STUDY ON THE EFFECT OF ZINC PIGMENTS SIZE ON THE ELECTROCHEMICAL BEHAVIOR OF ORGANIC ZINC-RICH COATINGS

Bin Liu;Ying Li;Fuhui Wang

中科院沈阳金属研究所;金属腐蚀与防护国家重点实验室

全文: PDF(190 KB)

摘要: 利用电化学阻抗谱(EIS)技术，研究了锌粉颜料平均粒度分别为7 μm、35 μm和500 nm的有机富锌涂层的电化学行为.研究表明，在阴极保护阶段，含有纳米尺度锌粉颜料的富锌涂层可对基底钢材提供更有效的电流保护，但锌粉颜料尺寸对富锌涂层阴极保护作用时间的长短没有显著影响；在阻挡保护阶段，含有纳米尺度锌粉颜料的富锌涂层中，锌粉的腐蚀速率较低，涂层具有较大的涂层电阻和较小的涂层电容，发展为具有较强阻挡保护作用的涂层.

关键词 ：颜料尺寸, 有机富锌涂层, 电化学行为, 电化学

Abstract：The electrochemical behavior of zinc-rich epoxy coa tings with different size of zinc pigments has been studied by EIS.The experimen tal results showed that,in the cathodic protection stage,the coating with nano-s cale zinc pigments could provide galvanic protection more efficiently,but had no effect on the duration of cathodic protection.However,in the barrier protection stage,the coating with nano-scale zinc pigments had lower zinc dissolution rate ,lower coating capacitance and higher coating resistance,becoming more efficient in barrier protection.

Key words： pigment size organic zinc-rich coatings electrochemi cal behavior EIS

收稿日期: 2003-04-23

ZTFLH:

TG174.41

通讯作者: 刘斌

Corresponding author: Bin Liu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘斌
	李瑛
	王福会
44.8K

引用本文:

刘斌; 李瑛; 王福会 . 锌粉颜料尺寸对有机富锌涂层电化学行为的影响[J]. 中国腐蚀与防护学报, 2003, 23(6): 350-354 .
Bin Liu, Ying Li, Fuhui Wang. STUDY ON THE EFFECT OF ZINC PIGMENTS SIZE ON THE ELECTROCHEMICAL BEHAVIOR OF ORGANIC ZINC-RICH COATINGS. J Chin Soc Corr Pro, 2003, 23(6): 350-354 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I6/350

[1]AbreuCM ,IzquierdoM ,MerinoP ,etal.Anewapproachtothedeterminationofthecathodicprotectionperiodinzinc-richpaints[J].Corrosion,1999,55(12):1173-1181
[2]GervasiCA ,SarliARDi,CavalcantiE ,etal.Thecorrosionprotec tionofsteelinsea-waterusingzinc-richalkydpaints-anassess mentofthepigment-contenteffectbyEIS [J].Corros.Sci.,1994,36(12):1963-1972
[3]AbreuCM ,IzquierdoM ,KeddamM ,etal.Electrochemicalbe haviourofzinc-richepoxypaintsin3%NaClsolution[J].Elec trochim.Acta,1996,41(15):2405-2415
[4]RealSG ,EliasAC ,VilcheJR ,etal.Anelectrochemicalimpedancespectroscopystudyofzincrichpaintsonsteelsinartificialsea-wa terbyatransmission-linemodel[J].Electrochim.Acta,1993,38(14):2029-2035
[5]ArmasRA ,GervasiCA ,SarliADi,etal.Zinc-richpaintsonsteelsinartificialseawaterbyEIS[J].Corrosion,1992,48(5):379-383
[6]VilcheJR ,BucharskyEC ,GiudiceCA .ApplicationofEISandSEMtoevaluatetheinfluenceofpigmentshapeandcontentinZRPformulationsonthecorrosionpreventionofnavalsteel[J].Corros.Sci.,2002,44(6):1287-1309
[7]FeliuS ,BarajasR ,BastidasJM ,MorcilloM .Mechanismofcathod icprotectionofzinc-richpaintsbyelectrochemicalimpedancespectroscopy.Ⅰ.Galvanicstage[J].J.Coat.Technol.,1989,61(775):63-69
[8]FeliuS ,BarajasR ,BastidasJM ,MorcilloM .Mechanismofcathod icprotectionofzinc-rich paintsbyelectrochemicalimpedancespectroscopy.Ⅱ.Barrierstage[J].J.Coat.Technol.,1989,61(775):71-76
[9]FaidiSE ,ScantleburyJD ,BullivantP ,WhittleNT ,SavinR .Anelectrochemicalstudyofzinc-containingepoxycoatingsonmild-steel[J].Corros.Sci.,1993,35(5-8):1319-1328
[10]PereiraD ,ScantleburyJD ,FerreiraMGS ,AlmeidaE .Theappli cationofelectrochemicalmeasurementstothestudyandbehaviorofzinc-richcoatings[J].Corros.Sci.,1990,30(11):1135-1147
[11]NovoaXR ,IzquierdoM ,MerinoP ,EspadaL .Electrochemicalimpedancespectroscopyandzeroresistanceammeters(ZRA)astoolsforstudyingthebehaviorofzinc-richinorganiccoatings[J].Mater.Sci.Forum,1989,44-45:223
[12]IzquierdoM ,NovoaXR ,PenaG ,EspadaL .Themechanismofprotectionofzinc-richinorganiccoatings.astudybasedonelec trochemicalimpedancespectroscopy(EIS)[J].Mater.Sci.Fo rum,1992,111-112:257

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[4]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[5]	孙海静, 覃明, 李琳. 深海低溶解氧环境下Al-Zn-In-Mg-Ti牺牲阳极性能研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 508-516.
[6]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[7]	翟思昕, 杨幸运, 杨继兰, 顾剑锋. 淬火-配分-回火钢在模拟海水环境中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[8]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[9]	付海波, 刘晓茹, 孙媛, 曹大力. 环氧树脂/重结晶碳化硅复合材料的抗腐蚀性能[J]. 中国腐蚀与防护学报, 2020, 40(4): 373-380.
[10]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[11]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[12]	王廷勇, 董如意, 许实, 王辉. 石墨烯改性Ti/IrTaSnSb-G金属氧化物阳极在低温和低盐NaCl溶液中的电化学性能[J]. 中国腐蚀与防护学报, 2020, 40(3): 289-294.
[13]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[14]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[15]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.

Viewed

Full text

Abstract

Cited

Shared

Discussed