NaCl水溶液中缓蚀剂控制电偶腐蚀的研究

艾俊哲;郭兴蓬;梅平

长江大学化学与环境工程学院

Study on corrosion mechanism of carbon steel induced by Galvanic coupling in inhibitor solution

;;

长江大学化学与环境工程学院

全文: PDF(1123 KB)

摘要: 用电化学方法和原子力显微镜及红外光谱分析技术研究了阳离子缓蚀剂（咪唑啉衍生物）在电偶电极上的吸附行为及其对电偶腐蚀的抑制作用。结果表明，在NaCl水溶液中，缓蚀剂只吸附在碳钢表面，而不吸附在不锈钢表面；当碳钢与不锈钢耦合后，缓蚀剂在偶对的阴极（不锈钢）和阳极（碳钢）都有吸附。缓蚀剂在偶对阳极（碳钢）上的覆盖度小于在单独碳钢上的覆盖度，并且缓蚀剂与前者表面的结合力也有所降低。电偶对中碳钢的腐蚀归因于缓蚀剂的覆盖度与结合力减小的双重因素。

关键词 ：原子力显微镜, 电偶腐蚀, 红外光谱, 阳离子缓

Abstract：The adsorption behavior of imidazoline derivative as a cationic inhibitor for inhibiting galvanic corro?鄄sion has been investigated by using electrochemical methods, atomic force microscopy (AFM) and Fourier trans?鄄form infrared spectroscopy (FTIR) technology. The results show that the inhibitor adsorbs on the surface of carbon steel while it does not adsorb on the surface of stainless steel in aqueous NaCl solution. When the two metals are electrically coupled in NaCl solution, the inhibitor can adsorb to the surface of both carbon steel and stainless steel. However, in this case, the surface coverage of the inhibitor film formed on the carbon steel decreases com?鄄pared with that on the surface of single carbon steel immersed in the same electrolyte, and the adsorbability of the inhibitor on the surface of carbon steel is weakened. The corrosion failure for carbon steel of the couple at?鄄tributes to the decreases of both coverage and adorability of the inhibitor adsorbed on the metal surface.

Key words： AFM Galvanic corrosion FTIR Cationic inhibitor adsorption Electrochemical method

收稿日期: 2006-08-01

通讯作者: 艾俊哲 E-mail: aajzz@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	艾俊哲
	郭兴蓬
	梅平
44.8K

引用本文:

艾俊哲; 郭兴蓬; 梅平 . NaCl水溶液中缓蚀剂控制电偶腐蚀的研究[J]. 中国腐蚀与防护学报, 2008, 28(2): 90-94 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I2/90

[1]Scully J R,Hack H P.in:Hack H P,Ed.Galvanic Corrosion,ASTM STP987[S].1988,136-157
[2]Hack H P,Ed.Galvanic Corrosion,ASTM STP987,American Soci-ety for Testing and Materials[S].PA,1988
[3]Ashley C J,in:Strutt J E,Nicholl J R,Eds.Plant Corrosion-Pre-diction and Performance[M].Chichester,England:Ellis Horwood Ltd.,1987,53-78
[4]Yang H Y,Chen J J,Cao C N,et al.Study on corrosion and inhi-bition mechanism in H2S aqueous solutions VI.The relationshipbetween molecular structure of imidazoline derivatives and inhibi-tion performance in H2S solutions[J].J.Chin.Soc.Corros.Prot.,2002,22(3):148-152(杨怀玉,陈家坚,曹楚南等.H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅵ.H2S溶液中咪唑啉衍生物分子结构与其缓蚀性能的关系[J].中国腐蚀与防护学报,2002,22(3):148-152)
[5]Yang H Y,Chen J J,Cao C N.Study on corrosion and inhibition mechanism in H2S aqueous solutions VII.Effect of imidazoline derivatives on the corrosion process of mild steel electrodes in H2Ssolutions[J].J.Chin.Soc.Corros.Prot.,2002,22(6):321-325(杨怀玉,陈家坚,曹楚南等.H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅶ.H2S溶液中咪唑啉衍生物对碳钢腐蚀电极过程的影响[J].中国腐蚀与防护学报,2002,22(6):321-325)
[6]Ai J Z,Mei P,Chen W.et al.CO2/H2S corrosion of carbon steel and its inhibition behavior[J].J.Yangtze Univ.,(Natural scienceedition),2006,3(4):39-41(艾俊哲,梅平,陈武等.碳钢CO2/H2S腐蚀及缓蚀行为试验研究[J].长江大学学报(自科版),2006,3(4):39-41)
[7]Chetouani A,Hammouti B,Benhadda T,et al.Inhibitive action of bipyrazolic type organic compounds towards corrosion of pure ironin acidic media.[J].Appl.Surf.Sci.,2005,249,375-385
[8]Ai J Z,Ji E Y,Zu R,et al.Inhibiting effect of thiourea derivative of imidazoline on galvanic corrosion[J].Chemical Engineering ofOil and Gas,2004,33(5):357-361(艾俊哲,姬鄂豫,祖荣等.咪唑啉硫脲衍生物对电偶腐蚀的抑制作用[J].石油与天然气化工,2004,33(5):357-361)
[9]Kuznetsov Y I,Ibatullin K A.On the inhibition of the carbon diox-ide corrosion of steel by carboxylic acids[J].Zashchita Metalloy,2002,38:496-501
[10]Huang G Q,Yu C J,Li L S.Study on galvanic corrosion of steelcouples in sea water[J].J.Chin.Soc.Corros.Prot.,2001,21(1):46-53(黄桂桥,郁春娟,李兰生.海水中钢的电偶腐蚀研究[J].中国腐蚀与防护学报,2001,21(1):46-53)
[11]Osman M M,Shalaby M N.Some ethoxylated fatty acids as corro-sion inhibitors for low carbon steel in formation water[J].Mater.Chem.Phys.,2003,77(1):261-269
[12]Abdallah M.Rhodanine azosulpha drugs as corrosion inhibitors for corrosion of 304 stainless steel in hydrochloric acid solution[J].Corros.Sci.,2002,44(4):717
[13]Wei Z Q,Duby P,Somasundaran P.Pitting inhibition of stainlesssteel by surfactants:an electrochemical and surface chemical ap-proach[J].J.Colloid Interf.Sci.,2003,259(1):97-102
[14]Ai J Z,Guo X P,Qu J E,Chen Z Y.Adsorption behavior of imida-zoline amide on the surface of galvanic electrode[J].Acta Phys.Chim.Sin.,2005,21(10):1096-1101(艾俊哲,郭兴蓬,屈钧娥等.咪唑啉酰胺在电偶电极表面的吸附行为[J].物理化学学报,2005,21(10):1096-1101)
[15]Cao C N,Zhang J Q.An Introduction to Electrochemical Impedance Spectroscopy[M].Beijing:Science Press,2002(曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002)

