FAILURE MECHANISM OF ONE SIDE COATED THERMAL BARRIER COATING

J Chin Soc Corr Pro

2006, Vol. 26

Issue (3): 146-151 DOI:

Research Report

Current Issue | Archive | Adv Search

FAILURE MECHANISM OF ONE SIDE COATED THERMAL BARRIER COATING

LI yunduan;;Shengkai Gong;Huibing Xv

北京航空航天大学

Download:

PDF(431KB)
Export: BibTeX | EndNote (RIS)

Abstract Two layered structure thermal barrier coatings were prepared by electron beam physical vapor deposition.The changes on microstructure and the failure mode of the specimen during thermal cyclic oxidation were analyzed by scanning electron microscopy (SEM) and impedance spectroscopy (IS).It is shown that the spallation of one side coated TBCs occurred mainly in YSZ top coat,instead of in thermally grown oxide (TGO) layer as often observed in double sides coated TBCs.Stress analysis indicates that during thermal cycling,double sides coated TBCs are mainly subjected to the thermal mismatched shear stress parallel to the sample surface,but one side coated TBCs are subjected not only to the shear stress,but also to the stress along the normal direction,and finally crack inside the YSZ.IS method can characterize the initiation and expansion of the transversal crack in the TBCs.

Key words: thermal barrier coatings failure mechanism impedance spectroscopy thermal cycling

Received: 03 February 2005

ZTFLH:

TG174.444

Corresponding Authors: LI yunduan E-mail: liyunduan@mse.buaa.edu.cn

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	LI yunduan
	Shengkai Gong
	Huibing Xv

Cite this article:

LI yunduan; Shengkai Gong; Huibing Xv. FAILURE MECHANISM OF ONE SIDE COATED THERMAL BARRIER COATING. J Chin Soc Corr Pro, 2006, 26(3): 146-151 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2006/V26/I3/146

[1]	CAO Jingyi, WANG Zhiqiao, LI Liang, MENG Fandi, LIU Li, WANG Fuhui. Failure Mechanism of Organic Coating with Modified Graphene Under Simulated Deep-sea Alternating Hydrostatic Pressure[J]. 中国腐蚀与防护学报, 2020, 40(2): 139-145.
[2]	Xia WANG,Shuaifei REN,Daixiong ZHANG,Huan JIANG,Yue GU. Inhibition Effect of Soybean Meal Extract on Corrosion of Q235 Steel in Hydrochloric Acid Medium[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[3]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Equivalent Electrical Circuits Fitting of Electrochemical Impedance Spectroscopy for Rebar Steel Corrosion of Coral Aggregate Concrete[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[4]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Influence of Inhibitors on Reinforced Bar Corrosion of Coral Aggregate Seawater Concrete[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[5]	Xiuling LAN,Guangming LIU,Jiesheng ZHOU,Zhilei LIU,Shusen PENG,Maodong LI. Preparation and Properties of Organosilicone/SiO₂Hybrid Sol Modified Acrylic Resin[J]. 中国腐蚀与防护学报, 2018, 38(6): 601-606.
[6]	Peichang DENG, Quanbing LIU, Ziyun LI, Gui WANG, Jiezhen HU, Xie WANG. Corrosion Behavior of X70 Pipeline Steel in the Tropical Juncture Area of Seawater-Sea Mud[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[7]	Sanxi DENG, Xiaoyu YAN, Ke CHAI, Jinyi WU, Hongwei SHI. *Effect of Pseudomonas* sp. on Decomposition and Anticorrosion Behavior of Polysiloxane Varnish Coating**[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[8]	Haijiao CAO, Yinghua WEI, Hongtao ZHAO, Chenxi LV, Yaozong MAO, Jing LI. Effect of Preheating Time on Protective Performance of Fusion Bonded Epoxy Powder Coating on Q345 Steel II: Failure Behavior Analysis of Coating[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[9]	Qi GUI, Dajiang ZHENG, Guangling SONG. Electrochemically Accelerated Evaluation of Protectiveness for an Alkyd Varnish Coating[J]. 中国腐蚀与防护学报, 2018, 38(3): 274-282.
[10]	Meng MEI, Hongai ZHENG, Huida CHEN, Ming ZHANG, Daquan ZHANG. Effect of Sulfate Reducing Bacteria on Corrosion Behavior of Cu in Circulation Cooling Water System[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[11]	Fandi MENG, Li LIU, Ying LI, Fuhui WANG. *Embedded Microelectrode for In situ* Electrochemical Impedance Spectroscopy Measurement of Organic Coating Under Marine Alternating Hydrostatic Pressure**[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.
[12]	Jun WANG, Chao FENG, Bicao PENG, Yi XIE, Minghua ZHANG, Tangqing WU. Corrosion Behavior of Weld Joint of S450EW Steel in NaHSO₃ Solution[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[13]	Jia WANG, Mengyang JIA, Zhaohui YANG, Bing HAN. On Completeness of EIS Equivalent Circuit Analysis for Electrochemical Corrosion Process[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.
[14]	Zhenning CHEN,Rihui CHEN,Jinjie PAN,Yanna TENG,Xingyue YONG. Organic/inorganic Compound Corrosion Inhibitor of L921A Steel in NaCl Solution[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.
[15]	Yalin CHEN, Wei ZHANG, Qi WANG, Jia WANG. Debonding Mechanism of Organic Coating with Artificial Defect in Areas Nearby Water-line in 3.5%NaCl Solution by WBE Technique-II[J]. 中国腐蚀与防护学报, 2017, 37(4): 322-328.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed