NaCl盐膜对CuCr合金高温腐蚀行为的影响

中国腐蚀与防护学报

2005, Vol. 25

Issue (5): 291-294

研究报告

本期目录 | 过刊浏览

NaCl盐膜对CuCr合金高温腐蚀行为的影响

李秋荣;王丽敏

燕山大学环境与化学工程学院

Effect of NaCl Deposit on the Corrosion Behavior of CuCr Alloy at 700℃～900℃

Qiurong Li;Limin Wang

燕山大学环境与化学工程学院

全文: PDF(158 KB)

摘要: 用金相、X射线衍射(XRD)、扫描电镜/能谱(SEM/EDX)及热重分析法研究了NaCl盐膜对CuCr合金在700℃～900℃下的腐蚀行为的影响.结果表明：CuCr合金在NaCl盐膜下比在单独空气中发生更严重的腐蚀，其腐蚀产物疏松且易剥落，Cr相较Cu易腐蚀，且在腐蚀区以下的合金基体中有贫铬现象.讨论了在该环境下变形对CuCr合金腐蚀的影响及NaCl加速CuCr合金腐蚀作用的机制.

关键词 ： NaCl, CuCr合金, 腐蚀

Abstract：The effect of NaCl deposit on the corrosion behavior of CuCr alloy at 700℃～900℃ was studied by means of metalloscope,XRD,SEM/EDX and thermogravimety.Results indicated that CuCr alloy coated with NaCl deposit suffered from seriously corrosion than in single air; the corrosion production was loose and easy to scale off; and Cr phase was easier to be eroded than Cu phase,and chromium depletion is developed in the matrix of alloy beneath the corrosion region.Effect of deformation on the corrosion of the CuCr alloy were discussed,and acceleration mechanisms of NaCl on the corrosion of CuCr alloy were also discussed.

Key words： NaCl CuCr alloy corrosion

收稿日期: 2004-04-16

ZTFLH:

TG174.44

通讯作者: 李秋荣 E-mail: qiurong@ysu.edu.cn

Corresponding author: Qiurong Li E-mail: qiurong@ysu.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李秋荣
	王丽敏
44.8K

引用本文:

李秋荣; 王丽敏 . NaCl盐膜对CuCr合金高温腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2005, 25(5): 291-294 .
Qiurong Li, Limin Wang. Effect of NaCl Deposit on the Corrosion Behavior of CuCr Alloy at 700℃～900℃. J Chin Soc Corr Pro, 2005, 25(5): 291-294 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I5/291

[1]Slade P G.Advances in material development for high power vacu-um interrupter contacts[J].IEEE Trans on CPMT,1994,17(1):96-106
[2]Chiang K T.Hot gas erosion resistance of a vapor-deposited Cu-Cr coating[J].Surf.Coat.Technol.,1999,114:1-6
[3]Walter R J,Chiang K T.Creep of uncoated and Cu-Cr coatedNARloy-Z[J].Mater.Sci.Eng.,1999,A263:8-14
[4]Fu G Y,Niu Y,Wu W T.Corrosion of Cu-Cr alloys in H2-H2Smixture[J].Chin.J.Nonfer.Metals,2001,11(4):562-565(付广艳,牛焱,吴维.Cu-Cr合金在H2-H2S混合气中的腐蚀行为[J].中国有色金属学报,2001,11(4):562-565)
[5]Zhang Chengyu,Wang Jiang,Zhang Hui,et al.Deoxidization of Cu-Cr25 alloys prepared by vacuum induction melting[J].Trans.Non-ferrous Met.Soc.China,2001,11(3):337-339
[6]Chiang K T,Ampaya J P.Oxidation kinetics of Cu-30vol.%Crcoating[J].Surf.Coat.Technol.,1996,78:243-247
[7]Fu G Y,Niu Y,Wu W T,et al.Oxidation of two-phase Cu-Cralloys with different microstructures[J].Trans.Nonferrous Met.Soc.China,2001,11(3):233-236
[8]Liang Y J,Che Y C.The Manual of Thermodynamic Data of Min-eral[M].Shenyang:Northeastern University Press,1993(梁英教,车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,1993)
[9]Shu Y H,Wang F H,Wu W T.Effect of NaCl deposit and watervapor on the corrosion behavior of pure Cr at 500~700℃[J].J.Chin.Soc.Corros.Prot.,2000,20(2):88-94(舒勇华,王福会,吴维.NaCl盐膜和水蒸气对纯Cr腐蚀行为的影响[J].中国腐蚀与防护学报,2000,20(2):88-94)
[10]Li Y S,Niu Y,Wu W T.Corrosion behavior of pure Cr and two Cr-containing alloys beneath ZnCl2and KCl-ZnCl2deposits[J].J.Chin.Soc.Corros.Prot.,2002,22(1):27-31(李远士,牛焱,吴维.纯Cr和两种含Cr合金在ZnCl2及KCl-ZnCl2盐膜下的腐蚀[J].中国腐蚀与防护学报,2002,22(1):27-31)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed