COKING BEHAVIORS OF THREE KINDS OF METALSAND THEIR OXIDE FILMS DURING THERMAL CRACKING REACTION OF HYDROCARBONS

Chuseng Li;Li Yu;Yuansheng Yang

中科院金属所

Download:

PDF(278KB)
Export: BibTeX | EndNote (RIS)

Abstract The present paper, for three kinds of typical metals, Ni, Cu, Cr, and their oxide films NiO, CuO, Cr2O3, firstly analyzes the coking characteris tics in thermal cracking reaction of hydrocarbons and the possibilities of reduc tion , then they were tested separately with a quick coking device at 800℃, com bing with the analysis of morphology, elemental composition and valence on the s urface by scan electron microscope (SEM), electron dispersion X-ray analysis (ED AX) and X-ray photoelectron spectroscope (XPS), it was uncovered that the three kinds of metals and their oxide films have the different coking behaviors and co king mechanisms.

Key words: coking catalysis thermal cracking reduction

Received: 06 March 2000

ZTFLH:	O621.25+4.2
	O643.38

Corresponding Authors: Chuseng Li

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Chuseng Li
	Li Yu
	Yuansheng Yang

Cite this article:

Chuseng Li; Li Yu; Yuansheng Yang. COKING BEHAVIORS OF THREE KINDS OF METALSAND THEIR OXIDE FILMS DURING THERMAL CRACKING REACTION OF HYDROCARBONS. J Chin Soc Corr Pro, 2001, 21(3): 158-166 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2001/V21/I3/158

[1]LahayeJ,BadieP ,DucretJ .Mechanismofcarbonformationduringsteamcrackingofhydrocarbon[J].Carbon,1977,15:87-93
[2]BakerRTK ,YatesDJC ,DumesicJA .Mechanismofcarbonformationduringsteamcrackingofhydrocarbon[C],the182 ndMeetingoftheAmericanChemicalSociety[A].NewYork,1981
[3]BoehmHP .Carbonfromcarbonmonoxidedisproportiononnickelandironcatalyst:Morphologicalstudiesandpossiblegrowthmechanisms[J].Carbon,1973,11:583-590
[4]JacksonPRS ,YoungDJ ,TrimmDL .Cokedepositiononandremovalfrommetalsandheat-resistantalloysundersteam-crackingconditions[J].J .Mater.Sci.,1986,21:4376-4384
[5]JacksonPRS ,TrimmDL ,YoungDJ.Thecokingkineticofheatresistantausteniticsteelsinhydrogen-propyleneatmo spheres[J].J.Mater.Sci.,1986,21:3125-3134.
[6]ChenGuanrong,ShiJun,etal.EncyclopediaofChemicalEngineering(Vol.18)[M ].Beijing:ChemicalIndustryPress,1993,856-858(陈冠荣,时钧等编.化工百科全书(18)[M ].北京:化学工业出版社,1993,856-858)
[7]LiYuin.Thetheoryofindustrialcatalysis(SecondEdition)[M ].Tianjin:TianjinUniversityPress,1996,72-78(李玉敏.工业催化原理(第二版)[M].天津:天津大学出版社,1996,72-78)
[8]JacksonPRS ,TrimmDL ,YoungDJ .Morphologicalstudiesofcokingonheat-resistantalloy[J].J .Mater.Sci.,1985,20:4035-4044
[9]清山哲郎.TranslatedbyHuangMinming,CheckedbyWangJiwu.MetallicOxideanditsCatalyticAction[M].Hefei:ChineseScienceandTechnologyUniversityPress,1991,84-93([日]清山哲郎著,黄敏明译,王基武校.金属氧化物及其催化作用[M ],合肥:中国科学技术大学出版社,1991,84-93)
[10]YinYongjia,LiDazhen,etal.PhysicalChemistry(SecondEdition)[M ].Beijing:HighEducationPress,1990,368-379(印永嘉,李大珍编.物理化学(第二版)[M ].北京:高等教育出版社,1990,368-379)
[11]YangYuansheng,WuXinqiang,etal.ChinesePatentZL 97216734.X[P].1998(杨院生,吴欣强等.中国专利97216734.X[P],1998)
[12]MitchellDRG ,YoungDJ.Akineticandmorphologicalstudyofthecokingofsomeheat-resistantsteel[J].J .Mater.Sci.,1994,29:4357-4370

