南海榆林海域环境因素对钢局部腐蚀的影响

刘大扬;魏开金;李文军

洛阳船舶材料研究所

INFLUENCE OF ENVIRONMENTAL FACTORS IN YULIN AREA OFTHE SOUTH CHINA SEA ON LOCALIZED CORROSION OF STEELS

Dayang Liu;Kaijin Wei;Wenjun Li

洛阳船舶材料研究所

全文: PDF(259 KB)

摘要: 采用典型钢宏观海生物实海验证腐蚀试验，测试分析钢样锈层中主要腐蚀细菌、FeS和钙盐沉淀物.结果表明，由于南海榆林海域水温较高，海生物一年四季生长旺盛，在钢样表面呈不均匀附着，使钢样表面电化学不均匀性增大；榆林站钢样锈层中几种好氧菌及厌氧的硫酸盐还原菌比温度较低的青岛站的高几倍至3个数量级，并呈聚集分布；几种钢样腐蚀产物中的FeS含量榆林比青岛高01～1倍左右，南海榆林海域细菌局部腐蚀效应较大，这是加剧钢的局部腐蚀的两个重要因素.

关键词 ：钢, 海洋环境, 局部腐蚀

Abstract：The severe localized corrosion of steels in Yulin a r ea of the South China Sea was analyzed by the use of macroscopic testing of seaw ater corrosion of typical steels induced by marine organisms,testing of major co rrosive bacteria and FeS in the rust layer on steel specimens and testing of cal cium deposits in the rust layer on steel specimens.The results reveal that the m arine organisms grow vigorously all year round due to rather high temperature of seawater in this area and result in uneven fouling to the surface of steel speci mens,which increases the electrochemical heterogeneity of the surface of steel s pecimens,the amounts of several aerobic bacteria and anaerobic SRB in the rust l ayer on steel specimens exposed in Yulin testing station are several times to th ree orders of magnitude larger than those on steel specimens exposed in Qingdao testing station,where the temperature of seawater is lower,and show collective d istribution;the content of FeS in the corrosion product on steel specimens expo sed in Yulin testing station is 0.1 times to twice higher than that of steel spe cimens exposed in Qingdao testing station.High Content of FeS and severe localiz ed corrosion induced by bacteria are two important factors for aggravation of lo calized corrosion of steels in Yulin area of the South China Sea.

Key words： steel marine environment localized corrosion

收稿日期: 2002-08-19

ZTFLH:

TG172.5

通讯作者: 刘大扬

Corresponding author: Dayang Liu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘大扬
	魏开金
	李文军
44.8K

引用本文:

刘大扬; 魏开金; 李文军 . 南海榆林海域环境因素对钢局部腐蚀的影响[J]. 中国腐蚀与防护学报, 2003, 23(4): 211-216 .
Dayang Liu, Kaijin Wei, Wenjun Li. INFLUENCE OF ENVIRONMENTAL FACTORS IN YULIN AREA OFTHE SOUTH CHINA SEA ON LOCALIZED CORROSION OF STEELS. J Chin Soc Corr Pro, 2003, 23(4): 211-216 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I4/211

[1]SchumacherM .SeawaterCorrosionHandbook[M ].Beijing:Nation alDefenceIndustryPress.1985,4:547-580([美]M .舒马赫编,李大超,杨荫等译.海水腐蚀手册[M ].北京:国防工业出版社,1985,4:547-580)
[2]WagnerP ,LittleB .Impactofalloyingonmicrobiologicallyinflu encedcorrosion-areview[J].MaterialsPerformance,September1993:65-68
[3]LeeTS ,etal.Theeffectofenvironmentalvariablesoncrevicecor rosionofstainlesssteelinseawater[J].MaterialsPerformance,July1984:9-15
[4]NevilleA ,etal.Surfacescalesinseawatersystems:effectsoftheirformationoncorrosionbehaviorofengineeringsteels[J].Br.Cor ros.J.,1997,32(4):279
[5]HuangSG ,etal.Influenceofmarinefoulingorganismsoncorrosionofsomematerials[A].Proceedingsof1979SymposiumonCorro sionandProtection(PartofSeawater,IndustrialWaterandBiologi calCorrosion)[C].Beijing:TheAcademicPress,1982,10:370-375(黄尚高等.海洋附着生物对某些材料腐蚀的影响[A].1979年腐蚀与防护学术报告会议论文集(海水、工业水和生物部分)[C].北京:科学出版社,1982,10:370-375)
[6]TheCompilingCommitteeofChinaSocietyforCorrosionandPro tectionforMetalCorrosionHandbook.MetalCorrosionHandbook[M].Shanghai:ShanghaiAcademicPress,1987,6:119(中国腐蚀与防护学会《金属腐蚀手册》编委会编.金属腐蚀手册[M].上海:上海科学出版社,1987,6:119)

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[4]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[5]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[6]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[7]	刘洋, 吴进怡, 闫小宇, 柴柯. 海洋环境中芽孢杆菌对聚氨酯清漆涂层分解的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[8]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[9]	王雷, 董俊华, 韩达, 梁坚坤, 李权, 柯伟. 含铜钢在1150 ℃高温保温条件下的铜偏聚现象[J]. 中国腐蚀与防护学报, 2020, 40(6): 545-552.
[10]	刘晓, 王海, 朱忠亮, 李瑞涛, 陈震宇, 方旭东, 徐芳泓, 张乃强. 电站用奥氏体耐热钢HR3C与Sanicro25在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[11]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[12]	李子运, 王贵, 罗思维, 邓培昌, 胡杰珍, 邓俊豪, 徐敬明. 热带海洋大气环境中EH36船板钢早期腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[13]	李琳, 陈义庆, 高鹏, 艾芳芳, 钟彬, 伞宏宇, 杨颖. 除冰盐环境下桥梁钢的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[14]	翟思昕, 杨幸运, 杨继兰, 顾剑锋. 淬火-配分-回火钢在模拟海水环境中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[15]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.

Viewed

Full text

Abstract

Cited

Shared

Discussed