不锈钢在海水飞溅区的腐蚀行为

中国腐蚀与防护学报

2002, Vol. 22

Issue (4): 211-216

研究报告

本期目录 | 过刊浏览

不锈钢在海水飞溅区的腐蚀行为

黄桂桥

青岛海洋腐蚀研究所

CORROSION OF STAINLESS STEELS IN SEAWATER SPLASH ZONE

青岛海洋腐蚀研究所

全文: PDF(178 KB)

摘要: 总结了5种不锈钢在青岛海域飞溅区暴露16年的腐蚀行为和规律.2Cr13在飞溅区不能维持其表面的钝态，耐蚀性较差.含16%Cr以上的不锈钢在飞溅区有较好的耐蚀性.1Cr18Ni9Ti、00Cr19Ni10和000Cr18Mo2在飞溅区暴露2～4年间，F179 在1、2年间，点蚀速度较大，此后它们的点蚀深度随时间无明显加深.不锈钢在飞溅区的点蚀密度随暴露时间增大.增加Cr含量、添加Mo能提高不锈钢在飞溅区的耐蚀性.

关键词 ：腐蚀, 不锈钢, 海水, 飞溅区

Abstract：Corrosion results of 5 types of stainless steels ex posed to splash zone at Qingdao Sea area of China were obtained.Corrosion behavi or and law of stainless steels in splash zone were summarized.2Cr13 could not ke ep passive state in splash zone.Its corrosion resistance was poor.Stainless stee ls containing more than 16% Cr shown good corrosion resistant in splash zone,and their maximum pitting depths at Qingdao Sea area for 16 years exposure were les s than 025mm.It was found that pitting rate is big for 1Cr18Ni9Ti,00Cr19Ni10,0 00 Cr18Mo2 during the 2 to 4 years and for F179 during 1,2 years,after which the pi tting depth deepened not obviously with exposure time.Pit density of stainless s teels in splash zone increased with exposure time.Crevice corrosion of stainless steels in splash zone formed and grew more easily than pitting corrosion.Increas ing Cr content and adding Mo enhanced corrosion resistance in stainless steels i n splash zone.Corrosion behavior of stainless steels in splash zone was similar t o their corrosion behavior in marine atmosphere.Stainless steels in splash zone corroded seriously than ones in marine atmosphere.

Key words： corrosion stainless steel seawater splash zone

收稿日期: 2001-03-02

ZTFLH:

GB172.5

通讯作者: 黄桂桥

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	黄桂桥
44.8K

引用本文:

黄桂桥 . 不锈钢在海水飞溅区的腐蚀行为[J]. 中国腐蚀与防护学报, 2002, 22(4): 211-216 .

链接本文:

https://www.jcscp.org/CN/Y2002/V22/I4/211

[1]SchumacherM .SeawaterCorrosionHandbook[M ].ParkRidge,NewJersey:NoyesDataCorporation,1979,26
[2]WarrenN .TranslatedbyWuMin,ZhangYi.MetalCorrosionInBoats[M ].Beijing:NationalDefenceIndustryPublishingHouse.1987,19([英]奈杰尔·沃伦著.吴敏,张义译.船舶中的金属腐蚀[M ].北京:国防工业出版社,1987,19)
[3]HuangGuiqiao.Corrosionofmetallicmaterialsinmarinesplashzone[J].MaterialsProtection.1999,32(2):28(黄桂桥.金属材料在海洋飞溅区的腐蚀[J].材料保护,1999,32(2):28)
[4]HuangGuiqiao.Corrosionofstainlesssteelsinmarineenvironment[J],CorrosionandProtection,1999,20(9):392.(黄桂桥.不锈钢在海洋环境中的腐蚀[J].腐蚀与防护,1999,20(9):392)
[5]ChengZhuoyuan,LinZhijian,SongWensang.CorrosionbehaviorandregularityofcorrosiondataforstainlesssteelsinXiamenSeaarea[J].CorrosionandProtection,1999,20(7):303(陈卓元,林志坚,宋文桑.不锈钢在厦门海域的腐蚀行为及数据规律性研究[J].腐蚀与防护,1999,20(7):303)
[6]GB5776-86,Methodforsurfaceseawaterexposurecorrosiontestsofmetallicmaterials[S].(GB5776-86,金属材料表面海水常规暴露腐蚀试验方法[S].)
[7]JohnsonKE .Roleofinclusionintheatmosphericpittingofstain lesssteels[J].Br.Corros.J .,1980,15(3):123
[8]TochiharaM ,UjiroT ,YazawaY ,etal.Atmosphericcorrosionofstainlesssteelsusedfortheeavesofbuilding[J].MaterialsPerfor mance,1996,35(12):58
[9]KearnsJR ,BarkowskiLR .Appearanceandcorrosionofstainlesssteelsintheatmosphere[J].MaterialsPerformance,1988,27(2):47
[10]LiangCaifeng,YuChunjuan,HouWentai.Astudyofatmosphericcorrosionofstainlesssteels-asummaryof12yearexposuretest ing[J].J .ChineseSocietyforCorrosionandProtection,1999,19(4):227(梁彩凤,郁春娟,侯文泰.不锈钢的大气腐蚀研究—12年暴露试验总结[J].中国腐蚀与防护学报,1999,19(4):227)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[12]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[13]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[14]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[15]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.

Viewed

Full text

Abstract

Cited

Shared

Discussed