铝合金阳极氧化膜上阴极电解沉积的稀土铈转化膜

李国强;李荻;李久青

北京科技大学材料学院腐蚀系

CERIUM CONVERSION COATINGS FORMED ONANODIZED ALUMINUM BY CATHODIC ELECTROLYSIS

;Di Li;Jiuqing Li

北京科技大学材料学院腐蚀系

全文: PDF(222 KB)

摘要: 通过阴极电解的方法在铝合金多孔阳极氧化膜上沉积了富铈转化膜.电解成膜溶液为含1 g /L CeCl3·7H2O和10 ml/L H2O2的水溶液.用XPS、FEM、XRD、和EDAX等分析手段对此种转化膜的组成、结构形貌进行了研究.结果表明: 这种铈转化膜的微结构与氧化膜的多孔结构紧密相关，并且随电解时间和电流密度的改变而逐渐变化；转化膜主要由三价铈化合物组成，阴极电解1 h后膜厚约140 nm，并呈非晶态特征.

关键词 ：铝合金, 阳极氧化膜, 铈转化膜, 阴极电解

Abstract：Cerium-rich conversion coatings were deposited on p orous film of anodized auminoum by cathodic electrolysis in a solution containin g 1 g/L CeCl3·7H2O and 10 ml/L H2O2.X-ray photoelectron spectroscopy (X PS),scanning electron microscopy (SEM),X-ray diffraction (XRD) and energy disper sion analyzer of X-ray (EDAX) have been used to study these cerium-containing co nversion coatings.The results revealed that the microstructure of the cerium con version coatings was closely related to the porous structure of anodized film an d changed gradually with electrolysis time and cathodic current density.The coat ing being of an amorphous nature,predominately consisted of 3-valent-state ceriu m compound,and was up to about 140nm after one-hour cathodic electrolysis.

Key words： auminoum alloy anodized film cerium conversion coating cathodic electrolysis

收稿日期: 2000-01-31

ZTFLH:

TQ153

通讯作者: 李国强

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李国强
	李荻
	李久青
44.8K

引用本文:

李国强; 李荻; 李久青 . 铝合金阳极氧化膜上阴极电解沉积的稀土铈转化膜[J]. 中国腐蚀与防护学报, 2001, 21(3): 150-157 .
Di Li, Jiuqing Li. CERIUM CONVERSION COATINGS FORMED ONANODIZED ALUMINUM BY CATHODIC ELECTROLYSIS. J Chin Soc Corr Pro, 2001, 21(3): 150-157 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2001/V21/I3/150

[1]HintonBRW ,ArnottDR ,RyanNE .Theinhibitionofaluminumcorrosionbyceriumcations[J].MetalsForum,1984,7(4):211-217
[2]LiGQ ,LiD .Thestudyofrareearthconversioncoatingsforaluminumalloys[J].J .MaterialsEngineering,1998,(8):1-5(李国强,李荻.铝合金稀土转化膜的研究进展[J].材料工程,1998,(8):1～5)
[3]LiGQ .Thestudyofrareearthceriumconversioncoatingsformedonaluminumalloysbyelectrochemicalprocess.Ph.D .disser tation,UniversityofScience&TechnologyBeijing,Beijing,2000.6(李国强.铝合金稀土铈电化学转化膜的研究[D].北京科技大学博士学位论文,2000,6)
[4]KellerF ,HunterMS ,RobinsonDLetal.Structuralfeaturesofoxidecoatingsonaluminum[J].J .theElectrochemicalSociety,1953,100(9):411～419
[5]EplingWS ,MounktKC ,HoflundBG .Surfacecharacterizationstudyofthechemicalalterationofanair-exposedpolycrystal linetinfoilduringH -atomexposures[J].AppliedSurfaceScience,1998,134:187～193
[6]ShyuJZ ,OttoK ,WatkinsWLH ,etal.CharacterizationofPd/γ-auminoacatalystscontainingceria[J].J .Catalysis,1988,114:22～33
[7]RenshawTA .Astudyofporestructuresonanodizedauminoum[J].J.ElectrochemicalSociety,1961,108(2):185～191
[8]PatermarakisP ,LenasP ,KaravassilisCh,PapayiannisG ,KineticksofgrowthofporousanodicAl2O3filmsonAlmetal[J].ElectrochemicalActa,1991,36(3/4):709～725
[9]GaoYX ,RenJJ ,NingFY .SurfaceTreatmentofAluminumAlloys[M ].Beijing:MetallurgyIndustryPress,1991,16-46(高云霞,任继嘉,宁福元.铝合金表面处理[M].北京:冶金工业出版社,1991,16～168)
[10]DavenportAJ,IsaacsHS ,KendigMW .XANESinvestigationoftheroleofceriumcompoundsascorrosioninhibitorsforalu minum[J].CorrosionSci.,1991,32(5/6):653～663
[11]AldykiewiczAJ,IsaacsHS ,DavenportAJ .Studiesofformationofcerium-richprotectivefilmsusingX -rayabsorptionnear-edgespectroscopyandrotatingdiskelectrodemethods[J].J.Electrochem.Soc.,1996,143(1):147～154
[12]XuGX .RareEarch[M ].PartI ,Beijing:MetallurgyIndustryPress,1996.(徐光宪等编.稀土[M ].北京:冶金工业出版社,1996)

[1]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[6]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[7]	夏俊捷,牛红志,刘敏,曹华珍,郑国渠,伍廉奎. 基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[8]	陈高红,胡远森,于美,刘建华,李国爱. 硫酸阳极化对2E12铝合金力学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 579-586.
[9]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.
[10]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[11]	郝利新, 贾瑞灵, 张慧霞, 张伟, 赵婷, 翟熙伟. 7A52铝合金双丝MIG焊接头的不均匀性对其表面微弧氧化膜腐蚀防护作用的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 219-225.
[12]	杨钊, 时惠英, 蒋百灵, 葛延峰, 张静, 张曼玉, 李研. 脉冲电流对1050铝合金微弧氧化过程的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 283-288.
[13]	崔晓飞, 谭晓明, 王德, 钱昂. 铝合金表面聚氨酯涂层在加速实验条件下的老化机制及规律研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 74-80.
[14]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[15]	赵苇杭, 王浩伟, 蔡光义, 董泽华. AA6061铝合金在含盐薄液膜下的局部腐蚀与缓蚀机理[J]. 中国腐蚀与防护学报, 2017, 37(4): 366-374.

Viewed

Full text

Abstract

Cited

Shared

Discussed