EFFECT OF TEMPERATURE ON CO2 CORROSION BEHAVIOUR OF P110 STEEL

J Chin Soc Corr Pro

2005, Vol. 25

Issue (2): 93-96 DOI:

Research Report

Current Issue | Archive | Adv Search

EFFECT OF TEMPERATURE ON CO2 CORROSION BEHAVIOUR OF P110 STEEL

Guoxian Zhao;Xianghong Lv;Helin Li;Minxv Lu

西安交通大学材料科学与工程系

Download:

PDF(166KB)
Export: BibTeX | EndNote (RIS)

Abstract Influences of temperature on CO2 corrosion behaviors of P110 steel were studied in stimulated oilfield environments. Morphologies of scales and their effects on corrosion rate and corrosion shape were analyzed by SEM and XRD. The results showed, at 40℃, corrosion products were similar to loosen soil, few and hanging on the surface of the material composed by deposited KCl. In 90℃, corrosion products were grains, compact and much holes in it, constituted by calcium/magnesium/iron carbonate and few KCl and Fe2O3. In 140℃, corrosion products were in the similar morphology as compact clay in the outer layer and grains in the inner layer, made up of FeCO3 and KCl. The phenomena of different morphology in different temperature resulted in that the maximal corrosion rate presented in 90℃.

Key words: CO2 corrosion P110 steel corrosion scale corrosion rate temperature

Received: 15 October 2003

ZTFLH:

TG172

Corresponding Authors: Guoxian Zhao E-mail: zhaoguoxianxian@sohu.com

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Guoxian Zhao
	Xianghong Lv
	Helin Li
	Minxv Lu

Cite this article:

Guoxian Zhao; Xianghong Lv; Helin Li; Minxv Lu. EFFECT OF TEMPERATURE ON CO2 CORROSION BEHAVIOUR OF P110 STEEL. J Chin Soc Corr Pro, 2005, 25(2): 93-96 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2005/V25/I2/93

[1]De,WaardC ,LotzU ,MilliamsDE .PredictionmodelforCO2 cor rosionengineeringinwetnaturalgaspipeline[A ].Corrosion/91,Corrosion,1991,47(12):976
[2]DugstadA ,LundeL ,VidemK .ParametricstudyofCO2 corrosionofcarbonsteel[A].Corrosion/94[C].NACE ,1994,14
[3]McMahonAJ ,PaisleyDME .Corrosionpredictionmodeling-aguidetotheuseofcorrosionpredictionmodelsforriskassessmentinoilandgasproductionandtransportationfacilities[A].ReportNo.ESR96.ER .066[C].BPInternational,Sunbury,1997
[4]HalvorsenAMK ,SontvedtT .CO2 corrosionmodelforcarbonsteelincludingawallshearstressmodelformultiphaseflowandlimitsforproductionratetoavoidmesaattack[A].Corrosion/99[C].NACE ,1999,42
[5]NesicS ,PostlethwaiteJ ,NyborgR .AmechanisticmodelforCO2corrosion[A].Corrosion/2001[C].NACE ,2001,40
[6]LindaGSGray,BruceGAnderson.EffectofpHandtemperatureonthemechanismofcarbonsteelcorrosionbyaqueouscarbondiox ide[A].Corrosion/90[C].NACE ,1990,40
[7]MishraB ,etal.PredictionofmicrostructuraleffectonthecorrosionofpipelinesteelsinCO2-brinesolution[A].Corrosion/93[C].NACE ,1993,90
[8]HauslerRH ,StegmannDW .CO2 corrosionanditspreventionbychemicalinhibitioninoilandgasproduction[A].Corrosion/88[C].NACE ,1988,363
[9]IkedaA ,UedaM ,MukaiS .AdvancedinCO2 corrosion,EditedbyBurke,PAetal

