2205双相不锈钢与316L奥氏体不锈钢钝化膜内点缺陷扩散系数的计算分析

刘佐嘉¹,程学群¹,刘小辉²,李晓刚¹

1. 北京科技大学腐蚀与防护中心北京 100083
2. 中国石油化工股份有限公司青岛安全工程研究院青岛 266071

CALCULATION AND ANALYSIS OF DIFFUSIVITY OF POINT DEFECTS IN PASSIVE FILM FORMED ON 2205 DUPLEX STAINLESS STEEL AND 316L AUSTENITIC STAINLESS STEEL

LIU Zuojia¹, CHENG Xuequn¹, LIU Xiaohui², LI Xiaogang¹

1. Corrosion and Protection Centre, University of Science and Technology Beijing, Beijing 100083
2. Safety & Engineering Academy of SINOPEC, Qingdao 266071

全文: PDF(1642 KB)

摘要:

应用电容测试法并借助于点缺陷模型（PDM）计算了2205双相不锈钢与316L 奥氏体不锈钢在NaCl溶液中所形成的钝化膜内点缺陷的扩散系数，利用实验测得钝化膜的稳态电流和PDM模型对计算结果进行了验证分析。通过两种计算方法得到点缺陷在2205双相不锈钢与316L奥氏体不锈钢钝化膜内的扩散系数约为10^-23cm²/s~10^-20 cm²/s数量级，并发现在模拟海水溶液中2205钢的扩散系数比316L钢小，氧空位所形成的点缺陷在2205钢的钝化膜内比316L钢扩散困难，从而使得2205不锈钢的钝化膜比316L不锈钢更加致密与完整，保护性能更好。

关键词 ：扩散系数, 点缺陷模型, 钝化膜, 电容测试法, 稳态电流密度

Abstract：

The diffusivity of point defects in the passive film formed on 2205 duplex stainless steel and 316L stainless steel in NaCl solution was calculated by means of capacitance measurement and PDM (point defect model). The calculated result was testified and analyzed by experimental steady current density of passive film and PDM. It is showed that the order of magnitude of diffusivity is about 10^-23 cm²/s~10^-20 cm²/s, and the diffusivity of 2205 DSS is less than 316L SS in simulated ocean solution. It is concluded that the diffusion of point defect which is caused by oxygen vacancy in 2205 DSS is harder than 316L SS, so in contrast to 316L SS, the passive film of 2205 DSS is much densified and compact with completeness and excellent protection.

Key words： diffusivity point defect model passive film capacitance measurement steady current density

收稿日期: 2009-06-29

ZTFLH:

TG142.71

基金资助:

国家自然科学基金项目（50871020）资助

通讯作者: 刘佐嘉 E-mail: lzandj@yahoo.com.cn

Corresponding author: Liu Zuojia E-mail: lzandj@yahoo.com.cn

作者简介: 刘佐嘉，男，1985年生，硕士生，研究方向为金属腐蚀与防护

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘佐嘉
	程学群
	李晓刚
	刘小辉
44.8K

引用本文:

刘佐嘉,程学群,刘小辉,李晓刚. 2205双相不锈钢与316L奥氏体不锈钢钝化膜内点缺陷扩散系数的计算分析[J]. 中国腐蚀与防护学报, 2010, 30(4): 273-277.
LIU Zuo-Jia, CHENG Hua-Qun, LI Xiao-Gang, LIU Xiao-Hui. CALCULATION AND ANALYSIS OF DIFFUSIVITY OF POINT DEFECTS IN PASSIVE FILM FORMED ON 2205 DUPLEX STAINLESS STEEL AND 316L AUSTENITIC STAINLESS STEEL. J Chin Soc Corr Pro, 2010, 30(4): 273-277.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2010/V30/I4/273

[1] Zeng R C, Han E H. Corrosion and Protection of Materials [M].Beijing: Chemical Industry Press, 2006: 144\par} (曾荣昌，韩恩厚．材料的腐蚀与防护 [M]．北京：化学工业出版社，2006: 144) [2] Zeng Y M，Luo J L．Electronic band structure of passive film on X70 pipeline steel [J]．Electrochim. Acta, 2003, 48: 3551-3562 [3] Sikora E, Macdonald D D. Nature of the passive film on nickel [J]. Electrochim. Acta, 2002, 48(1): 69-77 [4] Li D G, Feng Y R, Bai Z Q, et al. Calculation of diffusivity of point defects in passive film formed on X80 pipeline steel [J]. Chin. J. Appl.Chem., 2008, 25(9): 1007-1010 (李党国，冯耀荣，白真权等．X80管线钢钝化膜内点缺陷扩散系数的计算 [J]．应用化学, 2008, 25(9): 1007-1010) [5] Elzbieta S, Janusz S, MacDonald D D．A new method for estimating the diffusivities of vacancies in passive film [J]．Electrochim. Acta，1996，41(6)：783-789 [6] Cheng Y F，Yang C，Luo J L．Determination of the diffusivities of point defects in passive films on carbon steel [J]．Thin Solid Film，2002，416：169-173 [7] Ahn S J，Kwon H S．Diffusivity of point defects in the passive film on Fe [J]．Electroanal. Chem.，2005, 579: 311-319 [8] Buchler M，Schmuki P，Bohni H．A light reflectance technique for thickness measurement of passive films [J]．Electrochim. Acta，1997，43(5-6)：635-637 [9] Horowitz G．Capacitance-voltage measurements and flat-band potential determination on Zr-doped α-Fe₂O₃ single-crystal electrodes[J]．Electroanal. Chem.，1983，159：421-436 [10] Bellucci F，Nicodemo L，Monetta T，et al. A study of corrosion initiation on polyimide coatings [J]．Corros.Sci.，1992，33(8)：1203-1226 [11] Li J B, Zheng M S, Zhu J W.Semiconductive properties of passive film formed on 304L stainless steel [J]. Corros. Sci. Prot. Technol., 2006, 18(5): 348-352 (李金波，郑茂盛，朱杰武．304L不锈钢钝化膜半导体性能研究 [J]．腐蚀科学与防护技术，2006，18(5)：348-352) [12] Cheng X Q, Li X G, Du C W. Passive film formed and semiconductive properties of 316L and 2205 stainless steel in acetic acid solution [J]. Chin. Sci. Bull., 2009, 54(1): 104-109 (程学群，李晓刚，杜翠薇．316L和2205不锈钢在醋酸溶液中钝化膜的生长及其半导体属性研究 [J]．科学通报，2009，54(1)：104-109)

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3]	张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[4]	严少坤,郑大江,韦江,宋光铃,周廉. 钝性纯Ti在人工海水中的电化学活化行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[5]	丰涵,宋志刚,吴晓涵,李惠,郑文杰,朱玉亮. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 138-144.
[6]	刘东,向红亮,刘春育. 含Ag抗菌双相不锈钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[7]	刘明,程学群,李晓刚,卢天健. 低合金钢筋在水泥萃取液中钝化膜的耐蚀机理研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[8]	廖梓含, 宋博, 任泽, 何川, 陈旭. X70钢及其焊缝在Na₂CO₃+NaHCO₃溶液中电化学腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 158-166.
[9]	李广宇, 雷明凯. γ_Ν相在硼酸溶液中钝化膜的组成及其半导体特性研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 47-53.
[10]	严寒, 赵晴, 杜楠, 胡彦卿, 王力强, 王帅星. 镀锌层三价铬钝化成膜过程及耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 547-553.
[11]	王彦亮,陈旭,王际东,宋博,范东升,何川. 316L不锈钢在不同pH值硼酸溶液中的电化学行为研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 162-167.
[12]	张天翼,吴俊升,郭海龙,李晓刚. 模拟海水中HSO₃^-对2205双相不锈钢钝化膜成分及耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 535-542.
[13]	张建春,蒋金洋,李阳,施锦杰,左龙飞,王丹芊,麻晗. 耐海水腐蚀钢筋00Cr10MoV在模拟混凝土孔隙液中钝化膜的研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 441-449.
[14]	吴欣强,付尧,柯伟,徐松,冯兵,胡波涛,陆佳政. 高氮奥氏体不锈钢的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(3): 197-204.
[15]	孟向楠,陈旭,吴明,赵阳,范裕文. 静水压力对X100钢在NaHCO₃+NaCl溶液中电化学行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(3): 219-224.

Viewed

Full text

Abstract

Cited

Shared

Discussed