碳钢和耐侯钢在北京城市大气环境中初期腐蚀行为

林翠;李晓刚;刘晓东

北京科技大学材料学院腐蚀与防护中心

THE INITIAL STAGE OF ATMOSPHERIC CORROSION OF CARBON AND WEATHERING STEEL IN BEIJING CITY ATMOSPHERE

Cui Lin;;

北京科技大学材料学院腐蚀与防护中心

全文: PDF(292 KB)

摘要: 对碳钢和耐候钢在北京城市大气中的初期腐蚀行为进行了研究.主要采用金相、扫描电镜、X-射线衍射方法分析和探讨了初期腐蚀层形貌、腐蚀产物和合金元素的分布.结果表明：在腐蚀初期，耐候钢表面生成的锈层较碳钢致密，裂纹和孔洞相对较少；25?d后碳钢和耐候钢局部都出现了分层现象，腐蚀产物没有区别，差别主要是锈层中合金元素的作用.耐候钢锈层中有Cu、Cr合金元素的析出，聚集在裂纹处可抵御大气中水气及其有害离子的侵入，防止基体金属进一步腐蚀.

关键词 ：北京大气环境, 碳钢, 耐候钢, 初期腐蚀, 合金元

Abstract：This paper focuses on the initial corrosion behavior of carbon and weathering steel.The surface morphology of corrosion layer,corrosion products,structure and alloy elements of rust layer in natural city atmosphere were studied by metallographic observation,SEM and XRD.The results show that the rust layer of weathering steel was a little denser than that of carbon steel at the initial corrosion period.Two layers partly formed in both carbon and weathering steel after 25 days,there was no essential difference of corrosion products in both of them.The ifference in rust layer was mainly due to the function of alloy elements.Cu,Cr elements were found in rust layer of weathering steel.They were concentrated in the cracks and voids,which prevented water,oxygen and pollutants penetrating to the steel substrate.

Key words： Beijing city atmosphere carbon steel weathering steel atmospheric corrosion alloy elements

收稿日期: 2004-04-06

ZTFLH:

TG172.3

通讯作者: 林翠 E-mail: Lincui@soun.com

Corresponding author: Cui Lin E-mail: Lincui@soun.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	林翠
	李晓刚
	刘晓东
44.8K

引用本文:

林翠; 李晓刚; 刘晓东 . 碳钢和耐侯钢在北京城市大气环境中初期腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(4): 193-199 .
Cui Lin. THE INITIAL STAGE OF ATMOSPHERIC CORROSION OF CARBON AND WEATHERING STEEL IN BEIJING CITY ATMOSPHERE. J Chin Soc Corr Pro, 2005, 25(4): 193-199 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I4/193

[1]HouWT,LiangCF.Economicweatheringsteel[J].J.Ironand SteelResearch,1994,6(2):40-46(侯文泰,梁采凤.经济耐候钢[J].钢铁研究学报,1994,6(2):40-46)
[2]WangCY,QiZF.Chemicalcompositionandpropertyofatmo sphericcorrosionresistantsteels[J].SpecialSteel,1997,18(1):13-19(王传雅,戚正风.耐候钢的化学成分和性能[J].特殊钢,1997,18(1):13-19)
[3]AhmedZ,Al-SulaimanFA.Corrosionofcarsineasterncoastalen vironmentofsaudiarabia[J].Br.Corros.J.,1993,28(2):112-116
[4]LengQM,FuGH,ZhaoRM.Experimentalresearchonatmo sphericcorrosionresistantsteelusedincar[J].SteelResearch,1989,(2):41-49(冷启明,傅国洪,赵润鸣.汽车用耐大气腐蚀钢的试验研究[J].钢铁研究,1989,(2):41-49)
[5]OeschS.TheeffectofSO2,NO2andO3onthecorrosionofunal loyedcarbonsteelandweatheringsteel-theresultsoflaboratory exposures[J].Corros.Sci.,1996,38(8):1357-1368
[6]SuzukiI,HidamatsuY.Natureofatmosphericrustoniron[J].J.Electrochem.Soc.,1980,127(10):2210-2215
[7]WangGY,WangHJ,LiXL,etal.CorrosionandProtectionof NaturalEnvironment-Atmosphere·SeaWater·Soil[M].Beijing:ChemicalIndustryPress,1997(王光雍,王海江,李兴濂等编著.自然环境的腐蚀与防护-大气·海水·土壤[M].北京:化学工业出版社,1997)
[8]ZhangQC,WuJS,WangJJ,etal.Corrosionbehaviorofweather ingsteelinmarineatmosphere[J].MaterialsChemistryand Physics,2002,77:603-608

[1]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[2]	王帅,刘新宽,刘平,陈小红,李伟,马凤仓,何代华,张珂. Sn、Al对无镍白铜耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 45-50.
[3]	许萍,张硕,司帅,张雅君,汪长征. EPS的主要成分-蛋白质、多糖抑制碳钢腐蚀机理研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 176-184.
[4]	钟显康,扈俊颖. 恒定的pH值和Fe²⁺浓度下X65碳钢的CO₂腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[5]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[6]	乔越, 朱志平, 杨磊, 刘志峰. 高温状态下锅炉给水氧化还原电位监测与模拟实验研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[7]	彭晚军, 丁纪恒, 陈浩, 余海斌. 生物基缓蚀剂糠醇缩水甘油醚的缓蚀性能及机理[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[8]	钱备, 刘成宝, 宋祖伟, 任俊锋. 纳米容器改性环氧涂层对Q235碳钢的防腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.
[9]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[10]	王越, 刘子利, 刘希琴, 章守东, 田青超. 热轧态Cr、Ni微合金化高强度耐候钢组织与耐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(1): 39-46.
[11]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[12]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[13]	程庆利,陶彬,刘栓,刘全桢,张卫华,田松柏,王立平. 原油沉积水对Q235B碳钢的腐蚀影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 126-134.
[14]	张飘飘,杨忠民,陈颖,王慧敏. 含铬耐候钢在模拟海洋大气环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(2): 93-100.
[15]	郝永胜,Luqman Abdullahi SANI,宋立新,徐国宝,葛铁军,方庆红. 中性和酸性溶液中Q235碳钢表面沉积植酸转化膜的耐蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.

Viewed

Full text

Abstract

Cited

Shared

Discussed