[1]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[2]	WANG Yu, WU Jiajia, ZHANG Dun. Research Progress on Corrosion of Metal Materials Caused by Dissimilatory Iron-reducing Bacteria in Seawater[J]. 中国腐蚀与防护学报, 2020, 40(5): 389-397.
[3]	WANG Yi,ZHANG Dun. Research Progress of Bismuth Based Visible Light Photocatalytic Antifouling Materials[J]. 中国腐蚀与防护学报, 2019, 39(5): 375-386.
[4]	Yue QIAO, Zhiping ZHU, Lei YANG, Zhifeng LIU. Monitoring and Simulated Experiments of Oxidation-Reduction Potential of Boiler Feedwater at High Temperatures[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[5]	Qimeng CHEN,Junxi ZHANG,Xujie YUAN,Nianwei DAI. Effect of Alternating Electric Field on Diffusion Coefficient of Oxygen in Thin Electrolyte Layer[J]. 中国腐蚀与防护学报, 2015, 35(6): 549-555.
[6]	WANG Meiqing, YANG Weihua, CAI Chengjie, LIN Xiaoyan, FU Fang. Influence of Polyvinyl Alcohol on Structure and Property of PbO₂ Electrode[J]. 中国腐蚀与防护学报, 2015, 35(1): 81-85.
[7]	NIE Yuanyuan, DUAN Jizhou, DU Min, HOU Baorong. Influence of NaN₃ on Cathodic Oxygen Reduction Induced by Microbe-assisted Catalysis on Surface of 316LSS in Seawater[J]. 中国腐蚀与防护学报, 2014, 34(4): 359-365.
[8]	ZHU Zhiping, LU Haiwei, TANG Xueying, JIAO Xiaocui, YU Weiwei. Corrosion Characteristics of 15CrMoG Steel a Supercritical Unit Water-wall Tube Material in Waters ofDifferent Water Chemistry[J]. 中国腐蚀与防护学报, 2014, 34(3): 243-248.
[9]	LI Junfeng, WEN Jiuba, HE Junguang, MA Jingling, LI Gaolin. MECHANISM OF PITTING CORROSION ACTIVATION AND PASSIVATION OF Al-Zn-Sn-Ga ALLOY[J]. 中国腐蚀与防护学报, 2012, 32(5): 407-411.
[10]	WANG Guangjin, PAN Mu. RESEARCH PROGRESS OF IRIDIUM OXIDE COMPOSITES ELECTRODES[J]. 中国腐蚀与防护学报, 2012, 32(2): 85-89.
[11]	YUAN Bifei, ZHENG Yanjun, JING Dong, CUI Lishan, LU Guiwu. CARBURIZATION BEHAVIORS OF Mn-Cr-O AND Mn-Al-O SPINELS[J]. 中国腐蚀与防护学报, 2011, 31(1): 18-22.
[12]	;. Coking and Carburizing Behaviors of Metal Materials in High Temperature Carbon-Containing Atmosphere[J]. 中国腐蚀与防护学报, 2004, 24(3): 188-192 .
[13]	Jiangjiang Song; Jianian Shen; Lingfeng Li; Shudian Yao. CHARACTERISTICS AND PROPERTY OF PHOTO-CATALYTIC NANO CRYSTALLINE TITANIUM DIOXIDEFILM PREPARED BY ELECTROCHEMICAL OXIDATION〖ST〗〖HT〗〖WT〗〖KH1D〗[J]. 中国腐蚀与防护学报, 2002, 22(2): 98-100 .
[14]	Zhanpeng Lv; Wu Yang; Delun Huang. OPEN CIRCUIT STATE AND CATHODIC DIFFUSION PROCESS OF COPPER IN SULFURIC ACID SOLUTION CONTAINING FERRIC ION INTHE PRESENCE OF MAGNETIC FIELD WITH DIFFERENT INTENSITY[J]. 中国腐蚀与防护学报, 2001, 21(3): 129-136 .
[15]	Xinqiang Wu; Qugui Zheng; Wei Ke. STUDY ON SURFACE COKING MORPHOLOGY OF PURE NICKEL AND ITS CORRELATIVE FACTORS[J]. 中国腐蚀与防护学报, 2001, 21(1): 10-18 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed