| STUDY ON ELECTRO CHEMICAL IMPEDANCE STECTRUM OF FeAl INTERMETALLIC COMPOUND DURING CORROSION IN MOLTEN (Li,k)2CO3 |
| Wen Wang;; |
| 中科院金属所 |
|
|
|
|
Abstract Electrochemical impedance spectrum(EIS)was wmployed to study the corrosion of FeAl in molten (Li,K)2CO3 at 650℃.It is shown that the EIS exhibited the characteristics of diffusion-controlled reaction at the initial corrosion stage,while it was composed od two capacitance loops during wxtended corrosion.The corrosion of FeAl at the initial stage was controlled by the diffusion of oxidants O2 and O22- formed by the chemical dissolution of oxygen in the melt.The concentration of O2- at the scale/melt interface generated by the reduction of O2- and O22- tended to increase,which might promote the reaction of Fe2O3 grown on FeAl with Li2O, forming LiFeO2. The formation of LiFeO2 gave rise to a larger amss gain of FeAl,but provided a better protection to the alloy.With the formation of continuous external LiFeO2 and inner Al2O3 layer,the corrosion of FeAl was controlled by the transfer of the charged particles through the scale.Corresponding equivalent circuits were also proposed to fit the EIS of FeAl.
|
|
Received: 08 December 1998
|
|
Corresponding Authors:
Wen Wang
|
1 杜森林,卢洪德,路连清- 化工进展,1994 ,1:29
2 Spiegel M,BiedenkopfP,Grabke HJ.Corro.Sci.,1997,39(7) :1193
3 Donado RA, Marianowski LG,Maru HC,Selman JR.J.Electrochem .SOC.,1984,131 :2535
4 曾潮流,张鉴清,牛焱,吴维山文- 科学通报,1994,39(13) :1190
5 牛焱,张鉴清,吴维山文- 中国腐蚀与防护学报,1990,10:221
6 Smith SW,Vogel W M,Kapelmer S.J.Electrochem .Soc.,1982,129:1668
7 王佳,施存余,宋诗哲- 中国腐蚀与防护学报,1989,9 :125 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|