X70级管线钢抗硫化物应力腐蚀开裂实验研究

中国腐蚀与防护学报

2008, Vol. 28

Issue (2): 86-89

研究报告

本期目录 | 过刊浏览

X70级管线钢抗硫化物应力腐蚀开裂实验研究

谢广宇

中钢炉料公司

Investigation of sulfide stress corrosion cracking for X70 pipeline steel

中钢炉料公司

全文: PDF(928 KB)

摘要: 用三点弯曲方法及SEM?TEM等手段研究了不同组织类型的X70级管线钢硫化物应力腐蚀开裂(SSCC)行为?结果表明,显微组织以均匀细小的针状铁素体为主的管线钢具有优良的抗SSCC性能;这主要是源于针状铁素体内高密度缠结的位错和碳氮化物在位错网络上的沉淀析出起到了强烈的氢陷阱作用?

关键词 ：管线钢, 针状铁素体, 硫化物应力腐蚀开裂

Abstract：Using the NACE standard bent-beam test, sulfide stress corrosion cracking (SSCC) of different types microstructure in X70 grade pipeline steel with different types of microstructure was investigated. The X70 pipeline steel are all obtained from Ansteel, The result showed that the X70 pipeline steel had the excellent performance to the SSCC and the microstructure dominated by fine and homogeneous acicular ferrite had the excellent resistance to SSCC. Both the high density tangled dislocation and carbonitride precipitiated along with dislocation networks are the main reasons for the steel with acicular ferrite to have excellent resistance to SSCC. The microstructure is the main factor to decide the SSCC performance.

Key words： pipeline steel acicular ferrite sulfide stress corrosion cracking (SSCC)

收稿日期: 2006-09-12

通讯作者: 谢广宇 E-mail: ghostcool@126.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	谢广宇
44.8K

引用本文:

谢广宇 . X70级管线钢抗硫化物应力腐蚀开裂实验研究[J]. 中国腐蚀与防护学报, 2008, 28(2): 86-89 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I2/86

[1]Li H L.Developingpulse and prospect ofoil and gas transmission pipe[J].Welded Pipe and Tube,2004,27(6):1-11(李鹤林.油气输送钢管的发展动向与展望[J].焊管,2004,27(6):1-11)
[2]Tao Y Y,Du Z Y,Li Y T.Influencing factors of SSCC for domes-tic pipeline steels[J].J.Tianjin Univ.,2004,37(4):358-362(陶勇寅,杜则裕,李云涛.管线钢硫化氢应力腐蚀的影响因素[J].天津大学学报,2004,37(4):358-362)
[3]Wu J W,Li X G,Du C W,et al.Short-term corrosion behavior of X70 steel in Ku'Erle soil[J].J.Chin.Soc.Corros.Prot.,2005,25(1):15-19(武俊伟,李晓刚,杜翠薇等.X70钢在库尔勒土壤中短期腐蚀行为研究[J].中国腐蚀与防护学报,2005,25(1):15-19)
[4]Zhao M C,Shan Y Y,Li Y M.Effect of microstructure on sulfidestress corrosion cracking of pipeline steels[J].Acta.Metall.Sin.,2001,37(10):1087-1092(赵明纯,单以银,李玉梅等.显微组织对管线钢硫化物应力腐蚀开裂的影响[J].金属学报,2001,37(10):1087-1092)
[5]Laboratory Testing of Metals for Resistance to Specific Forms ofEnvironmental Cracking in H2S Environments.NACE TM 0177-2005,NACE International[S].2005(美国腐蚀工程师协会(NACE TM 0177-2005)标准[S].)
[6]Evaluation of Pipeline and Vessel Steels for Resistance to Hydro-gen Induced Cracking,NACE TM 0284-2003,NACE Internation-al[S].2003(美国腐蚀工程师协会(NACE TM 0284-2003)标准[S].)
[7]Kong J H,Zhen L,Guo B,et al.Influence of Mo content on mi-crostructure and mechanical properties of high strength pipelinesteel[J].Mater.Des.,2004,25:723-728
[8]Li M,Li XG,Chen H.A reviewon corrosion behavior and mechanism of metals in wet H2S[J].Corros.Sci.Prot.Technol.,2005,17(2):107-111(李明,李晓钢,陈华.在湿H2S环境中金属腐蚀行为和机理研究概述[J].腐蚀科学与防护,2005,17(2):107-111)E

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[4]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[5]	王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[6]	陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[7]	袁玮,黄峰,甘丽君,戈方宇,刘静. 显微组织对X100管线钢氢致开裂及氢捕获行为影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 536-542.
[8]	史显波,杨春光,严伟,徐大可,闫茂成,单以银,杨柯. 管线钢的微生物腐蚀[J]. 中国腐蚀与防护学报, 2019, 39(1): 9-17.
[9]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[10]	廖梓含, 宋博, 任泽, 何川, 陈旭. X70钢及其焊缝在Na₂CO₃+NaHCO₃溶液中电化学腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 158-166.
[11]	任继栋,高荣杰,张宇,刘勇,丁甜. 混酸刻蚀-氟化处理制备X80管线钢双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 233-240.
[12]	张康南,吴明,谢飞,王丹,伞宇曦,江峰. 磁场对X80管线钢在沈阳草甸土中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 148-154.
[13]	罗金恒,胥聪敏,杨东平. SRB作用下X100管线钢在酸性土壤环境中的应力腐蚀开裂行为[J]. 中国腐蚀与防护学报, 2016, 36(4): 321-327.
[14]	张弟,梁平,张云霞,史艳华,秦华. 库尔勒土壤模拟溶液中形成的腐蚀产物膜对X80钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(4): 313-320.
[15]	宋博强,陈旭,马贵阳,刘睿. SRB对X70管线钢在近中性pH溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(3): 212-218.

Viewed

Full text

Abstract

Cited

Shared

Discussed