J Chin Soc Corr Pro  1996, Vol. 16 Issue (4): 281-286    DOI:
Current Issue | Archive | Adv Search |
XPS AND AES STRUDIES OF ANTITARNISHING FILM FORMED BY LAURYLAMINE ON TINPLATE
HAN Keping;FANG Jingli (Department of Chemistry; Applied Chemistry Institure; Nanjing University)
Download:  PDF(443KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  By comparison of the antitarnishing effects of various agents, the laurylamine was found to be an excellent antitaranishing agent for tinplate. The optimum conditions of treatment were laurylamine 2.5g/L; pH=8.70℃; 10min. The results of XPS and AES analyses showed that on tinplate surface an anticorrosive coordination compound film of laurylamine was formed, and N atoms in laurylamine molecule were coordinated with Sn (II). The relative atomic percent contents (A.C.%) of the film calculated at the constat elemental composition section of the AES profile curves were O 39.0%; Sn 48.7%; N 7.9%; C 4.4%.
Key words:  Antitarnish film      Tinplate      Laurylarmine      XPS      AES     
Received:  25 August 1996     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

HAN Keping;FANG Jingli (Department of Chemistry; Applied Chemistry Institure; Nanjing University). XPS AND AES STRUDIES OF ANTITARNISHING FILM FORMED BY LAURYLAMINE ON TINPLATE. J Chin Soc Corr Pro, 1996, 16(4): 281-286.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1996/V16/I4/281

1BrittonSC;BrightK.Metallrugia,1957,56:1632BijimiD,GabeDR.Br.Corros.J,,1983,18:933WilcoxGD,GabeDR.Br.Corros.J,1984,19:1964JPPat,62-057718(1988)5方景礼,李莹,王占文,王济奎,刘琴.中国腐蚀与防护学报,1993,13:2456InternationalTinResearchInstitute,“GuidetoTinplate”,London:ITRIPublicationNo.6227方景礼,刘琴,韩克平,陈耀辉.应用化学,1995;12:18WagnerCD;RiggsWM,DavisLE,MoulderJF,MuilenbergGE.HandbookofX-rayPhotoelectronSpectroscopytPerkin-ElmerCorp,EdenPrairie,MN:1978
[1] ZHANG Chen, LU Yuan, ZHAO Jingmao. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Cationic Surfactants in H2S/CO2 Brine Solution[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[2] WANG Le,YI Danqing,LIU Huiqun,JIANG Long,FENG Chun. Effect of Ru on Corrosion Behavior of Ti-6Al-4V Alloy and Its Mechanism[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[3] Zhaodeng LI,Zhendong CUI,Xiangyu HOU,Lili GAO,Weizhen WANG,Jianhua YIN. Corrosion Property of Nuclear Grade 316LN Stainless Steel Weld Joint in High Temperature and High Pressure Water[J]. 中国腐蚀与防护学报, 2019, 39(2): 106-113.
[4] Dong LIU,Hongliang XIANG,Chunyu LIU. XPS Analysis of Corrosion Product Scale on Surface of Silver-bearing Antibacterial Duplex Stainless Steel[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[5] Ming LIU,Xuequn CHENG,Xiaogang LI,Tianjian LU. Corrosion Resistance Mechanisms of Passive Films Formed on Low Alloy Rebar Steels in Liquor of Cement Extract[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[6] Yanliang WANG,Xu CHEN,Jidong WANG,Bo SONG,Dongsheng FAN,Chuan HE. Electrochemical Behavior of 316L Stainless Steel in Borate Buffer Solution with Different pH[J]. 中国腐蚀与防护学报, 2017, 37(2): 162-167.
[7] Yongsheng HAO,Abdullahi SANI Luqman,Lixin SONG,Guobao XU,Tiejun GE,Qinghong FANG. Corrosion Inhibition Effect of Phytic Acid Conversion Coating Formed on Q235 Carbon Steel in Acidic and Neutral Solutions[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.
[8] Shenggang WANG, Miao SUN, Kang LONG. Progress in Characterization of Metallic Materials Corrosion by Ultraviolet Photoelectron Spectroscopy and X-ray Photoelectron Spectroscopy[J]. 中国腐蚀与防护学报, 2016, 36(4): 287-294.
[9] Wenjing LV,Yingjun ZHANG,Chao SHI,Yawei SHAO,Yanqiu WANG,Guozhe MENG. Synthesis and Corrosion Inhibition Performance of Polyatyrolsulfon-acid Doped Polyaniline[J]. 中国腐蚀与防护学报, 2015, 35(6): 519-524.
[10] LIU Xiaolan, XU Yaxin, ZHANG Tao, SHAO Yawei, MENG Guozhe, WANG Fuhui. EFFECT OF ALTERNATING VOLTAGE (AV)MODULATED PASSIVATION ON CORROSION RESISTANCE OF AZ91D MAGNESIUM ALLOY
Ⅱ-Effect of Alternating Voltage (AV) Modulated Passivation on Surface Properties of AZ91D Magnesium Alloy
[J]. 中国腐蚀与防护学报, 2010, 30(3): 187-191.
[11] . Effect of Sb and Mn alloying additions on the Corrosion Behaviour of Zn[J]. 中国腐蚀与防护学报, 2008, 28(5): 257-264 .
[12] Dangguo Li; Genshu Zhou; Guanfa Lin; Maosheng Zheng. Properties of Anodic Scale of New Pb-Ca Grid Alloy[J]. 中国腐蚀与防护学报, 2005, 25(6): 340-343 .
[13] ;. Research on the Inhibitor of the Silver Strip Corrosion in Jet Fuel[J]. 中国腐蚀与防护学报, 2004, 24(6): 376-378 .
[14] Chunbo Huang; Zhanpeng Lv; Wu Yang. AES ANALYSIS OF THE SURFACE FILMS FORMED ON ALLOY800M IN HOT CONCENTRATED CAUSTIC SOLUTION[J]. 中国腐蚀与防护学报, 2003, 23(5): 266-270 .
[15] . CORROSION COMPOSITIONS OF CARBON STEELUNDER ION-SELECTIVE COATINGS BY XPS[J]. 中国腐蚀与防护学报, 2001, 21(5): 273-279 .
No Suggested Reading articles found!