纳米化对K38G合金900℃涂盐热腐蚀行为的影响

中国腐蚀与防护学报

2003, Vol. 23

Issue (1): 1-6

研究报告

本期目录 | 过刊浏览

纳米化对K38G合金900℃涂盐热腐蚀行为的影响

耿树江;朱圣龙;王福会

中科院金属所;金属腐蚀与防护国家重点实验室

THE EFFECT OF NANOCRYSTALLIZATION ON HOT CORROSION BEHAVIOR OF K38G ALLOY AT 900℃

Shujiang Geng;Shenglong Zhu;Fuhui Wang

中科院金属所;金属腐蚀与防护国家重点实验室

全文: PDF(318 KB)

摘要: 通过磁控溅射方法在K38G合金上沉积了一层与其同成分的纳米晶涂层.研究了铸态K38G合金及其纳米晶涂层在900℃的涂盐(盐的成分为75%Na2SO4+2 5%K2SO4)热腐蚀行为.结果表明：当涂薄盐膜时(08 mg/cm2)，纳米晶涂层表面生成一层连续的Al2O3膜，消除了内硫化；当涂厚盐膜时(3 mg/cm2)，纳米晶涂层表面氧化产物为Al2O3、Cr2O3和TiO2混合氧化物，虽然没有消除内硫化，但纳米晶涂层仍然提高了合金的抗热腐蚀性能.并讨论了纳米晶涂层的抗热腐蚀机理.

关键词 ： K38G合金, 纳米晶涂层, 热腐蚀

Abstract：The sputtered nanocrystalline coating of K38G alloy was obtained by magnetron sputtering.The effect of nanocrystallization on the h ot corrosion behavior of K38G alloy at 900℃ was studied.The results indicated t hat the internal sulfidation was eliminated for the coating by pre-deposition wi th 0.8 mg/cm2 of 75%Na2SO4+25%K2SO4.Although the internal sulfides wer e still formed for the coating by pre-deposition with 3 mg/cm2 of 75%Na2SO 4+25%K2SO4,the hot corrosion resistance of K38G alloy was clearly enhanced t hrough nanocrystallization.The hot corrosion mechanism was proposed.

Key words： K38G sputtered nanocrystalline coating hot corrosion

收稿日期: 2001-07-13

ZTFLH:

TG174.4

通讯作者: 耿树江

Corresponding author: Shujiang Geng

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	耿树江
	朱圣龙
	王福会
44.8K

引用本文:

耿树江; 朱圣龙; 王福会 . 纳米化对K38G合金900℃涂盐热腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2003, 23(1): 1-6 .
Shujiang Geng, Shenglong Zhu, Fuhui Wang. THE EFFECT OF NANOCRYSTALLIZATION ON HOT CORROSION BEHAVIOR OF K38G ALLOY AT 900℃. J Chin Soc Corr Pro, 2003, 23(1): 1-6 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I1/1

[1]WangF ,LouH ,BaiL .MagnetronsputteredCoCrAlYcoatingsonsuperalloyIN738[J].Chin.J .Met.Sci.Tech.,1990,6:61
[2]LouH ,WangF ,XiaB ,ZhangL .High-temperatureoxidationre sistanceofsputteredmicro-grainsuperalloyK38G [J].Oxid.Met.,1992,38:299
[3]LouH ,WangF ,ZhuS ,XiaB ,ZhangL .OxideformationofK38Gsuperalloyanditssputteredmicrograinedcoating[J].Surf.Coat.Tech.,1994,63:105
[4]WangF .TheeffectofnanocrystallizationontheselectiveoxidationandadhesionofAl2O3scales[J].Oxid.Met.,1997,48:215
[5]WangF ,YoungDJ .EffectofnanocrystallizationonthecorrosionresistanceofK38GsuperalloyinCO +CO2 atmospheres[J].Oxid.Met.,1997,48:497
[6]GoebelJA ,PettitFS .Na2SO4-inducedacceleratedoxidation(hotcorrosion)ofnickel[J].Metall.Trans.,1970,1:1943
[7]GoebelJA ,PettitFS ,GowardGW .Mechanismsforthehotcor rosionofnickel-basealloys[J].Metall.Trans.,1973,4:261
[8]ZhangYS .SolubilityofCr2O3infusedNa2SO4at1200K[J].J .Electrochem.Soc.,1986,133:655
[9]WangMC ,JinZJ,etal.Structureandhot-corrosionresistancepropertiesofM 38superalloyinlaser-irradiatedzones[J].J .Chi neseSocietyforCorrosionandProtection,1986,6:65(王茂才,金柱京等.M 38合金激光辐照层的结构及其抗热腐蚀性能[J].中国腐蚀与防护学报,1986,6:65)
[10]ZhangY .DissolutionbehaviorofmetaloxidesinfusedNa2SO4[J].J .ChineseSocietyCorrosionandProtection,1989,9:121(张允书.金属氧化物在熔融Na2SO4中的溶解行为[J].中国腐蚀与防护学报,1989,9:121)

