晶须对铝基复合材料应力腐蚀开裂行为的影响

胡津;罗仁胜;姚忠凯

哈尔滨工业大学材料科学与工程学

EFFECT OF WHISKER ON STRESS CORROSION CRACKINGBEHAVIOR OF ALUMINUM MATRIX COMPOSITES

;;

哈尔滨工业大学材料科学与工程学

全文: PDF(175 KB)

摘要: 采用双悬臂梁试验，研究了碳化硅晶须增强纯铝基及碳化硅晶须增强2024铝基复合材料和2024铝合金在3.5%NaCl溶液中的应力腐蚀(SCC)开裂行为，探讨了晶须对复合材料应力腐蚀开裂行为的影响.结果表明，晶须的存在改变了材料的应力腐蚀特性，晶须在复合材料应力腐蚀开裂过程中具有促进和阻碍应力腐蚀裂纹扩展的双重作用 .

关键词 ：碳化硅晶须, 铝基复合材料, 应力腐蚀开裂

Abstract：Stress corrosion cracking behavior of SiCw/p-Al、 SiCw/2024Al composite and 2024 alloy in 3.5%NaCl solution have been studied by using double-cantilever-beam method.The effect of whisker on stress corrosion c racking behavior of the composites was examined.The results presented that the p rese nce of whisker changed the characters of stress corrosion of composites.Whisker plays a special role in the processing of stress corrosion cracking of the comp osites，which is both promoting and hindering the crack propagation.

Key words： SiC whisker aluminum matrix composite stress corrosi on cracking

收稿日期: 2000-02-28

ZTFLH:

TG151

通讯作者: 胡津

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	胡津
	罗仁胜
	姚忠凯
44.8K

引用本文:

胡津; 罗仁胜; 姚忠凯 . 晶须对铝基复合材料应力腐蚀开裂行为的影响[J]. 中国腐蚀与防护学报, 2001, 21(4): 240-244 .

链接本文:

https://www.jcscp.org/CN/Y2001/V21/I4/240

[1]ShiCX .AGrowthpointofmaterialsscienceandtechnology[J].MaterialsScienceProgress,1990,4(2):92-104(师昌绪.材料科学技术的生长点[J].材料科学进展,1990,4(2):97～104)
[2]FeiWD ,JiangXD ,LiC ,YaoCK .EffectofInterfacialReactionontheYoung’sModulusofAluminumBorateWhiskerRein forcedAluminiumComposite[J].J .Mater.Sci.Lett.,1996,15:1966～1968
[3]HaoYK ,Studyingsituationandprospectfornonrcontinuousreinforcedlightmetalmatrixcomposites[J].MaterialsReview.,1994,5:67-71(郝元恺.非连续增强轻金属复合材料研究现状及展望[J].材料导报,1994,5:67～71)
[4]WuRJ .Thepresentconditionandprospectsonmetalmatrixcomposites[J].ActaMetallurgicaSinica,1997,33(1):78-84(吴人洁.金属基复合材料的现状与展望[J].金属学报,1997,33(1):78～84)
[5]GengL ,OchiaiS ,WangB ,YaoCK .Effectofwhiskervolumefractiononthecoefficientofthermalexpansionandthermalcon ductivityofSiCw/6061Alcomposites[J].J .Mater.Sci.Lett.,1998,17:403～405
[6]LiWF ,MengJL ,DuSY .InfluenceofResidualThermalStrainonTensileandCompressionBehaviorofMetalMatrixCom posite[J].ActaMetallurgicaSinica,1995,31(5):B226-B232(李文方,蒙继龙,杜善义.热残余应变对金属基复合材料拉、压性能的影响[J].金属学报,1995,31(5):B226-B232)
[7]FeiWD ,LiuQY ,YaoCK .AcceleratingeffectofwhiskerontheagingprocessofSiCw/Alcomposite[J]J.Mater.Sci.Lett.,1996,15:831～835
[8]WangDZ ,YeF .Fatiguecrackpropagationofextruded19%SiCw/6061Alcompositesunder(I+II)mixed-loading[J].Scrip taMetall.Mater.,1995,32(10):1637～1640
[9]HuJ ,FeiWD ,YaoCK .Interfacialinaluminaboratewhiskerreinforcedaluminumcomposite[J].J .Mater.Sci.Lett.,1994,17:1797～1780
[10]HuJ ,LuoRS .EffectofannealingtreatmentonstresscorrosioncrackingbehaviorsofSiCw/Alcomposite[J].JournalofChi neseSocietyforCorrosionandProtection,1999,19(5):296-299(胡津,罗仁胜等.退火处理对SiCw/Al复合材料应力腐蚀开裂行为的影响[J].中国腐蚀与防护学报,1999,19(5):296-299)
[11]ChuWY ,QiaoLJ ,ChenQZ ,GaoKW .FractureandEnvironmentalFracture[M ].Beijing:SciencePress,2000.70
[12]CaoL ,LiGF ,YaoCK .StressCorrosionPropertiesofSiCw/AlCompositein3.5%NaClSolution[J].JournalofChineseSo cietyforCorrosionandProtection,1990,10(3):269(曹利,李光福等.SiCw/Al复合材料在3.5%NaCl溶液中的应力腐蚀特性[J].中国腐蚀与防护学报,1990,9:34～38)
[13]HiharaLH ,LatanisionRM .Corrosionofmetalmatrixcomposites[J].InternationalMaterialsReviews.,1994,39(6):245～263
[14]BurleignhTD .Thepostulatedmechanismsforstresscorrosioncrackingofaluminumalloys[J].Corrosion.,1991,47(2):89～93

[1]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[2]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[3]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[4]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[5]	陈旭,马炯,李鑫,吴明,宋博. 温度与SRB协同作用下X70钢在海泥模拟溶液中应力腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[6]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[7]	周霄骋, 崔巧棋, 贾静焕, 刘智勇, 杜翠薇. Cl^-浓度对316L不锈钢在碱性NaCl/Na₂S溶液中SCC行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 526-532.
[8]	张乃强,岳国强,吕法彬,曹琦,李梦源,徐鸿. Inconel625合金在高温水蒸气环境中应力腐蚀开裂裂纹扩展速率研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 9-15.
[9]	罗金恒,胥聪敏,杨东平. SRB作用下X100管线钢在酸性土壤环境中的应力腐蚀开裂行为[J]. 中国腐蚀与防护学报, 2016, 36(4): 321-327.
[10]	邓平,孙晨,彭群家,韩恩厚,柯伟. 堆芯结构材料辐照促进应力腐蚀开裂研究现状[J]. 中国腐蚀与防护学报, 2015, 35(6): 479-487.
[11]	郭跃岭,韩恩厚,王俭秋. 锻后热处理对核级316LN不锈钢在沸腾MgCl₂溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2015, 35(6): 488-495.
[12]	张志明,彭青娇,王俭秋,韩恩厚,柯伟. 核用锻造态316L不锈钢在330 ℃碱溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2015, 35(3): 205-212.
[13]	史显波, 王威, 严伟, 单以银, 杨柯. M/A组元对高强度管线钢抗H₂S性能的影响[J]. 中国腐蚀与防护学报, 2015, 35(2): 129-136.
[14]	王彬彬, 王振尧, 曹公望, 钟西舟, 柯伟. 受力的LY12和LC4铝合金在中国西部盐湖大气环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2014, 34(3): 287-293.
[15]	冯勇何德良龚德胜李菲吴建新. 国产825合金的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2013, 33(2): 164-170.

Viewed

Full text

Abstract

Cited

Shared

Discussed