): 1-5 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I1/1

[1]AskeyA ,LyonSB ,ThompsonGE ,etal.Theeffectoffly-ashparicu lateontheatmosphericcorrosionofzincandmild-steel[J].Corros.Sci.,1993,34:1055
[2]LloydGO .25yearsofresearchinatmosphericcorrosion[J].Br.Corros.J .,1990,25(1):31
[3]LobnigRE ,SiconolfiDJ ,Psota-KeltyL ,etal.Atmosphericcorrosionofzincinthepresenceofammoniumsulfateparticles[J].J .Elec trochem.Soc.,1996,143(5):1539
[4]SkerryBS ,JohnsomnJB ,WoodGC .Corrosioninsmoke,hydrocarbonandSO/sub2/pollutedatmospheres.Ⅲ.thegeneralbehaviourofzinc[J].Corros.Sci.,1988,28:721
[5]SanyalB ,BhadwarDV .Theeffectoforientationofspecimensonthecorrosionratesofsteelinoutdoorexposure[J].J .Sci.Industr.Res.,1962,21D :243
[6]SinghaniaGK ,LaiB ,SanyalB .Corrosionofmetalsbycoppersulphate[J].LabdevJ .Sci.Tech.,1973,11A :17
[7]SvenssonJE ,JohanssonLG .Alaboratorystudyoftheinitial-stagesoftheatmosphericcorrosionofzincinthepresenceofNaClinfluenceofSO2 andNO2[J].Corros.Sci.,1993,34:721
[8]LobnigRE ,FrankenthalRP ,SiconolfiDJ,SinclairJD .Theeffectofsubmicroammoniumsulfateparticlesonthecorrosionofcopper[J].J .Electrochem.Soc.,1993,140(7):1902
[9]StratmannM ,WolpersM ,StrechelH ,FeserR .Useofascanning-kelv inprobeintheinvestigationofelectrochemicalreactionsatthemetal/polymerinterface[J].Ber.Bunsebges.Phys.Chem.1991,95(11):365
[10]WolpersM ,StratmannM ,ViefhausH ,StrechelH .Thestructureandsta bilityofmetalsurfacesmodifiedbysilane-Langmuir-Blodgettfilm[J].ThinSolidFilms,1992,210/211:592
[11]HanLT ,MansfeldF .Scanningkelvinprobeanalysisofweldedstainlesssteel[J].Corros.Sci.,1997,39(1):199
[12]AraokaA ,NishikataA ,TsuruT .Kelvinprobemeasurementonpotentialdistributionofsteelsunderwet-dryconditionsinmarineatmosphere[A].ProceedingsoftheInternationalSymposiumofMarineCorrosionandControl[C].Qingdao,July29-Aug.1,2000,167
[13]WangJia,TsuruT .ElectrochemicalstudyonthecathodicreactionofmetalcorrosionunderthinwaterlayerusingKelvinprobereferenceelectrode[A].Proceedingsof13 thInternationalCorrosionCongress[C].Melbourne,Australia,November25-29,1996,415
[14]SchmutzP ,FrankelGS .CharacterizationofAA2024-T3byscanningKelvinprobeforcemicroscopy[J].J.Electrochem.Soc.,1998,145(7):2285
[15]TaharaAkira,KodamaToshiaki.PotentialdistributionmeasurementingalvaniccorrosionofZn/FecouplebymeansofKelvinprobe[J].Cor ros.Sci.,2000,42:655
[16]O’BrienFEM .Thecontrolofhumiditybysaturatedsaltsolution[J].J.ScientificInstrumentsandPhysicalinIndustry,1948,25(3):73-76

[1]	白苗苗, 白子恒, 蒋立, 张东玖, 姚琼, 魏丹, 董超芳, 肖葵. H62黄铜/TC4钛合金焊接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 159-166.
[2]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[3]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[4]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[5]	邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[6]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[7]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[8]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[9]	张新新,高志明,胡文彬,伍志鹏,韩连恒,卢丽花,修妍,夏大海. Q235钢在薄液膜下腐蚀行为与图像信息的相关性研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[10]	张鑫,戴念维,杨燕,张俊喜. 模拟工业环境下直流电场对金属Zn腐蚀机理的影响[J]. 中国腐蚀与防护学报, 2017, 37(5): 451-459.
[11]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[12]	孙霜青,郑弃非,李春玲,王秀民,胡松青. 腐蚀产物对纯Al 8A06长期大气腐蚀行为影响的研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 110-116.
[13]	白子恒,黄运华,李晓刚,杨浪,董超芳,颜利丹,肖葵. 硫硼酸阳极氧化处理的7050铝合金在工业海洋大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(6): 580-586.
[14]	李东亮,付贵勤,朱苗勇. 湿热工业海洋大气中Si对桥梁钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(5): 433-440.
[15]	刘艳洁,王振尧,柯伟. 纯Al在3种典型沿海,工业和乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(1): 47-51.

Viewed

Full text

Abstract

Cited

Shared

Discussed