环境诱导氢致断裂的非比例过载效应

曹卫杰;杨晓雷;高桦

上海工程技术大学能源与环境工程研究所

THE EFFECT OF NON-PROPORTIONAL OVERLOADING ON ENVIRONMENTAL HYDROGEN INDUCED FRACTURE

CAO Weijie;YANG Xiaolei;GAO Hua (Shanghai University of Engineering Science)

全文: PDF(1048 KB)

摘要: 研究连续充氢条件下短时非比例过载对４２ＣｒＭｏ钢／０．５ｍｏｌ／ＬＨ２ＳＯ４体系氢致断裂（ＨＩＦ）寿命的影响。结果表明：短时非比例过载对于ＨＩＦ的影响较之比例过载更为严重。究其原因，从非比例过载引起裂纹偏折、残余压应力、位错屏蔽和过载损伤等方面进行了分析与讨论。

关键词 ：过载效应, 氢致断裂, 高强钢

Abstract：The effect of short period non-proportional overloading on environmental hydrogen induced fracture life of 42CrMo steel in 0.5 mol/L H2SO4solution was studied under continuous hydrogen charging condition.A weight loading system was employed in the study. Experimental results showed that non-proportional overloading might cause more severe retardation than proportional one. The mechanisms responsible for retardation of subsequent crack growth were discussed. The influence of overloading was dependent on integral effect of the following faCtors: (1) crack branching,which decreassed significantly the crack growth driving force; (2) residual compressive stresses existing in the overloading plastic zone, which reduced effective stress intensity factors; (3) effect of dislocation shielding on retarding hydrogen transportation as well as accumulation; and (4) overloading damage, which might shorten HIF life.

Key words： Overloading effect Hydrogen induced fracture High strength steel

收稿日期: 1996-06-25

基金资助:国家自然科学基金;;上海市高教科技发展基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	曹卫杰
	杨晓雷
	高桦
44.8K

引用本文:

曹卫杰;杨晓雷;高桦. 环境诱导氢致断裂的非比例过载效应[J]. 中国腐蚀与防护学报, 1996, 16(3): 181-186.
. THE EFFECT OF NON-PROPORTIONAL OVERLOADING ON ENVIRONMENTAL HYDROGEN INDUCED FRACTURE. J Chin Soc Corr Pro, 1996, 16(3): 181-186.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1996/V16/I3/181

1高烨,杨晓雷,曹卫杰．中国腐蚀与防护学报,1995,15(4):2542高烨,曹卫杰．中国腐蚀与防护学报,1991;11(2):1633高桦,曹卫杰,方昌鹏,刘树望,陈廉．中国腐蚀与防护学报,1993;13(3):2374BarberaALa,MarchettiM,TizziS．InternationalJournalofWacture,1990,43:255ChatterjeeSN．solidsStruetures,1975,11:5216SureshS．FatigueofMaterials．CambridgeUniversityPress,1991．1417PoohLPEng．Fract．Mech,1971,3:2058路民旭,郑修麟．中国腐蚀与防护学报,1994,14(3):193

[1]	周宇, 张海兵, 杜敏, 马力. 模拟深海环境中阴极极化对1000 MPa级高强钢氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 409-415.
[2]	王凯, 易耀勇, 卢清华, 易江龙, 江泽新, 马金军, 张宇. 基于窄间隙焊接的热模拟峰值温度对Q690高强钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(5): 447-454.
[3]	王玉昆, 刘静, 胡骞, 黄峰. S^2-对A710钢在NaCl溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 233-240.
[4]	黄长河;李金许;王燕斌;褚武扬;梅冬生;俞梦文;籍可镔. 重轨钢氢脆的表现形式及规律[J]. 中国腐蚀与防护学报, 1997, 17(2): 129-134.
[5]	高桦;杨晓雷;曹卫杰. 环境诱导氢致断裂的过载效应[J]. 中国腐蚀与防护学报, 1995, 15(4): 254-260.

Viewed

Full text

Abstract

Cited

Shared

Discussed