[1]	陈超,梁艳芬,梁天权,满泉言,罗毅东,张修海,曾建民. 稀土复合掺杂ZrO₂陶瓷涂层抗Na₂SO₄+NaVO₃热腐蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 291-298.
[2]	虞礼嘉,梁文萍,林浩,缪强,黄彪子,崔世宇. 激光重熔YSZ热障涂层950 ℃的热腐蚀行为[J]. 中国腐蚀与防护学报, 2019, 39(1): 77-82.
[3]	陈浩,陈庆,辛丽,时龙,朱圣龙,王福会. DD98M纳米晶AlSi渗层制备及抗高温腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.
[4]	王希靖, 王博士, 杨超, 杨艳, 沈斌. 纯Ni母材及焊缝在熔融Na₂SO₄-K₂SO₄中热腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 495-501.
[5]	王喜忠,吴建颢,彭徽,郭洪波,宫声凯. 电子束物理气相沉积La₂Ce₂O₇热障涂层的高温燃气热腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 36-40.
[6]	刘光明,刘康生,毛晓飞,万中平,黄健航,于明明,汪元奎. T91钢在KCl+Na₂SO₄+K₂SO₄熔融盐中的热腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 23-28.
[7]	杨波,李茂东,刘光明,汪元奎,刘康生,翟伟,黄健航. 超音速喷涂Inconel 625/NiCr合金涂层的热腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(5): 483-488.
[8]	吴多利, 张洪宇, 韦华, 郑启, 金涛, 孙晓峰. 4种改性的铝化物涂层对DZ38G合金热腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2014, 34(6): 502-506.
[9]	崔玉卉,胡锐,张铁邦,李健,寇宏超,李金山. Fe基非晶/纳米晶涂层的微结构及其在H₂O₂溶液中的腐蚀性能[J]. 中国腐蚀与防护学报, 2012, 32(4): 317-321.
[10]	王理,刘春阳,韩振宇,佟文伟. 燃气轮机涡轮零部件及材料热腐蚀行为与评价方法研究[J]. 中国腐蚀与防护学报, 2011, 31(5): 399-403.
[11]	徐仰涛,夏天东,闫健强. 合金元素对新型Co-Al-W合金热腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(6): 457-464.
[12]	韦华;黄粮;梁静静;孙晓峰;管恒荣;胡壮麒. Re对NiCrAlY涂层热腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(2): 150-154.
[13]	朱明李美栓周延春. Ti₃Al基合金表面两种Cr_1-xAl_xN（x=0.18, 0.47）涂层热腐蚀性能[J]. 中国腐蚀与防护学报, 2009, 29(4): 306-311.
[14]	于忠锋; 郑志; 刘恩泽; 于永泗; 朱耀宵 . 两种低偏析镍基高温合金抗热腐蚀性能的研究[J]. 中国腐蚀与防护学报, 2008, 28(5): 277-281 .
[15]	田秀娟; 王福会; 李庆芬 . 搪瓷／NiCrAlY复合涂层的抗高温氧化及热腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(6): 344-350 .

Viewed

Full text

Abstract

Cited

Shared

Discussed