磁场对铁腐蚀过程中阴极析氢和阳极溶解的影响

王晨;陈俊明

中国科学院上海冶金研究所

THE EFFECT OF STRONG MAGNETIC FIELD ON CORROSION BEHAVIOR OF IRON

Wang Chen; Chen Junming(Shanghai Institute of Metallurpy; Chinese Academy of Sciences)

全文: PDF(482 KB)

摘要: 用动电位扫描法研究了０．５Ｔ磁场下纯铁在三种典型介质中的阴极极化曲线和两种介质中的阳极极化曲线．发现磁场会引起一个新的过电位一磁致过电位ｍａｇ，使铁上阴极析氢和铁的阳极溶解有不同程度的加速，尤以在酸性介质中为甚．认为这是由于磁场使铁－水溶液界面抗磁性离子的水合作用减少和使Ｆｅ２＋有吸附于铁电极表面的倾向，导致双电层结构的改变和腐蚀体系的活性增加．

关键词 ：磁场, 铁的阳极溶解, 阴极过程, 磁致过电位

Abstract：Cathodic process of iron in three typical solutions and anodic process of iron in two typical solutions were studied in the presence of magnetic field of 0.5T (tesla) at 23 ℃ Polarization curves for hydrogen evolution and iron dissolution during magnetization were measured. The experimental results indicate that both hydrogen evolution and iron dissolution were more or less accelerated by additional magnetic overpotential-- △φmag and the phenomenon is more evident in acidic solution. This could be attributed to the reduction of diamagnetic ion hydrate on the iron/solution interface and the adsorption of Fe2+ on the iron surface, which are responsible for the change of electric double layer structure and the increase of activity in the corrosion system.

Key words： Magnetic field anodic process of iron catholic processt magnetic overpotential

收稿日期: 1994-04-25

基金资助:国家自然科学基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王晨
	陈俊明
44.8K

引用本文:

王晨;陈俊明. 磁场对铁腐蚀过程中阴极析氢和阳极溶解的影响[J]. 中国腐蚀与防护学报, 1994, 14(2): 123-128.
. THE EFFECT OF STRONG MAGNETIC FIELD ON CORROSION BEHAVIOR OF IRON. J Chin Soc Corr Pro, 1994, 14(2): 123-128.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1994/V14/I2/123

1AtkinsPeter．Chem．Br,1976,12(7):2142DonaldsonJD．ProductFinishing,1986,(9):63BuschKW,BuxdhMA,ParkerDH,etal．Corrosion,1986,42(4):2114ChibaA,HosokawaA,OgawaT．Suat．Technal．,1986,27(2):1315QuraishiMS,FahidyTZ,AbdoMSE．Electrochim．Acta．1982,27(8):9956CousinsCA,DashJ,GoraC．J．Appl．Phys,1984,55(6):26067王晨,陈俊明．腐蚀与防护,1991,12(4):1658GhabashyME,SedahmedGH,MansourJAS．Br．Corros．J,1982,1(7):369GhabashyMA．Anti-Corrosion,1988,35(1):1210托马晓夫著,陈俊明译．氧退极化引起的金属腐蚀,北京:科学出版社,1959,P8211MansfeldFlorian．CorrosionMechanisms,NewYork:MarcelDekkerInc,1986,P412JelinekJ,NeufeldP．CorrosionScience,1980,20:48913克拉辛BN著,王鲁译．水系统的磁处理,北京:宇航出版社,1988;P2914SrivastavaK,NigamN．Br．Corros．J,1988,23(3):172

[1]	卫晓阳,杨丽景,吕战鹏,郑必长,宋振纶. 磁场对纯Cu微生物腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 484-494.
[2]	张康南,吴明,谢飞,王丹,伞宇曦,江峰. 磁场对X80管线钢在沈阳草甸土中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 148-154.
[3]	吕亚林,郑碧娟,刘宏伟,熊福平,刘宏芳,胡裕龙. 磁场对硫酸盐还原菌生物膜在304不锈钢表面吸附性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 652-658.
[4]	陈碧, 郑碧娟, 张帆, 刘宏芳. 静磁场下硫酸盐还原菌对HSn70-1铜合金的腐蚀行为[J]. 中国腐蚀与防护学报, 2014, 34(4): 339-345.
[5]	李克娟, 郑碧娟, 陈碧, 刘宏芳. 磁场对Q235钢微生物腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2013, 33(6): 463-469.
[6]	李健张涛孟国哲邵亚薇王福会. 用随机分析方法研究磁场对纯镁点蚀过程的影响机理[J]. 中国腐蚀与防护学报, 2009, 29(6): 405-410.
[7]	吕战鹏; 杨武; 黄德伦 . 磁场对铜在含三价铁离子硫酸溶液中的腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2001, 21(3): 129-136 .
[8]	吕战鹏; 黄德伦; 杨武 . 重铬酸根与磁场对铁在硫酸溶液中阳极极化行为的影响*[J]. 中国腐蚀与防护学报, 2001, 21(1): 1-9 .
[9]	吕战鹏; 黄德伦; 杨武 . 含重铬酸根硫酸溶液中磁场对铁自腐蚀状态及极化电阻的影响[J]. 中国腐蚀与防护学报, 2000, 20(4): 230-236 .
[10]	陈俊明;吕战鹏. 磁场和杂质离子存在下Fe/Na_2SO_4体系的阳极极化行为[J]. 中国腐蚀与防护学报, 1998, 18(2): 119-125.
[11]	王超;雷圣宾;陈慎豪;于锡玲. 磁场和Cl~-作用下硫酸溶液中铁的恒电位电流振荡[J]. 中国腐蚀与防护学报, 1998, 18(1): 27-34.
[12]	陈俊明;吕战鹏. 磁场对铁极化行为影响的瞬时效应和记忆效应[J]. 中国腐蚀与防护学报, 1997, 17(4): 276-280.
[13]	陈俊明;吕战鹏. 磁场和缓蚀剂对Fe/0.5mol·L~(-1)H_2SO_4等体系极化行为的影响[J]. 中国腐蚀与防护学报, 1997, 17(3): 195-202.
[14]	吕战鹏;陈俊明. 有无外磁场下铁在H_2SO_4+K_2Cr_2O_7溶液中的电化学状态和阴极极化行为[J]. 中国腐蚀与防护学报, 1997, 17(3): 203-209.
[15]	陈俊明;吕战鹏. 有、无磁场下缓蚀剂对Fe/0.05mol· L~(-1)HCl极化行为的影响[J]. 中国腐蚀与防护学报, 1997, 17(2): 135-141.

Viewed

Full text

Abstract

Cited

Shared

Discussed