油品腐蚀性阻抗谱检测技术及仪器研究

林国美^1,2,管亮¹,冯新泸¹

1. 后勤工程学院军事油料应用与管理工程系重庆 401311
2. 南京军区联勤部油料监督处南京 210037

A NEW OIL CORROSION DETECTION METHOD AND INSTRUMENT FOR PETROLEUM PRODUCTS BASED ON IMPEDANCE SPECTROSCOPY

LIN Guomei^1,2, GUAN Liang¹, FENG Xinlu¹

1. Department of Military Oil Application and Management Engineering, Logistical Engineering University,Chongqing 401311
2. Nanjing Military Area Joint Logistics Department, Nanjing 210037

全文: PDF(1081 KB)

摘要: 设计了一种金属叉指电容传感器，以腐蚀产物在传感器上沉积对叉指传感器阻抗特性的影响，建立了基于阻抗谱技术的油品腐蚀性能检测技术及仪器。通过对喷气燃料铜片腐蚀试验的应用研究，证明新的检测技术优于目前常规油品腐蚀性能检测方法。

关键词 ：叉指电容传感器, 阻抗谱, 油品腐蚀性能, 铜片腐蚀实验

Abstract：Based on interdigitated comb electrodes capacitor sensor and impedance spectroscopy technology, a new oil corrosion measurement technique as well as the instrument were developed. The new electrode and the associated instrument is applied to copper strip corrosion test (GB/T5096-90) of jet fuel. The results show that the new corrosion detection technology is better than that obtained by conventional oil corrosion measurement.

Key words： interdigitated comb electrode impedance spectroscopy petroleum products corrosiveness copper strip corrosion test

收稿日期: 2010-07-05

ZTFLH:

TE980.2

通讯作者: 管亮 E-mail: gl_200122@163.com

Corresponding author: GUAN Liang E-mail: gl_200122@163.com

作者简介: 林国美，男，1964年生，博士生，研究方向为油料监督技术及管理

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	林国美
	管亮
	冯新泸
44.8K

引用本文:

林国美,管亮,冯新泸. 油品腐蚀性阻抗谱检测技术及仪器研究[J]. 中国腐蚀与防护学报, 2011, 31(4): 299-304.
LIN Guo-Mei, GUAN Liang, FENG Xin-Lu. A NEW OIL CORROSION DETECTION METHOD AND INSTRUMENT FOR PETROLEUM PRODUCTS BASED ON IMPEDANCE SPECTROSCOPY. J Chin Soc Corr Pro, 2011, 31(4): 299-304.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I4/299

[1] Zuo H J, Jin W F. Application of online cortest instrument MS3500E [J]. Corros.Prot., 2000, 21(12): 556-557

    (左慧君, 金文房. 电阻探针MS3500E在线腐蚀监测应用 [J]. 腐蚀与防护. 2000, 21(12): 556-557)

[2] Yuan J G. Application of corrosion monitoring technologies in Zhenhai Refining & Chemical Co., Ltd [J]. Petrochem.Corros. Prot., 2002, 19(6): 49-53

    (袁军国. 腐蚀监测技术在镇海炼化公司的应用 [J]. 石油化工腐蚀与防护, 2002, 19(6): 49-53)

[3] Zheng L Q, Zhang W, Tai C, et al. Development and application of resistance probe and testing instrument for high-temperature corrosion monitoring [J]. Petrochem. Corros.Prot., 2002, 19(5): 50-53

    (郑立群, 张蔚, 台闯等. 高温腐蚀监测电阻探针和测试仪的研制及应用 [J]. 石油化工腐蚀与防护, 2002, 19(5): 50-53)

[4] Li Y X, Bi Y J. Development of anti-high temperature resistance prode [J]. Shengli Refinery Sci. Technol., 2003, 25(2): 31-35

    (李延祥, 毕延进. 耐温电阻探针的研制开发 [J]. 胜炼科技, 2003, 25(2): 31-35)

[5] Liang Z S, Xia Y S, Cui J X. Application of on-line corrosion monitoring in refinery process units [J]. Corros. Prot. Petrochem. Ind.,2003, 20(4): 51-55

    (梁自生, 夏延燊, 崔金喜. 在线腐蚀监测技术在炼油装置上的应用研究 [J]. 石油化工腐蚀与防护, 2003, 20(4): 51-55)

[6] Wang Q J, Wang D H. Application of electro-resistance probe in monitoring the corrosion of overhead system [J]. Corros. Prot. Petrochem. Ind.,2003, 20(5): 41-44

    (王庆军, 王德会. 电阻探针式腐蚀监测仪在塔顶系统的应用 [J]. 石油化工腐蚀与防护, 2003, 20(5): 41-44)

[7] Zeng Y H. Application of corrosion monitoring technology in refinery process units [J].Corros. Prot. Petrochem. Ind.,2005, 22(1): 56-59

    (曾彦华. 腐蚀监测技术在炼油装置上的应用 [J]. 石油化工腐蚀与防护, 2005, 22(1): 56-59)

