FATIGUE BEHAVIOR OF ROLLED AZ31B MAGNESIUM ALLOY IN AIR AND NaCl SOLUTION |
ZHOU Huamao; WANG Jianqiu; ZHANG Bo; HAN Enhou; ZANG Qishan |
State Key Laboratory for Corrosion and Protection;Institute of Metal Research;Chinese Academy of Sciences; Shenyang 110016 |
|
|
Abstract Fatigue crack initiation of rolled AZ31B magnesium alloy in air and NaCl solution was investigated. In air, the cracked second phases were responsible for crack initiation. While in NaCl solution, crack initiated from surface damage which was produced by pit corrosion or filiform corrosion. Increasing Cl- concentration, the crack initiation and propagation in NaCl solutions were enhanced and the fatigue lifetime was decreased.
|
Received: 29 May 2007
|
|
Corresponding Authors:
WANG Jianqiu
E-mail: jiqwang@imr.ac.cn
|
[1] Mordike B L, Ebert T. Magnesium properties-applica-\linebreak tions-potential [J].Mater. Sci. Eng., 2001, A302: 37-45
[2] Eisenmerier G, Holzwarth B. Cyclic deformation and fatigue behavior of the magnesium alloy AZ91[J]. Mater. Eng., 2001, A319: 578-582
[3] Mayer H, Papakyriacou M, Zettl B, et al. Influence of porosity on the fatigue limit of die cast magnesium and aluminum alloys[J]. Int. J. Fatigue.,2003, 25(3): 245-256
[4] Nan Z Y, Ishihara S, Goshima, et al. Scanning probe microscope observation of fatigue process in magnesium alloy AZ31 near the fatigue limit[J]. Scr. Mater.,2004, 50(4): 429-434
[5] Tokaji K, Kanakura M, Ishiizumi Y, et al. Fatigue behavior and fracture mechanism of a rolled AZ31 magnesium alloy[J]. Int. J. Fatigue.,2004, 26(11): 1217-1224
[6] Wolf B, Fleck C, Eifler D. Characterization of the fatigue behaviour of the magnesium alloy AZ91D by means of mechanical hysteresis and temperature measurements[J]. Int. J. Fatigue., 2004, 26(12): 1357-1363
[7] Shih T S, Liu W S, Chen Y J. Fatigue of as-extruded AZ61A magnesium alloy[J]. Mater. Sci. Eng., 2002, A325: 152-162
[8] Zeng R C, Han E H, Ke W, et al. Mechanism of corrosion fatigue for as-extruded magnesium alloy AZ80[J]. Chin. J. Mater. Res., 2004, 18(6): 561-567
(曾荣昌, 韩恩厚, 柯伟等. 变形镁合金AZ80的腐蚀疲劳机理 [J]. 材料研究学报,2004, 18(6): 561-567)
[9] Eliezer A, Gutman E M, Abramov E, et al. Corrosion fatigue of die cast and extruded magnesium alloys[J]. J. Light Met., 2001, 1: 179-186
[10]} Unigovski Y, Eliezer A, Abramov E, et al. Corrosion fatigue of extruded magnesium alloys[J]. Mater. Eng., 2003, A360: 132-139
[11]} Srivatsan T, Sudarshan T. Mechanisms of fatigue crack initiation in metals[J]. J. Mater. Sci., 1998, 23: 1521-1533
[12]} Suresh S. Fatigue of Materials[M]. Cambridge: Cambridge University Press. 1998
[13]} Chen J, Wang J Q, Han E H, et al. States and transport of hydrogen in the corrosion process of an AZ91 magnesium alloy in aqueous solution[J]. Corros. Sci.,2008, 50: 1292-1305
[14]} Zeng R C, Zhang J, Huang W J, et al. Review of studies on corrosion of magnesium alloys[J]. Trans. Nonferrous. Met. Soc.Chin., 2006, 16: 763-771
[15]} Hikmet A, Sadri S. Studies on the influence of chloride ion concentration and pH on the corrosion and electrochemical behavior of AZ63 magnesium alloy[J]. Mater. Des., 2004, 25: 637-643
|
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|