CORROSION POTENTIAL IMAGING AT INTERFACE OF POLYMERIC COATING/METAL BY ARRAY ELECTRODETECHNIQUE
LIN Changjing ZHUO Xiangdong CHEN Jidong WANG Hui(Stote Key Laboratory of Physical Chemistry for the Solid Surface; Department of Chemistry; XiamenUniversity; China)
Download:  PDF(393KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  An array electrode composed of 64 steel wires and a potential imaging system were developed as a new electrochemical technique for probing the corrosion potential distribution at interface of polymeric coating/metal. The measuring technique was described, and the availability of the technique was examined. The novel data related to the corrosion behavior at the interface were obtained and the effects of defects in the coating on its degradation were discussed. The potential imaging demonstrated the existence of inhomogeneities in the coatings, including intrinsic defects or damage in service (artificial defects). Corrosion preferentially initiated at the defect sites. The anodic sites surrounding cathodic area and the development process of corrosion reaction were in situ imaged for the first time for organically coated steel system. The relevant and direct information provided by this unique technique would be very helpful for further understanding some important physicochemical processes associated with degradation of coated metals.
Key words:  Corrosion potential imaging      Polymer/metal interface      Array electrode technique      Corrosion mechanism     
Received:  25 February 1997     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

LIN Changjing ZHUO Xiangdong CHEN Jidong WANG Hui(Stote Key Laboratory of Physical Chemistry for the Solid Surface; Department of Chemistry; XiamenUniversity; China). CORROSION POTENTIAL IMAGING AT INTERFACE OF POLYMERIC COATING/METAL BY ARRAY ELECTRODETECHNIQUE. J Chin Soc Corr Pro, 1997, 17(1): 7-11.

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y1997/V17/I1/7

1 Leidheiser H Jr. Journal of Coatings Technology, 1991, 63:21
2 Lin C J(林昌健), Nguyen T. NIST Technical Note, 1988, 1253
3 Walter G W. Corrosion Science, 1986, 26:39
4 Standish J V, Leidheiser H Jr. Corrosion, 1980, 36:390
5 Jun T Y, Progress in Organic Coatings, 1991, 19:95
6 Nguyen T, Lin C J.(林昌健) J. Adhesion Science and Technology, 1991, 5:679
7 Stratmann M, Wolper M, Streckel H, Feser R. Bunsenger. Phys. Chem., 1991, 95:1365
8 Stratmann M, Feser R, Leng A. Electrochimica Acta, 1994, 39:1207
9 Lin C J(林昌健), Nguyen T, McKnight M E. Progress in Organic Coatings, 1992, 20:169
[1] DONG Xucheng, GUAN Fang, XU Liting, DUAN Jizhou, HOU Baorong. Progress on the Corrosion Mechanism of Sulfate-reducing Bacteria in Marine Environment on Metal Materials[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2] YUE Liangliang, MA Baoji. Effect of Ultrasonic Surface Rolling Process on Corrosion Behavior of AZ31B Mg-alloy[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[3] ZHU Lixia, JIA Haidong, LUO Jinheng, LI Lifeng, JIN Jian, WU Gang, XU Congmin. Effect of Applied Potential on Stress Corrosion Behavior of X80 Pipeline Steel and Its Weld Joint in a Simulated Liquor of Soil at Lunnan Area of Xinjiang[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[4] LIANG Yi, DU Yanxia. Research Progress on Evaluation Criteria and Mechanism of Corrosion Under Cathodic Protection and AC Interference[J]. 中国腐蚀与防护学报, 2020, 40(3): 215-222.
[5] ZHANG Zhen, WU Xinqiang, TAN Jibo. Review of Electrochemical Noise Technique for in situ Monitoring of Stress Corrosion Cracking[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[6] Baojie WANG,Jiyu LUAN,Shidong WANG,Daokui XU. Research Progress on Stress Corrosion Cracking Behavior of Magnesium Alloys[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[7] Xijing WANG, Boshi WANG, Chao YANG, Yan YANG, Bin SHEN. Hot Corrosion of Pure Nickel and Its Weld Joints in Molten Na2SO4-K2SO4 Salts[J]. 中国腐蚀与防护学报, 2018, 38(5): 495-501.
[8] Dahai XIA, Shizhe SONG, Jihui WANG, Zhimng GAO, Wenbin HU. Research Progress on Corrosion Mechanism of Tinned Steel Sheet Used for Food Parkaging[J]. 中国腐蚀与防护学报, 2017, 37(6): 513-518.
[9] Zhenning CHEN,Rihui CHEN,Jinjie PAN,Yanna TENG,Xingyue YONG. Organic/inorganic Compound Corrosion Inhibitor of L921A Steel in NaCl Solution[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.
[10] Yan LI,Jintao LU,Zhen YANG,Ming ZHU,Yuefeng GU. Effect of Sulfur Content on Corrosion Behavior of Candidate Alloys Used for 700 ℃ Level A-USC Boiler in Simulated Coal Ash and Flue Gas Environments[J]. 中国腐蚀与防护学报, 2016, 36(5): 505-512.
[11] Chong SUN, Yong WANG, Jianbo SUN, Tao JIANG, Weimin ZHAO, Yanchun ZHANG. Investigation Progress on Corrosion Behavior of Supercr-itical CO2 Transmission Pipelines Containing Impurities in CCS[J]. 中国腐蚀与防护学报, 2015, 35(5): 379-385.
[12] ZHAO Guoqiang, WEI Yinghua, LI Jing. Current Efficiency and Corrosion Mechanism of Al-Zn-In Sacrificial Anode at Different Current Densities[J]. 中国腐蚀与防护学报, 2015, 35(1): 69-74.
[13] ZHOU Jing, FENG Zhiyong, ZHANG Jinling, WANG Shebin. Effect of Nd Addition on Corrosion Resistance of AM60 Magnesium Alloy[J]. 中国腐蚀与防护学报, 2014, 34(2): 185-191.
[14] CHANG Xinlong,LIU Wanlei,LAI Jianwei,ZHANG Xiaojun. Stress Corrosion Cracking Susceptibility of LD10 Aluminum Alloy[J]. 中国腐蚀与防护学报, 2013, 33(4): 347-350.
[15] YANG Chao,,ZHANG Huixia,GUO Weimin,FU Yubin. Effects of H2O2 Addition on Corrosion Behavior of High-strength Low-alloy Steel in Seawater[J]. 中国腐蚀与防护学报, 2013, 33(3): 205-210.
No Suggested Reading articles found!