铝电解质对TiB2镀层的渗透

李冰;邱竹贤;李军;徐金富

华东理工大学资源与环境工程学院金属材料工程专业379信箱

PENETRATION OF Al ELECTROLYTE INTO TiB2 COATING

Bing Li;Zhuxian Qiu;Jun Li;Jinfu Xv

华东理工大学资源与环境工程学院金属材料工程专业379信箱

全文: PDF(162 KB)

摘要: 采用盐体系在石墨基体上电沉积制备了TiB2镀层。将TiB2镀层和铝电解阴极碳块和石墨分别作为阴极，考察了Na和电解质对其渗透腐蚀。电解4h后，由酚酞试剂检测表明，Na对TiB2镀层的渗透深度为零，对阴极极炭块的渗透深度为16mm，对石墨的渗透深度为4mm。电子探针的分析结果指出，Na和F元素渗透到石墨基体的量很少，元素Al相对较多，TiB2镀层阻碍了Na的产生并减缓了Na的渗透，但没有改变Na的渗透机理。同时，镀层与基体的结合力良好，Al对TiB2镀层的湿润性良好。

关键词 ： TiB2镀层, 渗透, 钠, 铝电解质

Abstract：TiB2 coating was electrodeposited on graphite substrate from molten salts.The penetration of sodium and electrolyte into the TiB2 coating,cathode block used as cathode of Al electrolysis and graphite was tested.After four-hour electrolysis,the examinations by phenolphthalein reagent indicated that the penetration depth of sodium into TiB2 coating is zero,while into cathode block is 16mm and into graphite is 4mm.The EPM analysis showed that Na and F element penetrate slightly into the TiB2 coating, and Al element penetrates relatively more. TiB2 coating hinders sodium formation and decelerates sodium penetrtion,but the penetration mechanism has not been changed.Meanwhile the TiB2 coating has good coherence with the substrate and is well wetted by aluminum.

Key words： TiB2coating penetration Na electrolysis

收稿日期: 2003-08-01

ZTFLH:

TQ134.11

通讯作者: 李冰 E-mail: drlibing@163.com

Corresponding author: Bing Li E-mail: drlibing@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李冰
	邱竹贤
	李军
	徐金富
44.8K

引用本文:

李冰; 邱竹贤; 李军; 徐金富 . 铝电解质对TiB2镀层的渗透[J]. 中国腐蚀与防护学报, 2005, 25(1): 44-47 .
Bing Li, Zhuxian Qiu, Jun Li, Jinfu Xv. PENETRATION OF Al ELECTROLYTE INTO TiB2 COATING. J Chin Soc Corr Pro, 2005, 25(1): 44-47 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I1/44

[1]LiuYX .Theresearchprogressoftheinertanodeandwettedcath odeofaluminiumelectrolysis[J].LightMetal,2001,5:26-29(刘业翔.铝电解惰性阳极和可湿润阴极的研究进展[J].轻金属,2001,5:26-29)
[2]LiB .Studyonpenetrationofelectrolysisintocathodematerialsofaluminumelectrolysis[D].DoctoralDissertation,NortheastUniver sity,2001(李冰.铝电解质对阴极材料渗透的研究[D].博士学位论文,东北大学,2001)
[3]MakytaM ,DanekV .Electrodepositionoftitaniumdiboridefromfusedsalts[J].JAppliedElectrochemistry,1996,26:319-324
[4]GerhardEtt,ElisabeteJPessine.PulsecurrentplatingofTiB2 inmoltenfluoride[J].ElectrochimicaActa,1999,44:2859-2870
[5]LiB ,ZhouF ,QiuZX .PreparationofTiB2 coatedcathodeofAlelectrolysis[J].J.Mater.Sci.Technol.,2001,17:S171-S173
[6]LiB ,YaoGC ,QiuZX .ElectrodepositionofTiB2 coatingfrommoltenstlats[A].ProceedingsoftheSeventhJapan-ChinaBilater alConferenceonMoltenSaltsChemistryandTechnology[C].Japan,2000,December
[7]LiB ,WangJQ ,GaoBL ,QiuZX .Studyonpenetrationphenomen-onofcathodeblockinaluminumelectrolysis[J].LightMetals,2001,7:37-40(李冰,王俊青,高炳亮,邱竹贤.铝电解阴极碳块渗透现象的研究[J].轻金属,2001,7:37-40)

[1]	闻洋, 熊林, 陈伟, 薛刚, 宋文学. 干湿循环下聚乙烯醇纤维混凝土抗Cl^-渗透性能研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 381-388.
[2]	赖德林,孔纲,车淳山. 硅酸盐封闭对TiO₂转化膜耐蚀性的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 607-614.
[3]	王海媛, 卫英慧, 杜华云, 刘宝胜, 郭春丽, 侯利锋. 绿色缓蚀剂SDDTC对AZ31B镁合金的缓蚀作用及吸附行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 62-67.
[4]	代陈林,李茂东,杨波,乔越,朱志平. 中央空调环保复合型阻垢缓蚀剂的筛选及性能研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 407-414.
[5]	聂亚楠,沈浩,谷坤鹏,王成启. 玻璃钢复合材料耐海水腐蚀性能及抗Cl^-渗透寿命预测[J]. 中国腐蚀与防护学报, 2016, 36(4): 357-362.
[6]	王玉娜, 聂凯斌, 杨冬, 姚隽旸, 董万田, 廖强强. 模拟海水淡化一级反渗透产水中咪唑啉缓蚀剂对20#碳钢的缓蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(5): 407-414.
[7]	吕晨曦, 魏英华, 李京, 孙超. 聚合物改性砂浆中钢筋的电化学行为及聚合物改性混凝土抗Cl^-渗透性[J]. 中国腐蚀与防护学报, 2015, 35(5): 467-473.
[8]	郭望,赵卫民,张体明,杜天海,王勇. 阴极极化和应力耦合作用下X80钢氢渗透行为研究[J]. 中国腐蚀与防护学报, 2015, 35(4): 353-358.
[9]	徐宏妍,第五江涛,刘霞,杨亚琴. ZK60镁合金在卤化钠溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(3): 245-250.
[10]	张体明, 赵卫民, 郭望, 王勇. 阴极保护下X65钢在模拟海水中的氢脆敏感性研究[J]. 中国腐蚀与防护学报, 2014, 34(4): 315-320.
[11]	梁沁沁，曹顺安，尹力，肖丽. Q235钢在海水淡化一级反渗透产水中的腐蚀行为[J]. 中国腐蚀与防护学报, 2012, 32(5): 412-416.
[12]	马方容,李金许,褚武扬,张万灵,杨大可. 搪瓷钢的氢扩散研究[J]. 中国腐蚀与防护学报, 2010, 30(4): 269-272.
[13]	黄彦良朱永艳黄偲迪张杨杨. 海洋结构用钢在海泥中的氢渗透行为[J]. 中国腐蚀与防护学报, 2008, 28(6期): 355-358.
[14]	朱丽琴 . 噻二唑衍生物在3%NaHCO3溶液中对铜的缓蚀作用[J]. 中国腐蚀与防护学报, 2006, 26(2): 125-128 .
[15]	钱建刚; 李荻; 王学力; 郭宝兰 . 硼酸钠浓度对镁合金阳极化的影响[J]. 中国腐蚀与防护学报, 2005, 25(5): 275-279 .

Viewed

Full text

Abstract

Cited

Shared

Discussed