EVALUATION OF DETERMINATION METHODS OF CRACK PROPAGATION RATE IN ENVIRONMENTALLY ASSISTED CRACKING

Download:

PDF(614KB)
Export: BibTeX | EndNote (RIS)

Abstract The determination methods and relevant models of crack propagation rate in environmentally assisted cracking were summed up and reviewed. The advantages and shortcomings as well as application range of these methods and models were analyzed and evaluated. The main purpose of the review was to provide convincing basis not only for the most suitable determination of crack propagation rate in various complex material/environment combinations but also for the life-prediction of components in practical service.

Key words: Crack propagation rate Environmentally assisted cracking Method

Received: 25 June 1998

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

NIU Lin LIN Hai-chao CAO Chu-nan SONG Guang-ling SHI Zhi-ming(The Institute of Corrosion and Protection of Metals; Chinese Academy of Sciences; State Key Laboratory of Corrosion and Protection; Shenyang 110015). EVALUATION OF DETERMINATION METHODS OF CRACK PROPAGATION RATE IN ENVIRONMENTALLY ASSISTED CRACKING. J Chin Soc Corr Pro, 1998, 18(3): 214-220.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1998/V18/I3/214

1 Brown B F. Stress Corrosion Cracking in High Strength Steels, and in Titanium and Aluminum Alloys, NRL, Washington D C. 1972
2 Chu W, Hsiao C, Tu S, et al. Corrosion, 1982, 38:446
3 Wendier-Kalsch E. Werkstoffe and Corrosion, 1978, 29:703
4 Speidel M O. Corrosion, 1977, 33:199
5 Haruna T, Shibata T. Corrosion, 1994, 50:785
6 Speidel M O. Metall. Trans. A, 1981, 12A: 779
7 Speidel M O. The Theory of Stress Corrosion Cracking in Alloys, eds. Scully J C, NATO, Scientific Affairs Division, Brussels, 1971. p289
8 Parking R N. Brit. Corros. J., 1979, 14:5
9 Ford F P. Corrosion Processes, eds. Parkins R N, Applied Science, New York, NY, 1982. p271
10 Ford F P. EPRI Report NP2589, Palo Alto, CA: EPRI, 1982
11 Ford F P, et al. Corrosion/85, Paper no. 352, Boston, 1985
12 Ford F P. Corrosion/86, Paper no. 327, Houston, 1986
13 Parkins R N. Proc. 3rd Int. Conf. Mechanical Behavior of Materials, Cambridge, U. K, August 1979, eds. K. J. Miller et al., Pergamon Press, 1980. p139
14 Ford F P. Corrosion, 1996, 52:375
15 Congleton J, et al. Corros. Sci., 1985, 25:633
16 Parkins R N, et al. Metal Sci., 1977, 11:405
17 Parkins R N. Corrosion, 1990, 46:178
18 Turnbull A. Corros. Sci., 1993, 34:921
19 Parkins R N. Environment-induced Cracking of Metals, eds. Gangloff R Petal., NACE, Houston,1990, pl
20 Scully J C. Corros. Sci., 1968, 8:513
21 Parkins R N. Corros. Sci., 1980, 20:147
22 Jones D A. Metall. Trans. A, 1985, 16A: 1133
23 Ford F P, Burstein G T, Hoar T P. J.Electrochem. Soc., 1980, 127:6
24 Hagyard T, Earl W B. J. Electrochem. Soc., 1968, 115:623
25 Less D J, Hoar T P. Corrs. Sci., 1980, 20:723
26 Newman R C, Burstein G T. Corros. Sci., 1981, 21:119
27 Diegle R B, Lineman D M. J. Electrochem. Soc., 1984, 131:106
28 Diegle R B, Vermilyea D A. J. Electrochem. Soc., 1975, 122:180
29 Ford F P, Silverman M. Corrosion, 1980, 36:558
30 Carranza R M, Galvele J R. Corros. Sci., 1988, 28:233
31 Carranza R M, Galvele J R. Corros. Sci., 1988, 28:851
32 Galvele J R, Torresi R M, Caxrauza R M. Corros. Sci.,1990, 31:536
33 Beck T R. J. Electrochem. Soc., 1982, 129:2500
34 Beck T R. Corrosion, 1974, 30:408
35 Wei R P, Alavi A. Scrip. Metall. 1988, 22:969

[1]	DENG Peichang, ZHONG Jie, WANG Kun, HU Jiezhen, LI Ziyun, CHEN Chuxin, SHEN Xiaohan. Important Influential Factor for Corrosion of High-altitude Marine Engineering Equipment in Atmosphere-chloride Ion Deposition Rate[J]. 中国腐蚀与防护学报, 2020, 40(5): 474-478.
[2]	JIA Qiaoyan, WANG Bei, WANG Yun, ZHANG Lei, WANG Qing, YAO Haiyuan, LI Qingping, LU Minxu. Corrosion Behavior of X65 Pipeline Steel at Oil-Water Interface Region in Hyperbaric CO₂ Environment[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[3]	Zhifeng LIU,Zhiping ZHU,Chun SHI,Zhaoxin HUANG. Preparation of Sulfuric Acid Vapor for Simulation of Sulfuric Acid Dew Point Corrosion by Inert Gas Carrying Method[J]. 中国腐蚀与防护学报, 2020, 40(1): 1-9.
[4]	SHI Kunyu,ZHANG Jinzhong,ZHANG Yi,WAN Yi. Preparation and Corrosion Resistance of Nb₂N Coating on TC4 Ti-alloy[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[5]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Equivalent Electrical Circuits Fitting of Electrochemical Impedance Spectroscopy for Rebar Steel Corrosion of Coral Aggregate Concrete[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[6]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Influence of Inhibitors on Reinforced Bar Corrosion of Coral Aggregate Seawater Concrete[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[7]	Jianguo LIU,Ge GAO,Yazhou XU,Zili LI,Wanran JI. Corrosion Inhibition Performance of Imidazoline Derivatives[J]. 中国腐蚀与防护学报, 2018, 38(6): 523-532.
[8]	Xiangfeng KONG, Jing ZHANG, Yuanqing JIANG, Dongzhi CHU, Chunhu LI, Nan GAO, Jing LV, Yan ZOU. Corrosion Performance of Underwater Welded Joints of E40 Steel in Coastal Water of Qingdao via Mass-loss Method[J]. 中国腐蚀与防护学报, 2018, 38(3): 226-232.
[9]	Shuangchen MA, Kunling JIAO, Linan ZHANG, Yao SUN, Wenlong WU, Xiaoni ZHANG. Corrosion Characteristics of Carbon Steel in High Temperature Gas Containing Ammonium Bisulfate and Ammonium Sulfate[J]. 中国腐蚀与防护学报, 2017, 37(6): 605-612.
[10]	Jie KOU, Xince ZHANG, Gan CUI, Baoan YANG. Research Progress on Cathodic Protection Potential Distribution of Tank Bottom Plate[J]. 中国腐蚀与防护学报, 2017, 37(4): 305-314.
[11]	Xinhui LI,Wen MA,Yichuan YIN,Bole MA,Yu BAI,Ruiling JIA,Hongying DONG. Optimization of Preparation Process of Solution Precursor Plasma Spraying for SrZrO₃ Thermal Barrier Coating[J]. 中国腐蚀与防护学报, 2017, 37(1): 41-46.
[12]	Shuangchen MA,Yue DENG,Wenlong WU,Yu TAN,Linan ZHANG,Feng CHAI,Panpan SUN,Xiaoni ZHANG. Corrosion Characteristics of Downstream Metal Material of Boiler System in Solution of By-product Ammonium Bisulfate from SCR Denitrification[J]. 中国腐蚀与防护学报, 2016, 36(4): 335-342.
[13]	Cui LIN,Xiaobin ZHAO,Yifei ZHANG. Research Progress on Cavitation-corrosion ofMetallic Materials[J]. 中国腐蚀与防护学报, 2016, 36(1): 11-19.
[14]	Fengping WANG,Lan LIU,Yanwei DING,Suijun HU,Zhaobin LIU,Dan LIU,Li ZHANG. Simulation of Carbon Steel Corrosion in Oil-gas Field Produced Waters Containing Hydrogen Sulfide[J]. 中国腐蚀与防护学报, 2015, 35(3): 251-256.
[15]	LI Qiang, TANG Xiao, LI Yan. Progress in Research Methods for Erosion-corrosion[J]. 中国腐蚀与防护学报, 2014, 34(5): 399-409.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed