| 晶粒尺寸对耐热钢在高温水蒸汽中的氧化行为的影响 |
| 袁军涛1 吴细毛2 王 文1 朱圣龙1 王福会1 |
1. 中国科学院金属研究所 金属腐蚀与防护国家重点实验室 沈阳 110016
2. 东北电力科学研究院有限公司 沈阳 110006 |
|
| Effect of Grain Size on Oxidation of Heat-resistant Steels in High Temperature Water Steam |
| YUAN Juntao1, WU Ximao2, WANG Wen1, ZHU Shenglong1, WANG Fuhui1 |
1. State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016,China;
2. Northeast Electric Power Research Institute Co. Ltd., Shenyang 110006, China |
引用本文:
袁军涛, 吴细毛, 王文, 朱圣龙, 王福会. 晶粒尺寸对耐热钢在高温水蒸汽中的氧化行为的影响[J]. 中国腐蚀与防护学报, 2013, 33(4): 257-264.
YUAN Juntao,
WU Ximao,
WANG Wen,
ZHU Shenglong,
WANG Fuhui.
Effect of Grain Size on Oxidation of Heat-resistant Steels in High Temperature Water Steam. Journal of Chinese Society for Corrosion and protection, 2013, 33(4): 257-264.
链接本文:
https://www.jcscp.org/CN/
或
https://www.jcscp.org/CN/Y2013/V33/I4/257
|
[1] Wright I G, Dooley R B. A review of the oxidation behaviour of structural alloys in steam [J]. Int. Mater. Rev., 2010, 55(3): 129-167
[2] Viswanathan R, Sarver J, Tanzosh J M. Boiler materials for ultra-supercritical coal power plants-steamside oxidation [J]. J. Mater. Eng. Perform., 2006, 15(3): 255-274
[3] Asteman H, Svensson J E, Johansson L G, et al. Indication of chromium oxide hydroxide evaporation during oxidation of 304L at 873 K in the presence of 10% water vapor [J]. Oxid. Met., 1999, 52(1/2): 95-211
[4] Asteman H, Svensson J E, Norell M, et al. Influence of water vapor and flow rate on the high-temperature oxidation of 304L: Effect of chromium oxide hydroxide evaporation [J]. Oxid. Met., 2000, 54(1/2): 11-26
[5] Asteman H, Svensson J E, Johansson L G. Evidence for chromium evaporation influencing the oxidation of 304L: The effect of temperature and flow rate [J]. Oxid. Met., 2002, 57(3/4): 193-216
[6] Asteman H, Svensson J E, Johansson L G. Oxidation of 310 steel in H2O-O2 mixtures at 600 oC: the effect of water-vapour-enhanced chromium evaporation [J]. Corros. Sci., 2002, 44(11): 2635-2649
[7] Young D J, Pint B A. Chromium volatilization rates from Cr2O3 scales into flowing gases containing water vapor [J]. Oxid. Met., 2006, 66(3/4): 137-153
[8] Holt A, Kofstad P. Electrical conductivity and defect structure of Cr2O3. II. Reduced temperatures (below 1000 oC) [J]. Solid State Ionics, 1994, 69(2): 137-143
[9] Norby T, Larring Y. Concentration and transport of protons in oxides [J]. Curr. Opin. Solid State Mater. Sci., 1997, 2(5): 593-599
[10] Shen J, Zhou L, Li T. High-temperature oxidation of Fe-Cr alloys in wet oxygen [J]. Oxid. Met., 1997, 48(3/4): 347-356
[11] Hansson A N, Danielsen H, Grumsen F B, et al. Microstructural investigation of the oxide formed on TP 347H FG during long-term steam oxidation [J]. Mater. Corros., 2010, 61(8): 665-675
[12] Jianmin J, Montgomery M, Larsen O H, et al. Investigation on steam oxidation behaviour of TP347H FG Part 1: Exposure at 256 bar [J]. Mater. Corros., 2005, 56(7): 459-467
[13] Jianmin J, Montgomery M, Larsen O H, et al. Investigation of steam oxidation behaviour of TP347H FG. Part 2: Exposure at 91 bar [J]. Mater. Corros., 2005, 56(8): 542-549
[14] Li X G, He J W. Observation of the effect of shot blasted on steam oxidation resistance of TP304H steel boiler tubing [J]. J. Chin. Soc. Corros. Prot., 2003, 23(3): 171-174
(李辛庚, 何家文. 喷丸处理提高TP304H耐热钢锅炉管抗水蒸汽氧化性能应用效果的观察[J]. 中国腐蚀与防护学报, 2003, 23(3): 171-174)
