含1%Cr的N80钢CO2腐蚀产物膜特征

中国腐蚀与防护学报

2003, Vol. 23

Issue (6): 330-334

研究报告

本期目录 | 过刊浏览

含1%Cr的N80钢CO2腐蚀产物膜特征

陈长风;路民旭;赵国仙

北京科技大学材料科学与工程学院

CHARACTERISTICS OF CO2 CORROSION SCALES ON 1%Cr-CONTAINING N80 STEEL

Changfeng Chen;Minxv Lu;Guoxian Zhao

北京科技大学材料科学与工程学院

全文: PDF(210 KB)

摘要: 在模拟油田CO2腐蚀环境下，研究了含1%Cr的N80钢腐蚀产物膜的特征.结果表明，试验条件下Cr会在腐蚀产物膜中富积形成非晶态的Cr(OH)3.含1 %Cr的N80油套管钢CO2腐蚀产物膜是由FeCO3晶体与Cr(OH)3混合构成，导致腐蚀产物膜具有阳离子选择性，使阳极反应受到抑制，腐蚀速率降低.腐蚀介质中的阴离子会穿过FeCO3晶体到达膜与基体界面，腐蚀基体金属，导致点蚀发生.

关键词 ： CO2腐蚀, 腐蚀产物膜, N80钢, 点蚀

Abstract：While simulating the CO2 corrosion environment in oilfield,the characteristics of CO2 corrosion scales on 1%Cr-containing N80 s teel were studied.The results demonstrated that Cr could be enriched in corrosio n scales forming amorphous compound Cr(OH)3 and the corrosion scale is compose d of Cr(OH)3 and FeCO3 crystals,that make the corrosion scale has the charac ter of cation-selectivity and as a result the anodic reactions could be suppress ed and corrosion rate be reduced.However anions in corrosion electrolyte still c an penetrate the FeCO3 crystal and get to the interface between matrix and cor rosion scale,which can lead to formation of pitting.

Key words： CO2 corrosion corrosion scales N80 steel pitting cor rosion

收稿日期: 2002-05-14

ZTFLH:

TG174

通讯作者: 陈长风

Corresponding author: Changfeng Chen

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	陈长风
	路民旭
	赵国仙
44.8K

引用本文:

陈长风; 路民旭; 赵国仙 . 含1%Cr的N80钢CO2腐蚀产物膜特征[J]. 中国腐蚀与防护学报, 2003, 23(6): 330-334 .
Changfeng Chen, Minxv Lu, Guoxian Zhao. CHARACTERISTICS OF CO2 CORROSION SCALES ON 1%Cr-CONTAINING N80 STEEL. J Chin Soc Corr Pro, 2003, 23(6): 330-334 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I6/330

[1]ZhangXY ,DiC ,LeiLC .CO2CorrosionandControl[M ].Beijing:ChemicalIndustryPress,2000(张学元,邸超,雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000)
[2]MasamuraK ,InoharaYA ,MinamiYU .EffectsofCandNoncor rosionresistanceofhighCralloysinCO2 andH2Senvironments[A].Corrosion/98[C].Houston:NACE ,1998,116
[3]CayardMS ,KaneRD .Serviceabilityof13Crtubularsinoilandgasproductionenvironments[A].Corrosion/98[C].Houston:NACE ,1998,112
[4]UedaM ,TakabeH .CorrosionresistanceoflowCrbearingsteelinsourandsweetenvironments[A].Corrosion/2002[C].Houston:NACE ,2002,41
[5]NoseK ,AsahiH ,NicePI ,MartinJ.Corrosionpropertiesof3%Crsteelsinoilandgasenvironments[A].Corrosion/2001[C].Hous ton:NACE ,2001,82
[6]IkedaA ,UedaM ,MukaiS .in:HauslerRH ,GiddardHP(Eds).AdvancesinCO2Corrosion[M ].Vol.1,NACE ,Houston,Texas.1984:39
[7]IkedaA ,UedaM .PredictingCO2CorrosionintheOilandGasIn dustry[M ].London,UK :TheInstituteofMaterials,1994,59-93
[8]ChenCF ,LuMX ,ZhaoGX ,etal.CharactersofCO2 corrosionscalesonN80welltubesteels[J].ActaMetall.Sin.,2002,38(4),411-416(陈长风,路民旭,赵国仙等.N80油套管钢CO2腐蚀产物膜特征[J].金属学报,2002,38(4),411-416)
[9]ChenCF ,ZhaoGX ,YanML ,etal.StudyofCO2 corrosionscalesonN80steel[J].J .Chin.Soc.Corros.Prot.,2002,22(3):143(陈长风,赵国仙,严密林等.N80钢CO2腐蚀产物膜研究[J].中国腐蚀与防护学报,2002,22(3):143)
[10]PalaciosCA ,ShadleyJR .CharacteristicsofcorrosionscalesonsteelsinCO2-saturatedNaClbrine[J].Corrosion,1991,47(2),122-127
[11]ChenCF ,ZhaoGX ,YanML ,etal.CharacteristicsofCO2 corro sionscalesonCr-containingN80steel[J].J .Chin.Soc.Corros.Prot.,2002,22(6):335(陈长风,赵国仙,严密林等.含Cr油套管钢CO2腐蚀产物膜特征[J].中国腐蚀与防护学报,2002,22(6):335)

