原位测试研究土壤环境因素对碳钢的腐蚀影响

孙成;韩恩厚;李洪锡

中国科学院金属研究所

IN-SITU STUDY OF CORROSION OF MILD STEEL AFFECTED BY SOIL FACTORS

Cheng Sun;Enhou Han;Hongxi Li

中国科学院金属研究所

全文: PDF(122 KB)

摘要: 在沈阳土壤腐蚀试验中心站，用便携式土壤腐蚀测试仪及土壤环境因素测试仪现场原位测试了土壤的电导、氧化还原电位、地温等土壤理化性质，以及碳钢的腐蚀速率变化情况.试验结果表明，土壤的电导受地温的影响显著，土壤中微生物腐蚀随着地温升高而显著增强.在春夏季节交替时(3月～7月)碳钢的腐蚀速率最大，而在冬季(12月～3月)碳钢的腐蚀速率最低.原位测试结果与失重值对比表明，碳钢的土壤腐蚀速率受地温的影响较大.

关键词 ：碳钢, 土壤腐蚀, 原位测试, 环境因素

Abstract：In situ measurement of corrosion rate of mild steel and soil factors has been carried out in Shenyang soil site.It showed that soil conductivity and soil salt content ，corrosion rate of mild steel increased wit h the raising of soil temperature.At the time of alternate spring and summer (f rom April to July),on account of underground temperature and soil conductance ri sing acutely,corrosion rate of mild steel was the highest.The error of copper be tween the in-situ corrosion and soil natural corrosion was not high,and the erro r reduced gradually with the extension of the test period.Therefore,the instrume nt of soil corrosion can measure quickly the corrosion rate of mild steel in-sit u.

Key words： mild steel soil corrosion in-situ

收稿日期: 2001-04-10

ZTFLH:

TG172.4

通讯作者: 孙成

Corresponding author: Cheng Sun

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	孙成
	韩恩厚
	李洪锡
44.8K

引用本文:

孙成; 韩恩厚; 李洪锡 . 原位测试研究土壤环境因素对碳钢的腐蚀影响[J]. 中国腐蚀与防护学报, 2002, 22(4): 207-210 .
Cheng Sun, Enhou Han, Hongxi Li. IN-SITU STUDY OF CORROSION OF MILD STEEL AFFECTED BY SOIL FACTORS. J Chin Soc Corr Pro, 2002, 22(4): 207-210 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I4/207

[1]RomanoffM .UndergroundCorrosion[S].NationalBureauofStan dardsCircular579,1957
[2]SunCheng,etal.Corrosionofstainlesssteelsinsoils[J].Corros.Sci.Prote.Technol.,1999,11(2):94.(孙成等,不锈钢在土壤中腐蚀规律研究[J].腐蚀科学与防护技术,1999,11(2):94)
[3]SunCheng,etal.AresearchoncorrosionofDagangseasidesoil[J].EnvironmentalScienceandTechnology,1999,2:1(孙成等.大港海滨盐土的腐蚀性研究[J].环境科学与技术,1999,2:1)
[4]SunCheng,etal.SaltconcentrationdifferencemacrocellcorrosionforLC4aluminumalloyinsoil[J].TheChineseJournalofNonfer rousMetals,2000,10(5):653(孙成等.铝合金的土壤盐浓差宏电池腐蚀[J].中国有色金属学报,2000,10(5):653)
[5]SunCheng,etal.Corrosionbehaviorof1Cr18Ni9Tistainlesssteelinsoils[J].ChineseJournalofMaterialsResearch,2000,14(sup pl.):84(孙成等.1Cr18Ni9Ti不锈钢在土壤中腐蚀规律研究[J].材料研究学报,2000,14(增):84)
[6]SunCheng,YINYaode.CorrosionBehaviorofLY11AluminumAlloyinSoils[A].Trans.ofNonferrousMetalSocietyofChina[C].1999,9(4)
[7]SunCheng.Corrosionof1Cr13stainlesssteelinsoils[J].ActaMet allurgicaSinica,1999,12(5):624
[8]SchwerdtfegerWJ ,McDormanON .J.Electrochem.Soc.,1952,99:407
[9]SternM .Corrosion,1958,14:440
[10]ChangSouwen,etal.Developmentandapplicationofportablesoilcorrosionmeter[J].Oil&GasStorageandTransportation,1989(1):30(常守文等.发展和应用便携式土壤腐蚀测量仪[J].油气储运,1989(1):30)
[11]CaoChu′nan.Amethodofcorrosioncurrentaccordingtoweakpo larizationcurve[J].CorrosionandProtection,1978,1:21(曹楚南.一种根据弱极化区的极化曲线测定腐蚀电流的方法[J].腐蚀与防护,1978,1:21)
[12]KuaiXiaoming,etal.Anewcorrosioncurrentmeasurementmeter[J].Corros.Sci.Prote.Technol.,1995,7(2):32(蒯晓明等.智能腐蚀电流测量仪的研制[J].腐蚀科学与防护技术,1995,7(2):32)

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[3]	朱亦晨,刘光明,刘欣,裴锋,田旭,师超. 红壤地区接地材料现场埋样与加速腐蚀实验的相关性研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 550-556.
[4]	许萍,张硕,司帅,张雅君,汪长征. EPS的主要成分-蛋白质、多糖抑制碳钢腐蚀机理研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 176-184.
[5]	钟显康,扈俊颖. 恒定的pH值和Fe²⁺浓度下X65碳钢的CO₂腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[6]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[7]	乔越, 朱志平, 杨磊, 刘志峰. 高温状态下锅炉给水氧化还原电位监测与模拟实验研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[8]	彭晚军, 丁纪恒, 陈浩, 余海斌. 生物基缓蚀剂糠醇缩水甘油醚的缓蚀性能及机理[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[9]	钱备, 刘成宝, 宋祖伟, 任俊锋. 纳米容器改性环氧涂层对Q235碳钢的防腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.
[10]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[11]	于利宝, 闫茂成, 王彬彬, 舒韵, 许进, 孙成. 酸性土壤环境中Q235钢的微生物腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 10-17.
[12]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[13]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[14]	程庆利,陶彬,刘栓,刘全桢,张卫华,田松柏,王立平. 原油沉积水对Q235B碳钢的腐蚀影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 126-134.
[15]	郝永胜,Luqman Abdullahi SANI,宋立新,徐国宝,葛铁军,方庆红. 中性和酸性溶液中Q235碳钢表面沉积植酸转化膜的耐蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.

Viewed

Full text

Abstract

Cited

Shared

Discussed