铝合金剥蚀过程的电化学阻抗谱分析

李劲风;郑子樵;张昭;张鉴清

中南大学材料科学与工程学院

ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY OF Al ALLOYS DURING EXFOLIATION CORROSION

Jinfeng Li;Ziqiao Zheng;Zhao Zhang;Jianqing Zhang

中南大学材料科学与工程学院

全文: PDF(156 KB)

摘要: 研究了轧制态及峰时效8090铝-锂合金、拉应力作用下及无应力作用时双级过时效7075铝合金的剥蚀发展过程，测量并拟合了合金发生剥蚀后的电化学阻抗谱。结果表明：发生剥蚀后，合金电化学阻抗谱由高一中频和中一低频容抗弧组成；可从电化学阻抗谱的拟合参数（变化趋势）得到剥蚀的相关信息，如剥蚀发展速度、剥蚀形貌、剥蚀表层是否脱落等。

关键词 ：铝合金, 剥蚀, 电化学阻抗谱

Abstract：The exfoliation development of 8090 Al - Li alloy and 7050 Al alloy was studied.The electrochemical impedance spectroscopy(EIS) of these alloys in EXCO solution was measured and simulated .At the beginning of immersion, the EIS is comprised by a capacitive arc at high - mediate frequency and an inductive arc at mediate - low frequency. Once exfoliation occurs, two capacitive arcs appear at high - mediate frequency and mediate - low frequency respectively.Some information about exfoliation, such as exfoliation development rate and exfoliation morphology, can be obtained through the simulated EIS data.

Key words： Al alloys electrochemical impedance spectroscopy (EIS) exfoliation corrosion

收稿日期: 2003-07-07

ZTFLH:

TG174.3

通讯作者: 李劲风 E-mail: jfli2000@163.net

Corresponding author: Jinfeng Li E-mail: jfli2000@163.net

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李劲风
	郑子樵
	张昭
	张鉴清
44.8K

引用本文:

李劲风; 郑子樵; 张昭; 张鉴清 . 铝合金剥蚀过程的电化学阻抗谱分析[J]. 中国腐蚀与防护学报, 2005, 25(1): 48-52 .
Jinfeng Li, Ziqiao Zheng, Zhao Zhang, Jianqing Zhang. ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY OF Al ALLOYS DURING EXFOLIATION CORROSION. J Chin Soc Corr Pro, 2005, 25(1): 48-52 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I1/48

[1]KellyDJ ,RobinsonMJ .InfluenceofheattreatmentandgrainshapeonexfoliationcorrosionofAl-Lialloy8090[J].Corrosion,1993,49(10):787～795
[2]HabashiM .BonteE ,GallandJ,etal.Quantitativemeasurementsofthedegreeoftheexfoliationonaluminumalloys[J].Corros.Sci.,1993,35(4):168～183
[3]LiD ,ZuoSZ ,GuoBL .StudyontheexfoliationcorrosionbehaviourofLY12aluminiumalloy[J].JChin.Soc.Corros.Prot.,1995,15(3):203～208(李荻,左尚志,郭宝兰.LY12铝合金的剥蚀行为研究[J].中国腐蚀与防护学报,1995,15(3):203～208)
[4]CondeA ,DamboreneaJde.Evaluationofexfoliationsusceptibilitybymeansoftheelectrochemicalspectroscopy[J].Corros.Sci.,2000,42(8):1363～1377
[5]CondeA ,DamboreneaJde.Electrochemicalmodelingofexfoliationcorrosionbehaviorof8090alloy[J].ElectrochimicaActa,1997,43(8):849～860
[6]LiJF ,ZhangZ ,CaoFH ,etal.StudyonelectrochemicalimpedancefeaturesofAl-LialloysinEXCOsolution[J].ActaMetall.Sin.,2003,39(4):426～430(李劲风,张昭,曹发和等.Al-Li合金在EXCO溶液中腐蚀的电化学阻抗研究[J].金属学报,2003,39(4):426～430)
[7]KeddamM ,KuntzC ,TakenoutiH ,etal.Exfoliationcorrosionofa luminumalloysexaminedbyelectrodeimpedance[J].ElectrochimicaActa,1997,42(1):87～97
[8]CaoCN ,WangJ ,LinHC .EffectofCl- ionontheimpedanceofpassive-film-coveredelectrodes[J].J .Chin.Soc.Corros.Prot.,1989,9(4):261～270(曹楚南,王佳,林海潮.氯离子对钝态金属电极阻抗频谱的影响[J].中国腐蚀与防护学报,1989,9(4):261～270)

[1]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[6]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[7]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[8]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[9]	夏俊捷,牛红志,刘敏,曹华珍,郑国渠,伍廉奎. 基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[10]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[11]	陈高红,胡远森,于美,刘建华,李国爱. 硫酸阳极化对2E12铝合金力学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 579-586.
[12]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[13]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.
[14]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[15]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.

Viewed

Full text

Abstract

Cited

Shared

Discussed