土壤中碳钢平均腐蚀速度统计特征的分形研究

翁永基;李相怡

北京石油大学

FRACTAL STUDY ON STATISTICAL CHARACTERISTICS OF AVERAGE CORROSION RATE OF CARBON STEEL IN SOILS

;

北京石油大学

全文: PDF(160 KB)

摘要: 碳钢/土壤腐蚀是一种复杂的随机现象，采用概率统计法不能获得很多这类腐蚀的信息.将这种腐蚀看作分形体系，引入分维修正因子来定量描述腐蚀随机性的复杂程度.通过讨论平均腐蚀速度的统计特性，证实无论平行(重复)试验还是区域土壤腐蚀试验，平均腐蚀速度数据均服从正态分布，并具备分形体系的二个基本特征：稳定分维值和变异系数的自相似性.这些特征值表明，区域土壤腐蚀试验数据的复杂程度要高于平行试验.

关键词 ：碳钢, 土壤腐蚀, 分形理论, 平均腐蚀速度, 变异

Abstract：Corrosion of carbon steel in soils is very complex and random.The information about this type corrosion could not be obtained completely by traditional methods of the probability and statistics.In the present paper,the corrosion was regarded as a fractal system,and the complexity level of the corrosion was quantitatively described by conception of fractal dimensions.After the statistical characteristics of average corrosion rates were discussed,it was proved that the data of average corrosion rates obeyed normal distribution both from the parallel or repeated tests and from the corrosion tests in local soil region.They had two typical features of fractal systems,namely stable fractal dimension,and the self comparability in variation coefficient of random variable.Based on these features,the complexity level from corrosion tests in local soil region was higher than that from repeated corrosion tests.

Key words： carbon steel rosion rate coefficient of variation soil corrosion fractal theory average corrosion

收稿日期: 2004-02-23

ZTFLH:

TG172.4

通讯作者: 翁永基

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	翁永基
	李相怡
44.8K

引用本文:

翁永基; 李相怡 . 土壤中碳钢平均腐蚀速度统计特征的分形研究[J]. 中国腐蚀与防护学报, 2005, 25(4): 200-204 .
. FRACTAL STUDY ON STATISTICAL CHARACTERISTICS OF AVERAGE CORROSION RATE OF CARBON STEEL IN SOILS. J Chin Soc Corr Pro, 2005, 25(4): 200-204 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I4/200

[1]ZhangJZ.Fractal[M].Beijing:TsinghuaUniversityPress,1995,1-7:138(张济忠.分形[M].北京:清华大学出版社,1995,1-7:138)
[2]WengYJ.Astudyonpredictionofsoilcorrosivitybymeansofpat ternrecognition[A].11thICCProceedings[C].ITALY,1990,5:171-178
[3]WengYJ,LiXY.Thepatternrecognitionmethodsinenvironmen talcorrosionscience[J].Corros.Sci.Prot.Technol.,1994,6(2):153-158(翁永基,李相怡.环境腐蚀研究模式识别方法[J].腐蚀科学与防护技术,1994,6(2):153-158)
[4]ChinaNationalSoilCorrosionTestOrganization.Testmethodsfor materialcorrosioninsoils[M].Beijing:SciencePress,1990:1-7(全国土壤试验网站,材料土壤腐蚀试验方法[M].北京:科学出版社,1990:1-7)
[5]WengYJ,LiXY,YangJP.AstudyonsoilcorrosionmodelsinDa-gangoilfield[J].ActaPetroleiSinica,1996,17(3):137-144(翁永基,李相怡,杨建平,大港油田土壤腐蚀模型研究[J].石油学报,1996,17(3):137-144)
[6]WengYJ.SurveyofsoilcorrosivityatTarimregionandstudyon steel-soilcorrosionmodels[A].CICCC’99Proceedings[C].Bei jing,1999:41-46
[7]DNVRP-G101.Riskbasedinspectionofoffshoretopsidestatic mechanicalequipment[S].DetNorskeVeritas,2002:9-20
[8]WengYJ.Designforthesoilcorrosiontest[J].Corros.Sci.Prot.Technol.,1991,3(2):17-24(翁永基.土壤腐蚀试验的设计按排[J].腐蚀科学与防护技术,1991,3(2):17-24)
[9]WengYJ.Distributioncharacteristicsofcorrosiondataofregional soiltests,A.Characterizationofprobabilitydistribution[J].Corros.Sci.Prot.Technol.,2002,14(5):249-252(翁永基.区域土壤腐蚀数据分布特征研究:A概率特征[J].腐蚀科学与防护技术,2002,14(5):249-252)
[10]WengYJ.Distributioncharacteristicsofcorrosiondataofregional soiltests,B.Characterizationofpositiondistribution[J].Corros.Sci.Prot.Technol.,2002,14(5):253-256(翁永基.区域土壤腐蚀数据分布特征研究:B位置特征[J].腐蚀科学与防护技术,2002,14(5):253-256)

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[3]	朱亦晨,刘光明,刘欣,裴锋,田旭,师超. 红壤地区接地材料现场埋样与加速腐蚀实验的相关性研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 550-556.
[4]	许萍,张硕,司帅,张雅君,汪长征. EPS的主要成分-蛋白质、多糖抑制碳钢腐蚀机理研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 176-184.
[5]	钟显康,扈俊颖. 恒定的pH值和Fe²⁺浓度下X65碳钢的CO₂腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[6]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[7]	乔越, 朱志平, 杨磊, 刘志峰. 高温状态下锅炉给水氧化还原电位监测与模拟实验研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[8]	彭晚军, 丁纪恒, 陈浩, 余海斌. 生物基缓蚀剂糠醇缩水甘油醚的缓蚀性能及机理[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[9]	钱备, 刘成宝, 宋祖伟, 任俊锋. 纳米容器改性环氧涂层对Q235碳钢的防腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.
[10]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[11]	于利宝, 闫茂成, 王彬彬, 舒韵, 许进, 孙成. 酸性土壤环境中Q235钢的微生物腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 10-17.
[12]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[13]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[14]	程庆利,陶彬,刘栓,刘全桢,张卫华,田松柏,王立平. 原油沉积水对Q235B碳钢的腐蚀影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 126-134.
[15]	郝永胜,Luqman Abdullahi SANI,宋立新,徐国宝,葛铁军,方庆红. 中性和酸性溶液中Q235碳钢表面沉积植酸转化膜的耐蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.

Viewed

Full text

Abstract

Cited

Shared

Discussed