电弧喷涂铝涂层的腐蚀电化学行为

刘存,赵卫民,艾华,王勇,董立先

中国石油大学（华东）机电工程学院东营 257061

ELECTROCHEMICAL CORROSION BEHAVIORS OF ARC-SPRAYED ALUMINUM COATING

LIU Cun, ZHAO Weimin, AI Hua, WANG Yong, DONG Lixian

School of Mechanical and Electrical Engineering, China University of Petroleum, Dongying 257061

全文: PDF(1139 KB)

摘要: 用电弧喷涂方法在钢表面制备铝涂层，研究其在3.5% NaCl溶液中的电化学腐蚀行为。采用电子探针技术（EPMA）分析研究浸泡30 d后涂层横截面的成分分布特征，发现腐蚀介质可沿孔隙或夹杂物向涂层内部渗入，且已有部分Cl^-渗达涂层深处。动电位极化实验结果显示，原始铝涂层具有明显的钝化现象，这与胶冻状腐蚀产物Al(OH)₃的附着力较强以及Al₂O₃膜的形成有关。电化学阻抗谱(EIS)测试结果表明，铝涂层在测试期内的EIS 图谱变化可分成4个阶段：孔蚀萌生阶段、孔内酸化析氢阶段、介质渗达钢基体后涂层作为牺牲阳极的阶段和孔蚀群急剧发展阶段。提出电极在腐蚀过程中的不同阻抗模型。

关键词 ：电化学阻抗谱, 电弧喷涂, 金属涂层, 铝涂层

Abstract：Aluminum was deposited on steel using arc spraying, and the corrosion electrochemical behavior of the coatings in 3.5% NaCl aqueous solution was investigated. The electron probe micro-analysis (EPMA) was used to examine composition profiles of the coating cross section after 30 day immersion. The results showed that the corrosion medium could penetrate into the coatings along the pores or inclusions, and chloride ions have penetrated into the depth of the coatings. The potentiodynamic polarization curves showed the passivation phenomenon of the original aluminum coating, which was related to the strong adhesion of jelly corrosion product Al(OH)₃ and the existence of Al₂O₃ films. The corrosion failure process of aluminum coating was investigated by means of electrochemical impedance spectroscopy (EIS) measurements. On the basis of the impedance diagram changes during the testing, the process can be separated into four stages: initiation of cavitations, acidification and hydrogen evolution in the hole, coating as the sacrificial anode when the corrosion medium penetrates into steel substrate and rapid development of cavitation groups. Finally various models for the electrode in the corrosion process were proposed.

Key words： electrochemical impedance spectroscopy arc spraying metal coating, aluminum coating

收稿日期: 2009-11-25

ZTFLH:

TG174

基金资助:

国家高技术研究发展(863)计划海洋技术领域项目(2008AA09A106)和山东省科技攻关项目(2007GG30004008)资助

通讯作者: 赵卫民 E-mail: zhaowm@hdpu.edu.cn

Corresponding author: ZHAO Weimin E-mail: zhaowm@hdpu.edu.cn

作者简介: 刘存，男，1982年生，硕士生，研究方向为材料失效与表面改性

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘存
	赵卫民
44.8K

引用本文:

刘存,赵卫民,艾华,王勇,董立先. 电弧喷涂铝涂层的腐蚀电化学行为[J]. 中国腐蚀与防护学报, 2011, 31(1): 62-67.
LIU Cun, DIAO Wei-Min. ELECTROCHEMICAL CORROSION BEHAVIORS OF ARC-SPRAYED ALUMINUM COATING. J Chin Soc Corr Pro, 2011, 31(1): 62-67.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I1/62

[1] Xu B S, Li C J, Liu S S,et al. Surface engineering an thermal spraying technology and their developments [J]. Chin. Surf.Eng., 1998, 38(1): 3-10

    (徐滨士, 李长久, 刘世参等. 表面工程与热喷涂技术及其发展 [J]. 中国表面工程, 1998, 38(1): 3-10)

[2] Li J G, Zheng J S. Surface Engineering Technology and Corrosion Inhibitors [M]. Beijing: China Petrochemical Press, 2007

    (李金桂, 郑家燊. 表面工程技术和缓蚀剂 [M]. 北京: 中国石化出版社, 2007)

[3] Xiao W G. Application of electric arc thermal spraying technique with wire material to anticorrosion of offshore steel structures in Shengli oilfield [J]. Pet. Eng.Constr., 2004, 30(3): 33-34

    (肖文功. 线材电弧喷涂技术在浅海钢结构防腐中的应用 [J]. 石油工程建设, 2004, 30(3): 33-34)

[4] Fischer K P, Thomason W H. Performance history of thermal-sprayed aluminum coatings in offshore service [J]. Mater Perform., 1995, 34(4): 27-35

[5] Yin Y S, Huang X, Dong L H. Marine Engineering Materials [M]. Beijing: Science Press, 2008

    (尹衍生, 黄翔, 董丽华. 海洋工程材料学 [M]. 北京: 科学出版社, 2008)

[6] Meroufel A, Touzain S. EIS characterization of new zinc-rich powder coatings [J]. Prog. Org. Coat., 2007, 59(3): 197-205

[7] O'Donoghue M, Garrett R, Datta V, et al. Electrochemical impedance spectroscopy: Testing coatings for rapid immersion service [J].Mater. Perform., 2003, 42(9): 36-41

[8] Marchebois H, Keddam M, Savall C, et al. Zinc-rich powder coatings characterization in artificial sea water EIS analysis of the galvanic action [J]. Electrochim. Acta, 2004, 49(11): 1719-1729

[9] Popa M V, Drob P, Vasilescu E, et al. Electrochemical characterization of electrodeposited organic coatings [J]. Mater. Corros., 2002, 53(2): 91-97

[10] He J, Yan R, Ma S N. Study on corrosion behaviors of epoxy coatings/substrate immersed in 3.5% NaCl solution by electrochemical methods [J]. China. Surf. Eng., 2006, 19(2): 47-50

     (何杰, 阎瑞, 马世宁. 电化学方法研究环氧涂层/基体在3.5% NaCl溶液中的腐蚀行为 [J]. 中国表面工程, 2006, 19(2): 47-50)

[11] Sami M. Electrochemical impedance spectroscopy of epoxy-coated steel exposed to dead sea water [J]. J. Miner. Mater. Charact. Eng.,2005, 4(2): 75-84

[12] Abreu C M, Cristobal M J, Losada R, et al. High frequency impedance spectroscopy study of passive films formed on AISI 316 stainless steel in alkaline medium [J]. J. Electroanal.Chem., 2004, 572(2): 335-345

[13] El-Mahdy G A, Nishikata A, Tsuru T. AC impedance study on corrosion of 55%Al-Zn alloy-coated steel under thin electrolyte layers [J].Corros. Sci., 2000, 42(9): 1509-1521

[14] Shibli S M A, George S.Electrochemical impedance spectroscopic analysis of activation of Al-Zn alloy sacrificial anode by RuO₂ catalytic coating [J]. Appl.Surf. Sci., 2007, 253(18): 7510-7515

[15] GB/T 9793-1997, Metallic and other inorganic coatings-thermal spraying-zinc, aluminium and their alloys [S].

     (GB/T 9793-1997, 金属和其他无机覆盖层热喷涂锌、铝及其合金 [S].)

[16] Yang Z H, Xu N,Qiu Z X. Measurement of aluminium of corrosive potential-pH and the polarization curve [J]. J. Northeast. Univ. (Nat.Sci.), 2000, 21(4): 401-403

     (杨振海, 徐宁, 邱竹贤. 铝的电位-pH图及铝腐蚀曲线的测定 [J]. 东北大学学报（自然科学版）, 2000, 21(4): 401-403)

[17] Hou B R, Marine Corrosive Environment Theory and Application [M]. Beijing: Science Press, 1999

     (侯保荣. 海洋腐蚀环境理论及其应用 [M]. 北京: 科学出版社, 1999)

[18] Creus J, Mazille H, Edrissi H. Porosity evaluation of protective coatings onto steel, through electrochemical techniques [J]. Surf. Coat Technol., 2000, 130(2-3): 224-232

[1]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[2]	余春堂,阳颖飞,鲍泽斌,朱圣龙. 先进高温热障涂层用高性能粘接层制备及研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 395-403.
[3]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[4]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[5]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[6]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[7]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[8]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[9]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[10]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[11]	孟凡帝, 刘莉, 李瑛, 王福会. 用于原位检测在深海并压力交变环境中有机涂层电化学阻抗的预埋微电极研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.
[12]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[13]	王佳, 贾梦洋, 杨朝晖, 韩冰. 腐蚀电化学阻抗谱等效电路解析完备性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.
[14]	陈振宁,陈日辉,潘金杰,滕艳娜,雍兴跃. L921A钢在3.5%NaCl溶液中的有机/无机复配缓蚀剂研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.
[15]	冯立, 张立功, 李思振, 郑大江, 林昌健, 董士刚. 柠檬酸铁浓度对镁合金微弧氧化黑色膜层微观结构及耐蚀性的影响[J]. 中国腐蚀与防护学报, 2017, 37(4): 360-365.

Viewed

Full text

Abstract

Cited

Shared

Discussed