[1]	REN Yan, QIAN Yuhai, ZHANG Xintao, XU Jingjun, ZUO Jun, LI Meishuan. Effect of Thermal Shock on Mechanical Properties of Siliconized Graphite with ZrB₂-SiC-La₂O₃/SiC Coating[J]. 中国腐蚀与防护学报, 2021, 41(1): 29-35.
[2]	JIA Shichao, GAO Jiaqi, GUO Hao, WANG Chao, CHEN Yangyang, LI Qi, TIAN Yimei. Influence of Water Quality on Corrosion of Cast Iron Pipe in Reclaimed Water[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[3]	WANG Lei, DONG Junhua, HAN Da, LIANG Jiankun, LI Quan, KE Wei. Phenonmenon of Cu Segregation in Cu-containing steel During Soaking at 1150 ℃[J]. 中国腐蚀与防护学报, 2020, 40(6): 545-552.
[4]	LIU Xiao, WANG Hai, ZHU Zhongliang, LI Ruitao, CHEN Zhenyu, FANG Xudong, XU Fanghong, ZHANG Naiqiang. Oxidation Characteristics of Austenitic Heat-resistant Steel HR3C and Sanicro25 in Supercritical Water for Power Station[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[5]	LI Qing, ZHANG Deping, LI Xiaorong, WANG Wei, SUN Baozhuang, AI Chi. Comparison of Stress Corrosion Behavior of TP110TS and P110 Steel in a Simulated Annular Environment of CO₂ Injection Well[J]. 中国腐蚀与防护学报, 2020, 40(4): 302-308.
[6]	XIE Dongbai, HONG Hao, WANG Wen, PENG Xiao, DUO Shuwang. Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[7]	WANG Haiwei, CHANG Sen, LUAN Xin'gang, SONG Xuemei, WANG Zhen, LI Yanzhang, CHEN Jianli, ZHANG Jirong, HAN Ming, QIU Dangui. Preparation and Properties of Ceramics Composed of Nano-Al₂O₃ and Polysiloxane-polyborosilicate-TiB₂ Modified Polysilborazane as High Temperature Adhesive for SiC Based Ceramics[J]. 中国腐蚀与防护学报, 2020, 40(4): 367-372.
[8]	ZHANG Zhen, WU Xinqiang, TAN Jibo. *Review of Electrochemical Noise Technique for in situ* Monitoring of Stress Corrosion Cracking**[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[9]	SHEN Shuyang, WANG Dongsheng, SUN Shibin, YANG Ti, ZHAO Qianjing, WANG Xin, ZHANG Yafei, CHANG Xueting. Corrosion Behavior in Artificial Seawater of Subzero Treated EH40 Marine Steel Suitable for ExtremelyCold Environments[J]. 中国腐蚀与防护学报, 2020, 40(2): 151-158.
[10]	ZHENG Yanxin, LIU Ying, SONG Qingsong, ZHENG Feng, JIA Yuchuan, HAN Peide. High-temperature Oxidation Behavior and Wear Resistance of Copper-based Composites with Reinforcers of C, ZrSiO₄ and Fe[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[11]	WU Dongcai,HAN Peide. Effects of Moderate Temperature Aging Treatment on Corrosion Resistance of SAF2304 DuplexStainless Steel[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[12]	XU Xunhu,HE Cuiqun,XIANG Junhuai,WANG Ling,ZHANG Honghua,ZHENG Xiaodong. High Temperature Oxidation Behavior of Co-20Re-25Cr-1Si Alloy in 0.1 MPa Pure Oxygen[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[13]	CHEN Xu,MA Jiong,LI Xin,WU Ming,SONG Bo. Synergistic Effect of SRB and Temperature on Stress Corrosion Cracking of X70 Steel in an ArtificialSea Mud Solution[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[14]	ZHAO Guoxian,HUANG Jing,XUE Yan. Corrosion Behavior of Materials Used for Surface Gathering and Transportation Pipeline in an Oilfield[J]. 中国腐蚀与防护学报, 2019, 39(6): 557-562.
[15]	AI Peng,LIU Lixiang,LI Xiaogang,JIANG Wentao. Influence of TiAlSiN Coatings on High Temperature Oxidation Resistance of γ-TiAl Based Alloys[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed