INHIBITIVE EFFECT OF TG500 IN THE SOLUTIONWITH HIGH CONTENT CO2 AND Cl-

;;;;

中国石油天然气集团公司石油管力学与环境行为重点实验室

Download:

PDF(1716KB)
Export: BibTeX | EndNote (RIS)

Abstract As a new quaternary ammonium of double-alkyl and double-annular imidazoline ,TG500 was designed for the oilfield with high content CO2 and Cl-.Weight losses of the steel N80 in static condition with high temperature high pressure and high CO2 and Cl- are tests for evaluating inhibition efficiency of TG500.The results show that the inhibition efficiency is increasing with the content of TG500 at first,and then does not increase any more,when the content is up to 0.3 g/L.The corrosion morphology on N80 steel surface is uniform corrosion in low concentration; when the content up to 0.3 g/L,then there is only invisible sign of corrosion unless a few pitting corrosion.

Key words: inhibitor Imidazoline Inhibitation efficiency CO2 Cl-

Received: 09 October 2005

ZTFLH:

TG174

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

. INHIBITIVE EFFECT OF TG500 IN THE SOLUTIONWITH HIGH CONTENT CO2 AND Cl-. J Chin Soc Corr Pro, 2007, 27(1): 23-26 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2007/V27/I1/23

[1]Li J P,Zhao G X,Hao S M.Dynamic corrosion behaviors of N80,P105 and SM110 steel[J].J.Chin.Soc.Corros.Prot.,2005,25(4):241-244(李建平,赵国仙,郝士明.几种因素对油套管钢CO2腐蚀行为的影响[J].中国腐蚀与防护学报,2005,25(4):241-244)
[2]Li J P,Zhao G X,Hao S M.The study on static corrosion of oil thim-ble used in Tarim oil field[J].J.Chin.Soc.Corros.Prot.,2004,24(4):230-233(李建平,赵国仙,郝士明.塔里木油田用油套管钢的静态腐蚀[J].中国腐蚀与防护学报,2004,24(4):230-233)
[3]Zhang X Y,Di C,Lei L C.Corrosion and Control for Dioxide[M].Beijing:Chemical Industry Press,2000,58(张学元,邸超,雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000,58)
[4]Nesi S,John P.Mechanism of carbon steel-form mechanism to em-pirical modeling[J].Corros.Rev.,1997,15:112-126
[5]Lin G F,Bai Z Q,Zhao G X.Effect of CO2partial pressure on themorphology of corrosion metallic product scales[J].J.Chin.Soc.Corros.Prot.,2004,24(5):284-288(林冠发,白真权,赵国仙.CO2压力对金属腐蚀产物膜形貌结构的影响[J].中国腐蚀与防护学报,2004,24(5):284-288)

[1]	BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[2]	WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[3]	SHAO Minglu, LIU Dexin, ZHU Tongyu, LIAO Bichao. Preparation of Urotropine Quaternary Ammonium Salt and Its Complex as Corrosion Inhibitor[J]. 中国腐蚀与防护学报, 2020, 40(3): 244-250.
[4]	JIA Qiaoyan, WANG Bei, WANG Yun, ZHANG Lei, WANG Qing, YAO Haiyuan, LI Qingping, LU Minxu. Corrosion Behavior of X65 Pipeline Steel at Oil-Water Interface Region in Hyperbaric CO₂ Environment[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[5]	ZHANG Chen, LU Yuan, ZHAO Jingmao. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Cationic Surfactants in H₂S/CO₂ Brine Solution[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[6]	YI Hongwei, HU Huihui, CHEN Changfeng, JIA Xiaolan, HU Lihua. Corrosion Behavior and Corrosion Inhibition of Dissimilar Metal Welds for X65 Steel in CO₂-containing Environment[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[7]	LV Xianghong,ZHANG Ye,YAN Yali,HOU Juan,LI Jian,WANG Chen. Performance Evaluation and Adsorption Behavior of Two New Mannich Base Corrosion Inhibitors[J]. 中国腐蚀与防护学报, 2020, 40(1): 31-37.
[8]	Xia WANG,Shuaifei REN,Daixiong ZHANG,Huan JIANG,Yue GU. Inhibition Effect of Soybean Meal Extract on Corrosion of Q235 Steel in Hydrochloric Acid Medium[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[9]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Influence of Inhibitors on Reinforced Bar Corrosion of Coral Aggregate Seawater Concrete[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[10]	Jianguo LIU,Ge GAO,Yazhou XU,Zili LI,Wanran JI. Corrosion Inhibition Performance of Imidazoline Derivatives[J]. 中国腐蚀与防护学报, 2018, 38(6): 523-532.
[11]	Yaqiong LI,Jingling MA,Guangxin WANG,Yujie ZHU,Yongfa SONG,Jingli ZHANG. Effect of Sodium Phosphate and Sodium Dodecylbenzene-sulfonate on Discharge Performance of AZ31 Magnesium Air Battery[J]. 中国腐蚀与防护学报, 2018, 38(6): 587-593.
[12]	Yunxiang CHEN, Lijuan FENG, Jianbin CAI, Xuan WANG, Yicheng HONG, Deyuan LIN, Jianhuang ZHUANG, Huaiyu YANG. Inhibition Effect of a New Composite Organic Inhibitor on Corrosion of Steel Rebar in Simulated Concrete Solution or Inside Mortar Specimen[J]. 中国腐蚀与防护学报, 2018, 38(4): 343-350.
[13]	Jingling MA, Shuai TONG, Fengzhang REN, Guangxin WANG, Yaqiong LI, Jiuba WEN. Influences of Inhibitor L-Cysteine/zinc Oxide on Electrochemical Performance of 3102 Al-alloy in Alkaline Solution[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[14]	Wanjun PENG, Jiheng DING, Hao CHEN, Haibin YU. Corrosion Inhibition of Bio-based Inhibitor Furfuryl Glycidyl Ether[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[15]	Bei QIAN, Chengbao LIU, Zuwei SONG, Junfeng REN. Anticorrosion Performance of Epoxy Coating Modified with Nanocontainers[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed