| Study of Galvanic Corrosion of Carbon Steel/Titanium and Carbon Steel/Titanium/Navel Brass in Seawater |
| ; |
| 中国海洋大学化学化工学院 |
|
|
|
|
Abstract The natural corrosion potential,corrosion rate and
steady-stat
e polarization curves of Q235B carbon steel,TA2 titanium and navel brass in seaw
ater were measured.The galvanic current,galvanic potential and galvanic corrosio
n rate of anode and cathode of couple with different area ratio,at different tem
perature and different velocity of seawater were measured.According to the data
of the couple with different area ratio,a dynamic polarization curve of Q235B ca
rbon steel was obtained.The galvanic corrosion characters of Q235B carbon steel
/TA2
titanium and Q235B carbon steel/TA2 titanium/navel brass in seawater were invest
igated.The results showed that corrosion rate of anode increased with increasing
of area ratio of cathode/anode,temperature and velocity of seawater.But t
here was a limited area ratio.The corrosion rate of anode did not increase when
area ratio of cathode/anode was larger than the limit.When the galvanic co
uple consists of the three metals,navel brass was cathode in the system and was
protected by carbon steel.
|
|
Received: 26 January 2006
|
|
|
[1]Peng Q,Yin Z A,Pan L.Study of galvanic corrosion of titanium/carbon steel and cathodic protection[J].Corros.Prot.Chem.Ind.,1994,22(3):7-9(彭乔,殷正安,攀雷.钛/碳钢电偶腐蚀和阴极保护研究[J].化工腐蚀与防护,1994,22(3):7-9)
[2]El-Dahshan M E,Shams A A,El-Din,et al.Galvanic corrosionin the systems titanium/316L stainless steel/Al brass in ArabianGulf water[J].Desalination,2002,142(2):161-169
[3]Kolman D G,Scully J R.An assessment of the crack tip potential ofβ-titanium alloys during hydrogen environmentally assisted crackpropagation based on crack tip and passive surface electrochemicalmeasurements[J].Corros.Sci.,2000,42(11):1863-1879
[4]Blackwood D J,Chooi S K M.Stability of protective oxide filmsformed on a porous titanium[J].Corros.Sci.,2002,44(3):395-405
[5]Chiu S Y,Wang Y L,Liu C P,et al.The application of electro-chemical metrologies for investigating chemical mechanical polishingof Al with a Ti barrier layer[J].Mater.Chem.Phys.,2003,82(2):444-451
[6]Cramer S D,Covino B S Jr,Bullard S J,et al.Corrosion preventionand remediation strategies for reinforced concrete coastal bridges[J].Cement&Concrete Composites,2002,24(1):101-117
[7]Batis G,Routoulas A,Rakanta E.Effects of migrating inhibitors oncorrosion of reinforcing steel covered with repair mortar[J].Ce-ment&Concrete Composites,2003,25(1):109-115
[8]Liu J H,Wu H,Li S M,et al.Galvanic corrosion behavior betweentitanium alloy and high-strength alloys[J].Journal of Beijing Uni-versity of Aeronautics and Astronautics,2003,29(2):124-127(刘建华,吴昊,李松梅等.高强合金与钛合金的电偶腐蚀行为[J].北京航空航天大学学报,2003,29(2):124-127)
[9]Yang S W,Xi H Z,Xie F Z,et al.Study of naval vessel galvanic cor-rosion[J].Journal of Harbin Engineering University,2000,21(6):34-38(杨世伟,席慧智,谢辅洲等.舰船材料的电偶腐蚀研究[J].哈尔滨工程大学学报,2000,21(6):34-38)
[10]Li S Y,Chen W.Galvanic coupling behavior on carbon steel/redcopper in NaCl media[J].Corros.Sci.Prot.Technol.,2000,12(5):300-302(李淑英,陈玮.碳钢/紫铜在NaCl介质中的电偶腐蚀行为[J].腐蚀科学与防护技术,2003,12(5):300-302)
[11]Zhan G S,Yao C L.Galvanic corrosion behavior of the alloys usedfor sacrificial anode in seawater[J].Mater.Prot.,1999,32(2):31-33(战广深,姚春玲.牺牲阳极合金在海水中的接触腐蚀行为[J].材料保护,1999,32(2):31-33)
[12]Song G L,Birgir J,Sarath H,et al.Galvanic corrosion of magnesiumalloy AZ91D in contact with an aluminium alloy,steel and zinc[J].Corros.Sci.,2004,46(4):955-977
[13]Huang G Q,Yu C J,Li L S.Study on galvanic corrosion of steelcouples in seawater[J].J.Chin.Soc.Corros.Prot.,2001,21(1):46-53(黄桂桥,郁春娟,李兰生.海水中碳钢的电偶腐蚀研究[J].中国腐蚀与防护学报,2001,21(1):46-53)
[14]Deng S Z,Gu G S,Zhou L Q,et al.Electrochemical corrosion be-havior of Ti plate in different media[J].Journal of Naval Academyof Engineering,1999,87(2):57-60(邓淑珍,顾桂松,周立清等.钛在各种介质中的电化学行为的研究[J].海军工程学院学报,1999,87(2):57-60) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|