用丝束电极(WBE)评价不锈钢在NaCl溶液中点蚀敏感性

翁永基

北京石油大学

EVALUATION OF PITTING SENSITIVITY OF STAINLESS STEELIN NaCl SOULTIONS BY MEANS OF WIRE BEAM ELECTRODES(WBE)

Yongji Weng

北京石油大学

全文: PDF(151 KB)

摘要: 用丝束电极作为参比或辅助电极，测量不锈钢材料在不同氯化物浓度溶液中的表面性质差异.发现表面电极电位、电偶电流和交流阻抗测量数据极差和环境氯离子浓度对数均呈良好线性关系.可作为评价材料点蚀敏感性指标，要比传统指标(如点蚀电位和阳极极化曲线滞后环面积等)更加优越.此外，基于自然浸泡试件的材料表面电位极差-时间曲线，可用丝束电极研究材料的点蚀潜伏期.

关键词 ：不锈钢, 点蚀敏感性, 潜伏期, 丝束电极, 极差指

Abstract：The surface differentials of stainless steel in dif ferent NaCl consistence solutions were measured using wire beam electrodes (WBE) as reference or supporting electrodes.It was found that the data-ranges measure d by WBE for items of potentials or galvanic currents or Faraday impedance had g ood linear relationship with logarithm of NaCl concentrations.They had superiori ty as the indexes of materials pitting sensitivity than the traditional indexes such as,the pitting potential,the lag ring area in scan anodic polarization curv es and so on.In additions,the pitting latent periods of materials could be also studied by WBE based on the curves of potential ranges vs.time in natural immers ion tests.

Key words： stainless steel pitting sensitivity latent period WBE indexes of the data-ranges

收稿日期: 2002-06-11

ZTFLH:

TG174.2

通讯作者: 翁永基

Corresponding author: Yongji Weng

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	翁永基
44.8K

引用本文:

翁永基 . 用丝束电极(WBE)评价不锈钢在NaCl溶液中点蚀敏感性[J]. 中国腐蚀与防护学报, 2003, 23(6): 326-329 .
Yongji Weng. EVALUATION OF PITTING SENSITIVITY OF STAINLESS STEELIN NaCl SOULTIONS BY MEANS OF WIRE BEAM ELECTRODES(WBE). J Chin Soc Corr Pro, 2003, 23(6): 326-329 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I6/326

[1]SongShizhe.ResearchMethodsofCorrosionElectrochemistry[M].Beijing:ChemicalIndustryPress,1988,187-191(宋诗哲.腐蚀电化学研究方法[M ].北京:化学工业出版社,1988,187-191)
[2]WuJianhua,LiuGuangzhou,YuHui,etal.Electrochemicalresearchofcorrosionbyoceanmicro-organisms[A].QuotedFrom:Sympo siumof1998NationalConferenceonCorrosionElectrochemistry[C].EditedbyHunanUniversity,1998,83(吴建华,刘光洲,于辉等.海洋微生物腐蚀的电化学研究方法[A].引自:一九九八年全国腐蚀电化学及测试方法学术论文集[C].湖南大学编,1998,83)
[3]CaoChu′nan,ChangXiaoyuan,LinHaichao.Studyonfeaturesofcurrentnoiseduringpittingcorrosion[J].J .Chin.Soc.Corros.Prot.,1989,9(1):21-28.(曹楚南,常晓元,林海潮.孔蚀过程中电化学噪声特征[J].中国腐蚀与防护学报,1989,9(1):21-28)
[4]ShiQingrong,LinHaichao,CaoChu′nan.Studyonwhitenoiseandcut-offfrequenceduringpittingcorrosion[J].J.Chin.Soc.Cor ros.Prot.,1989,10(1):29-33(石青荣,林海潮,曹楚南.孔蚀过程中电化学噪声“白噪声”水平与截止频率的研究[J].中国腐蚀与防护学报,1989,10(1):29-33)
[5]HuRongzong,LinChangjian,ZhouXiang,etal.Investigationonthecorrosionpotentialimmergingofironelectrodeatinterfaceofcon crete/reinforcingbarincorrosionmedia[A].QuotedForm:Sympo siumofConferenceonMaterialCorrosion&ProtectioninTwoShoresofStrait[C].EditedbyLinChangjian,CaiWenda.Xiamen:XiamenUniversityPublishers,1998,634-636(胡荣宗,林昌健,周香等.阵列电极研究钢筋/混凝土界面腐蚀过程[A].引自:海峡两岸材料腐蚀与防护研究进展[C].林昌健、蔡文达主编.厦门:厦门大学出版社,1998,634-636)
[6]ZhongQingdong,ShuYude,JiangHanying.Relationbetweenelec trochemicalheterogeneityofrustproofoil-filmanditsprotection[J].J.ZhongnanIndustrialUniversity,1995,26(6):834(钟庆东,舒余德,蒋汉赢.防锈油膜电化学不均匀性与其防护性能关系[J].中南工业大学学报,1995,26(6):834)
[7]ZhangHuamin,QiuYubin.Studyonlocalcorrosioncausedbysodi umnitro-benzoateusingwirebeamelectrodes[J].OilfieldChem istry,1996,13(2):165-168(张华民,邱于兵.用丝束电极研究对硝基苯甲酸钠引起的局部腐蚀[J].油田化学,1996,13(2):165-168)
[8]ZhaoHaiyan.Studyondetectionmethodsforpittingof18-8stain lesssteel(Dissertation)[D].Beijing:UniversityofPetroleum,2002,4(赵海燕.18-8不锈钢点蚀检测方法的研究(石油大学硕士学位论文)[D].北京:石油大学,2002,4)

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[7]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[10]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[11]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[12]	付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[13]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[14]	李雨,关蕾,王冠,张波,柯伟. 机械应力对不锈钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 215-226.
[15]	丰涵,宋志刚,吴晓涵,李惠,郑文杰,朱玉亮. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 138-144.

Viewed

Full text

Abstract

Cited

Shared

Discussed