[8] Zheng L Q. Lastest development of corrosion monitoring techniques in petrochemical industry [J].Corros. Prot. Petrochem. Ind., 2005, 22(1): 11-15

    (郑立群. 石油化工工业腐蚀监测技术的最新发展 [J]. 石油化工腐蚀与防护, 2005, 22(1): 11-15)

[9] Ao M, Xu D D, Bi W J, et al. Detection to corrosion of oil instruments and pipes with resistance probe [J]. Liaoning Chem. Ind.,2007, 36(2): 126-127

    (敖曼, 徐冬东, 毕文军等. 利用电阻探针对石油设备及管道的腐蚀进行监测 [J]. 辽宁石化, 2007, 36(2): 126-127)

[10] Bai R L, Dong Z H, Guo X P, et al. Study on principle of electrical resistance probe based on temperature compensation for corrosion monitoring [J].Corros. Sci. Prot. Technol., 2007, 19(5): 338-341

     (柏任流, 董泽华, 郭兴蓬等. 基于温度补偿的电阻探针腐蚀监测原理的研究 [J]. 腐蚀科学与防护技术, 2007, 19(5): 338-341)

[11] Bai R L, Zhou J. Exploitation and application of corrosion monitoring portable instrument [J].J. Qianan Norm. Coll. Nation., 2007, (3): 15-18

     (柏任流, 周静. 电阻探针腐蚀监测仪的开发与应用 [J]. 黔南民族师范学院学报, 2007, (3): 15-18)

[12] Cui J X. Applying inductive probe at atemospheric and vacuum distillation unit [J]. Guang Petrochem.Sci. Technol., 2007, (2): 30-32

     (崔金喜. 电感探针在常减压蒸馏装置的应用 [J]. 广石化科技, 2007, (2): 30-32)

[13] Hu Z X, Yang G H, Wang L G, et al. Exploration on mechanism of silver strip corrosion in jet fuel and accelerated testing method [J]. Corros.Prot., 1999, 20(2): 87-88, 72

     (胡泽祥, 杨官汉, 王立光等. 喷气燃料银片腐蚀机理及快速试验方法探讨 [J]. 腐蚀与防护, 1999, 20(2): 87-88, 72)

[14] Wang L G, He T, Zhang Q. An accelerated testing method for silver strip corrosion in jet fuels [J].Corros. Prot., 2000, 21(5): 223-225

     (王立光, 何滔, 张祁. 喷气燃料银片腐蚀快速测定方法的研究 [J]. 腐蚀与防护, 2000, 21(5): 223-225)

[15] Liu L, Zhai Y C, Qian J H, et al. Study on rapid corrosion test method for jet fuel [J].Petro. Process. Petrochem., 2001, 32(4): 49-51

     (刘琳, 翟玉春, 钱建华等. 喷气燃料银片腐蚀快速试验法的研究 [J]. 石油炼制与化工, 2001, 32(4): 49-51)

[16] An X C, Li D G. Fast determination of semiquantitative of element sulfur in tank bottom oil of oil-truch [J].Chem. Eng., 2007, 140(5): 21-23

     (安晓春, 李大光. 油罐车残存油中元素硫的半定量快速测定方法 [J]. 化学工程师, 2007, 140(5): 21-23)

[17] Chen F, Zhang T, Xu T G. Improvement on the evaluation of copper corrosion by petroleum products in copper strip test [J]. Corros. Prot.,2000, 21(11): 521-522

     (陈峰, 张涛, 徐同刚. 石油产品铜片腐蚀试验结果判断方法的改进初见 [J]. 腐蚀与防护, 2000, 21(11): 521-522)

[18] Liu X Y, Xu L H, Zhong Y L, et al. Method of digital image processing for evaluation copper corrosion test result [J]. J. Logistical Eng. Univ., 2004, (3): 34-37

     (刘信阳, 胥立红, 钟远利等. 铜片腐蚀试验结果评价的数字图像处理方法 [J]. 后勤工程学院学报, 2004, (3): 34-37)

[1]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[2]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[3]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[4]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[5]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[6]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[7]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[8]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[9]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[10]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[11]	孟凡帝, 刘莉, 李瑛, 王福会. 用于原位检测在深海并压力交变环境中有机涂层电化学阻抗的预埋微电极研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.
[12]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[13]	王佳, 贾梦洋, 杨朝晖, 韩冰. 腐蚀电化学阻抗谱等效电路解析完备性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.
[14]	陈振宁,陈日辉,潘金杰,滕艳娜,雍兴跃. L921A钢在3.5%NaCl溶液中的有机/无机复配缓蚀剂研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.
[15]	陈亚林, 张伟, 王琦, 王佳. WBE技术研究水线区破损涂层的剥离机制-II[J]. 中国腐蚀与防护学报, 2017, 37(4): 322-328.

Viewed

Full text

Abstract

Cited

Shared

Discussed