[1]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[2]	黄博博,刘平,刘新宽,梅品修,陈小红. 新型HSn70-1铜网衣两年期海水腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
[3]	鲍明昱, 任呈强, 胡静思, 刘博, 李佳蒙, 王丰, 刘丽, 郭小阳. 油气管材应力诱导腐蚀电化学行为探讨[J]. 中国腐蚀与防护学报, 2017, 37(6): 504-512.
[4]	韩帅豪,岑宏宇,陈振宇,邱于兵,郭兴蓬. 原油与高压CO₂共存条件下咪唑啉缓蚀剂的作用行为研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 221-226.
[5]	张弟,梁平,张云霞,史艳华,秦华. 库尔勒土壤模拟溶液中形成的腐蚀产物膜对X80钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(4): 313-320.
[6]	董洋洋, 黄峰, 程攀, 胡骞, 刘静. X65 MS耐酸管线钢在H₂S环境中腐蚀产物膜的演变[J]. 中国腐蚀与防护学报, 2015, 35(5): 386-392.
[7]	梁平, 王莹. 覆有短期腐蚀产物膜的X80钢的电化学行为[J]. 中国腐蚀与防护学报, 2013, 33(5): 371-376.
[8]	鲁照玲,郭兴蓬. 月桂酸在CO₂饱和盐水溶液中缓蚀行为和机理研究[J]. 中国腐蚀与防护学报, 2010, 30(6): 475-480.
[9]	俞芳高克玮路民旭. 流动状态下X65管线钢CO₂腐蚀产物膜结构和力学性能的评价[J]. 中国腐蚀与防护学报, 2009, 29(6): 401-404.
[10]	李党国 . 温度对N80钢饱和CO2地层水中腐蚀电化学性能影响[J]. 中国腐蚀与防护学报, 2008, 28(2): 104-107 .
[11]	李桐; 高克玮; 路民旭 . X65钢CO2腐蚀产物膜形成机理研究[J]. 中国腐蚀与防护学报, 2007, 27(6): 338-341 .
[12]	马文海; 裴晓含; 高飞; 高纯良 . N80钢在模拟深层气井水溶液中的CO2腐蚀行为[J]. 中国腐蚀与防护学报, 2007, 27(1): 8-13 .
[13]	赵国仙; 吕祥鸿; 李鹤林; 路民旭 . 温度对P110钢CO2腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2005, 25(2): 93-96 .
[14]	林冠发 . CO2压力对金属腐蚀产物膜形貌结构的影响[J]. 中国腐蚀与防护学报, 2004, 24(5): 284-288 .
[15]	陈长风; 路民旭; 赵国仙 . 腐蚀产物膜覆盖条件下油套管钢CO2腐蚀电化学特征[J]. 中国腐蚀与防护学报, 2003, 23(3): 139-143 .

Viewed

Full text

Abstract

Cited

Shared

Discussed