THE EFFECT OF Y-IMPLANTATION ON HIGH TEMPERATURE OXIDATION BEHAVIOR OF ALUMINIZED Ni-BASE ALLOY

J Chin Soc Corr Pro

1996, Vol. 16

Issue (1): 42-46 DOI:

Current Issue | Archive | Adv Search

THE EFFECT OF Y-IMPLANTATION ON HIGH TEMPERATURE OXIDATION BEHAVIOR OF ALUMINIZED Ni-BASE ALLOY

Xin Li;Li Meishuan;Li Tiefan

Download:

PDF(1946KB)
Export: BibTeX | EndNote (RIS)

Abstract The influences of implanted yttrium at doses of 1×10 17； 1×10 16；1×10 15Y+／cm2 on the high temperature oxidation behaviro of aluminized Ni-15Cr-6Al alloy were studied by electric thermal balance ,scanning electron microscopy（SEM）and X－ray diffraction(XRD).The results indicated that Y－implantation at the three doses had no effects on oxidation kinetics of the alloy．However，ion implantation dose of 1× 10 17 Y+／cm2 changed the oxide morphology and facilitated plastic deformation of the oxide scale， thus it altered the ways of stress relaxation in the scale and improved the scale adhension．The change of the oxide morphology might result from the change of growth mechanism of the oxide scale， Ion implantation doses of 1×10 16 1×10 15Y+／cm2 had only a little or no effect on the oxide scale morphology.

Key words: Oxidation Aluminize Ion－implantation

Received: 25 February 1996

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

Xin Li;Li Meishuan;Li Tiefan. THE EFFECT OF Y-IMPLANTATION ON HIGH TEMPERATURE OXIDATION BEHAVIOR OF ALUMINIZED Ni-BASE ALLOY. J Chin Soc Corr Pro, 1996, 16(1): 42-46.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1996/V16/I1/42

1WhittlePP,StringerJJ．Phil．Thans．R．Soc．London;1980,A295:3092HuntzAM．Mat．Sci．Eng．;1987;87:2513StottFH;WoodDC．idid,1987,87:2674JedlinskiJ,BorchardtG．Oxid．Met．;1991,36:3715ChoquetPSMevrelR．Mat．Sci．Eng,1989,A120:1536KofstadP．Oxid．Met,1985;24:2657RybickiGC,SmialekJL．Oxid．Met,1989,31:2758李铁藩,辛丽,李美栓．离子注入钇对镍基合金渗铝层氧化膜生长应力的影响(待发表文章)

[1]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	LIU Xiao, WANG Hai, ZHU Zhongliang, LI Ruitao, CHEN Zhenyu, FANG Xudong, XU Fanghong, ZHANG Naiqiang. Oxidation Characteristics of Austenitic Heat-resistant Steel HR3C and Sanicro25 in Supercritical Water for Power Station[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[3]	XIE Dongbai, HONG Hao, WANG Wen, PENG Xiao, DUO Shuwang. Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[4]	CAO Jingyi, FANG Zhigang, CHEN Jinhui, CHEN Zhixiong, YIN Wenchang, YANG Yange, ZHANG Wei. Preparation and Properties of Micro-arc Oxide Film with Single Dense Layer on Surface of 5083 Aluminum Alloy[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	FANG Xudong, LIU Xiao, XU Fanghong, LI Ruitao, ZHU Zhongliang, ZHANG Naiqiang. Oxidation Behavior in Supercritical Water of Domestic Austenitic Steel C-HRA-5 for Uultra-supercritical Power Stations[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[6]	ZHENG Yanxin, LIU Ying, SONG Qingsong, ZHENG Feng, JIA Yuchuan, HAN Peide. High-temperature Oxidation Behavior and Wear Resistance of Copper-based Composites with Reinforcers of C, ZrSiO₄ and Fe[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[7]	XU Xunhu,HE Cuiqun,XIANG Junhuai,WANG Ling,ZHANG Honghua,ZHENG Xiaodong. High Temperature Oxidation Behavior of Co-20Re-25Cr-1Si Alloy in 0.1 MPa Pure Oxygen[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[8]	JIANG Dongxue,FU Ying,ZHANG Junwei,ZHANG Wei,XIN Li,ZHU Shenglong,WANG Fuhui. Preparation and Properties of Alumina Ceramic Film on Ti-alloy Surface[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[9]	XIAO Jintao,CHEN Yan,XING Mingxiu,JU Pengfei,MENG Yingen,WANG Fang. Effect of Process Parameters on Corrosion Resistance of Anodizing Film on 2195 Al-Li Alloy[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[10]	AI Peng,LIU Lixiang,LI Xiaogang,JIANG Wentao. Influence of TiAlSiN Coatings on High Temperature Oxidation Resistance of γ-TiAl Based Alloys[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[11]	Yunhai MA. Effect of Shot Peening on Oxidation Resistance of Super 304H Steel in Supercritical Steam[J]. 中国腐蚀与防护学报, 2019, 39(3): 245-252.
[12]	Junjie XIA,Hongzhi NIU,Min LIU,Huazhen CAO,Guoqu ZHENG,Liankui WU. Enhancement of High Temperature Oxidation Resistance of Ti48Al5Nb Alloy via Anodic Anodization in NH₄F Containing Ethylene Glycol[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[13]	Dongbai XIE,Youyu ZHOU,Jintao LU,Wen WANG,Shenglong ZHU,Fuhui WANG. Effect of Al/Si Content on Corrosion of Ni-based Alloys in Supercritical Water[J]. 中国腐蚀与防护学报, 2019, 39(1): 68-76.
[14]	Ling WANG,Junhuai XIANG,Honghua ZHANG,Songlin QIN. High Temperature Oxidation Behavior of Three Co-20Re-xCr Alloys in 3.04×10^-5 Pa Oxygen at 1000 and 1100 ℃[J]. 中国腐蚀与防护学报, 2019, 39(1): 83-88.
[15]	Hao CHEN,Qing CHEN,Li XIN,Long SHI,Shenglong ZHU,Fuhui WANG. Preparation and High Temperature Corrosion Behavior of Aluminized Nanocrystalline Coating on DD98M Alloy[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed