己内酰胺精制薄膜蒸发器腐蚀失效分析

吴俊升; 李晓刚; 公铭扬; 李磊; 王博

北京科技大学腐蚀与防护中心

Corrosion failure analysis of thin-film evaporator for caprolactam production

;;;;

北京科技大学腐蚀与防护中心

全文: PDF(383 KB)

摘要: 用光学显微镜、扫描电镜和能谱分析等技术分析己内酰胺精制用薄膜蒸发器腐蚀减薄器壁的化学成分、金相组织、腐蚀形貌和腐蚀产物。结果表明：蒸发器内壁减薄主要是由于高速液膜流体所造成的有机酸冲刷腐蚀所致，装置提量后加剧了腐蚀减薄的速度。通过电化学极化测量304L、316、321三种不锈钢在酸性己内酰胺介质中的耐蚀性进行了比较，证实316不锈钢的耐冲刷腐蚀性能较好。

关键词 ：己内酰胺, 薄膜蒸发器, 有机酸, 冲刷腐蚀

Abstract：This paper mainly analyses the cause and principle of the failure of thin - film evaporator unit for purification processes in producing caprolactam. The device was forced to shutdown because of the decrease of wall thickness from 13.00 mm to 6.58 mm. The results of microstructrue and chemical composition analysis showed the failed component is eligible 304L stainless steel. By means of scanning electron microscopy it was found that there were corrosion ditches along the line of liquid flow and loose corrosion prduction layer on the surface of inner wall. Energy spectrum analysis showed the selective dissolution of elements Fe , Ni resulted in enrichment of Cr in the thinner corrosion production layer. According to the results of sample analysis and investigation of the operating conditions, it is confirmed that erosion - corrosion caused by high - speed liquid film containing organic acid is the main cause of the failure of the inner wall, and the corrosion thinned rate was accelerated after improving processing capacity. Moreover, corrosion resistance of stainless steels 304L,316,321 in acidic caprolactam solution was analyzed by potentiodynamic polarization curve measurement. It was confirmed that 316 stainless steel possessed better corrosion resistance to liquid flow.

Key words： caprolactam thin-film evaporation organic acid erosion-corrosion

收稿日期: 2005-11-25

ZTFLH:

TG172。8

通讯作者: 吴俊升 E-mail: wujs76@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	吴俊升
	李晓刚
	公铭扬
	李磊
	王博
44.8K

引用本文:

吴俊升; 李晓刚; 公铭扬; 李磊; 王博 . 己内酰胺精制薄膜蒸发器腐蚀失效分析[J]. 中国腐蚀与防护学报, 2007, 27(3): 181-185 .

链接本文:

https://www.jcscp.org/CN/Y2007/V27/I3/181

[1]Corrosion and Protection Team of Device.The Chinese ManagementSociety of Petrochemical Equipment.The Handbook of Corrosion andProtection of Petrochemical Equipment[M].Beijing:China Petro-chemical Press,1996,617(中国石油化工设备管理协会设备防腐专业组.石油化工装置设备腐蚀与防护手册[M].北京:中国石化出版社,1996,617)
[2]Stainless Steel Branch of Chinese Enterprise Society of Special Steel.The Handbook of Stainless Steel[M].Beijing:China Science andTechnology Press,2003,236(中国特钢企业协会不锈钢分会编.不锈钢实用手册[M].北京:中国科学技术出版社,2003,236)
[3]Lei L C,Liang HY,Xu Y X,et al.Naphthenic acid corrosion in pe-troleum processing[J].Corros.Prot.,2001,22(7):287-290(雷良才,梁红玉,徐永祥等.石油加工中的环烷酸腐蚀[J].腐蚀与防护,2001,22(7):287-290)
[4]Wu X Q,Jing HM,Zheng Y G,et al.Study on corrosion and erosion-corrosion behaviors of carbon steel in naphthenic acid mediums athigh temperatures[J].J.Chin.Soc.Corros.Prot.,2002,22(5):257-263(吴欣强,敬和民,郑玉贵等.碳钢在高温环烷酸介质中冲刷腐蚀行为[J].中国腐蚀与防护学报,2002,22(5):257-263)
[5]Wang R,He X H.Simulation of fluid flowof an agitated thin-filmevaporator[J].J.Nanjing Univ.Technol.,2004,26(1):72-77(汪蕊,贺小华.薄膜蒸发器内流体流动模拟[J].南京工业大学学报,2004,26(1):72-77)
[6]Jing HM,Wu X Q,Zheng Y G,et al.Effect of Mo content on thecorrosion and erosion-corrosion of stainless steel in oil containingnaphthenic acid[J].Acta Metall.Sin.,2002,38(10):1067-1073(敬和民,吴欣强,郑玉贵等.Mo含量对不锈钢在环烷酸介质中腐蚀与冲蚀的影响[J].金属学报,2002,38(10):1067-1073)
[7]Si Z P,Chen WY.Application of316Lstainless steel in vacuumdis-tillation[J].Petrochem.Corros.Prot.,2000,17(4):29-33(司兆平,陈文有.316L钢在减压塔中的应用[J].石油化工腐蚀与防护,2000,17(4):29-33)

[1]	胡宗武, 刘建国, 邢蕊, 尹法波. 单相流条件下90°水平弯管冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 115-122.
[2]	王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[3]	姜爱国,张建文,辛亚男,丛晓明,董轼. 加氢裂化空冷器管束多相流冲刷腐蚀数值模拟[J]. 中国腐蚀与防护学报, 2019, 39(2): 192-200.
[4]	魏木孟,杨博均,刘洋洋,王孝平,姚敬华,高灵清. Cu-Ni合金管海水冲刷腐蚀研究现状及展望[J]. 中国腐蚀与防护学报, 2016, 36(6): 513-521.
[5]	彭文山,曹学文. 固体颗粒对液/固两相流弯管冲蚀作用分析[J]. 中国腐蚀与防护学报, 2015, 35(6): 556-562.
[6]	刘贵群, 郑玉贵, 姜胜利, 荆军航, 董伟娟, 曾宏, 司品宪. 模拟炼油环境中Q235钢和Cr5Mo钢表面硫化物膜稳定性及动态冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(2): 122-128.
[7]	周婷婷, 袁成清, 曹攀, 王雪君, 董从林. 柴油机喷油嘴内流体冲刷腐蚀的数值模拟分析[J]. 中国腐蚀与防护学报, 2014, 34(6): 574-580.
[8]	李强, 唐晓, 李焰. 冲刷腐蚀研究方法进展[J]. 中国腐蚀与防护学报, 2014, 34(5): 399-409.
[9]	朱娟, 张乔斌, 陈宇, 张昭, 张鉴清, 曹楚南. 冲刷腐蚀的研究现状[J]. 中国腐蚀与防护学报, 2014, 34(3): 199-210.
[10]	乔岩欣,刘飞华,任爱,姜胜利,郑玉贵. 高氮钢和321不锈钢的冲刷腐蚀行为[J]. 中国腐蚀与防护学报, 2012, 32(2): 141-145.
[11]	杨根柱,李庆华,刘国帅,王博,刘杰,熊金平,何少平,陆正良. W0714己内酰胺薄膜蒸发器下料管管壁腐蚀减薄失效分析[J]. 中国腐蚀与防护学报, 2011, 31(6): 488-492.
[12]	李守彪, 许立坤,沈承金,李相波. 等离子喷涂耐冲蚀陶瓷涂层的性能研究[J]. 中国腐蚀与防护学报, 2011, 31(3): 196-201.
[13]	金威贤雒娅楠宋诗哲. 金属材料实海冲刷腐蚀检测[J]. 中国腐蚀与防护学报, 2008, 28(6期): 337-340.
[14]	王志武; 原素芳 . 黄铜HSn70-1A、HA177-2A的抗冲刷能力比较研究[J]. 中国腐蚀与防护学报, 2005, 25(3): 179-182 .
[15]	吴欣强; 敬和民; 郑玉贵 . 碳钢在高温环烷酸介质中冲刷腐蚀行为[J]. 中国腐蚀与防护学报, 2002, 22(5): 257-263 .

Viewed

Full text

Abstract

Cited

Shared

Discussed