[1]	丁清苗, 秦永祥, 崔艳雨. 大气环境中飞机构件的电偶腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 455-462.
[2]	伊红伟, 胡慧慧, 陈长风, 贾小兰, 胡丽华. CO₂环境下油酸咪唑啉对X65钢异种金属焊缝电偶腐蚀的抑制作用研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[3]	白苗苗, 白子恒, 蒋立, 张东玖, 姚琼, 魏丹, 董超芳, 肖葵. H62黄铜/TC4钛合金焊接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 159-166.
[4]	黄宸,黄峰,张宇,刘海霞,刘静. 高强耐候钢焊接接头电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 527-535.
[5]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[6]	王振华, 白杨, 马晓, 邢少华. 钛合金和铜合金管路电偶腐蚀数值仿真[J]. 中国腐蚀与防护学报, 2018, 38(4): 403-408.
[7]	刘艳洁,王振尧,王彬彬,曹岩,霍阳,柯伟. 实时监测技术研究薄液膜下电偶腐蚀的机理[J]. 中国腐蚀与防护学报, 2017, 37(3): 261-266.
[8]	赵景茂,赵起锋,姜瑞景. 咪唑啉缓蚀剂在CO₂/H₂S共存体系中的构效关系研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 142-147.
[9]	赵欣,胡裕龙,董赋,张晓东,王智峤. 湿态电绝缘对电偶腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 175-182.
[10]	孙朝晖,Masoumeh Moradi,杨丽景,Robabeh Bagheri,宋振纶,陈艳霞. 越南芽孢杆菌对2507双相不锈钢加速腐蚀的影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 659-664.
[11]	魏强,李谋成,沈嘉年. 两种不锈钢在模拟消声器环境中的电偶腐蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(3): 233-238.
[12]	赵晓宏, 郭泉忠, 杜克勤, 郭兴华, 王勇. 不同涂层处理的汽车紧固件用ST12冷轧钢与SS400热轧钢的电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(1): 86-90.
[13]	徐宏妍, 李智勇. AZ91D镁合金电偶腐蚀的研究[J]. 中国腐蚀与防护学报, 2013, 33(4): 298-305.
[14]	万俐杜伟李佳佳丁毅陈步荣. 十八硫醇自组装膜对青铜-银电偶腐蚀的抑制作用[J]. 中国腐蚀与防护学报, 2013, 33(3): 245-250.
[15]	蒋穹,缪强,丁祥,魏小昕. 片状Al-Zn-Si合金粉的析氢行为与抑制剂研究[J]. 中国腐蚀与防护学报, 2013, 33(1): 61-69.

Viewed

Full text

Abstract

Cited

Shared

Discussed