[15] Essuman E, Meier G H, Zurek J, et al. Enhanced internal oxidation as trigger for breakaway oxidation of Fe-Cr alloys in gases containing water vapor [J]. Scr. Mater., 2007, 57(9): 845-848
[16] Sanchez L, Hierro M P, Perez F J. Effect of chromium content on the oxidation behaviour of ferritic steels for applications in steam atmospheres at high temperatures [J]. Oxid. Met., 2009, 71(3/4): 173-186
[17] Peraldi R, Pint B A. Effect of Cr and Ni contents on the oxidation behavior of ferritic and austenitic model alloys in air with water vapor [J]. Oxid. Met., 2004, 61(5/6): 463-483
[18] Laverde D, Gomez-Acebo T, Castro F. Continuous and cyclic oxidation of T91 ferritic steel under steam [J]. Corros. Sci., 2004, 46(3): 613-631
[19] Zurek J, Wessel E, Niewolak L, et al. Anomalous temperature dependence of oxidation kinetics during steam oxidation of ferritic steels in the temperature range 550–650 °C [J]. Corros. Sci., 2004, 46(9): 2301-2317
[20] Angell M G, Lister S K, Rudge A. The effect of steam pressure on the oxidation behaviour of annealed 9Cr 1Mo boiler tubing materials [A]. ICPWS XV [C]. Berlin, 2008
[21] Li X, He J. Effect of shot blasting on oxidation behavior of TP304H steel at 610~770 ℃ in water vapor [J]. Mater. Lett., 2006, 60(3): 339-344
[22] Naraparaju R, Trindade V B, Christ H J, et al. Effect of shot peening on high temperature oxidation behaviour of boiler steel-experimental results and simulation [J]. Corros. Eng. Sci. Technol., 2009, 44(3): 211-217
[24] Naraparaju R, Christ H J, Renner F U, et al. Effect of shot-peening on the oxidation behaviour of boiler steels [J]. Oxid. Met., 2011, 76(3/4): 233-245
[24] Yue Z, Fu M, Wang X, et al. Effect of shot peening on the oxidation resistance of TP304H and HR3C steels in water vapor [J]. Oxid. Met., 2012, 77(1/2): 17-26
[25] Yuan J, Wu X, Wang W, et al. The effect of surface finish on the scaling behavior of stainless steel in water steam and supercritical water [J]. Oxid. Met., 2013, 79(5/6): 541-551
[26] Yue Z, Fu M, Li X, et al. Effect of shot peening treatment on steam oxidation resistance of TP304H reheater tube [J]. J. Chin. Soc. Corros. Prot., 2012, 32(2): 137-140
(岳增武, 傅敏, 李辛庚等. 内壁喷丸处理对TP304H耐热钢锅炉管抗水蒸汽氧化性能的影响 [J]. 中国腐蚀与防护学报, 2012, 32(2): 137-140)
[27] Peng X, Yan J, Zhou Y, et al. Effect of grain refinement on the resistance of 304 stainless steel to breakaway oxidation in wet air [J]. Acta Mater., 2005, 53(19): 5079-5088
[28] Halvarsson M, Tang J E, Asteman H, et al. Microstructural investigation of the breakdown of the protective oxide scale on 304 steel in the presence of oxygen and water vapour at 600 oC [J]. Corros. Sci., 2006, 48(8): 2014-2035
[29] Hansson A N, Pantleon K, Grumsen F B, et al. Microstructure evolution during steam oxidation of a Nb stabilized austenitic stainless steel [J]. Oxid. Met., 2010, 73(1/2): 289-309
[30] Huang Z, Peng X, Xu C, et al. Effect of alloy nanocrystallization and Cr distribution on the development of a chromia scale [J]. J. Electrochem. Soc., 2009, 156(3): C95-C102
[31] Wang F. The effect of nanocrystallization on the selective oxidation and adhesion of Al2O3 scales [J]. Oxid. Met., 1997, 48(3/4): 215-224
[32] Liu Z, Gao W, Dahm K, et al. The effect of coating grain size on the selective oxidation behaviour of Ni-Cr-Al alloy [J]. Scr. Mater., 1997, 37(10): 1551-1558
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|