45#钢表面TiO2晶膜的制备、结构及性能研究

齐公台;温敏

华中科技大学化学系应用化学教研室

PREPARATION AND PROPERTIES OF TiO2 COATINGS FOR 45# STEEL

Gongtai Qi;Min Wen;

华中科技大学化学系应用化学教研室

全文: PDF(182 KB)

摘要: 以Ti（OBU）4为前驱体，通过溶胶凝胶法在45#钢表面制备TiO2晶膜。用FTIR研究了80℃、400℃、600℃下得到的干凝胶的特性，用DTA/TG、XRD、AFM等手段研究了涂膜制备时由凝胶向玻璃态的转变以及涂膜的显微结构，用动电位极化曲线评估了涂膜样品的电化学腐蚀行为。结果表明，400℃、600℃制得的涂膜为锐钛矿型的TiO2晶膜且有较好的耐腐蚀性能。

关键词 ： 45#钢, 溶胶-凝胶, TiO2, 电化学腐蚀

Abstract：With Ti(OBu)4 as precursor, TiO2 coatings were prepared on the surface of 45# steel by sol - gelmethod. The structure of xerogels dried at 80℃,400℃,600℃ were studied by FTIR,the results showed that there were not organic components in dry xerogels at all.The transition from gel to glass of coatings were investigated by TG/DTA and xrd,the results indicated that TiO2 transformed from noncrystalline to anatase at 548℃, and TiO2 crystal dried at 600℃ was more integrated than that dried at 400℃.The microstructure of coatings was studied by AFM,the results indicated that the films were integrated and compact.The electrochemical corrosion of coatings were evaluated through potential dynamic polarization curves,the results showed anticorrosion of the coatings dried at 400℃ and 600℃ were good.

Key words： 45# steel sol-gel TiO2 electrochemical corrosion

收稿日期: 2003-07-07

ZTFLH:

TG174

通讯作者: 齐公台

Corresponding author: Gongtai Qi

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	齐公台
	温敏
44.8K

引用本文:

齐公台; 温敏 . 45#钢表面TiO2晶膜的制备、结构及性能研究[J]. 中国腐蚀与防护学报, 2005, 25(1): 57-60 .
Gongtai Qi, Min Wen. PREPARATION AND PROPERTIES OF TiO2 COATINGS FOR 45# STEEL. J Chin Soc Corr Pro, 2005, 25(1): 57-60 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I1/57

[1]VanovaT ,HarizanovaA .CharacterizationofTiO2 andTiO2-MnOoxidespreparedbysol-gelmethod[J].SolidStateIonics,2001,138:227-232
[2]Legrand-BuscemaC ,MalibertC ,BachS .Elaborationandcharac terizationofthinfilmofTiO2 preparedbysol-gelprocess[J].ThinSolidFilm,2002,418:79-84
[3]LiHB ,LiangKM ,MeiLF ,etal.Corrosionprotectionofmildsteelbysol-gelzirconiacoatings[J].Corros.Sci.Proct.Technol.,2002,14(2):92-94(李海滨,梁开明,梅乐夫等.溶胶_凝胶法制备的ZrO2涂层对低碳钢腐蚀的防护[J].腐蚀科学与防护技术,2002,14(2):92-94)
[4]LiC ,ZhouYY ,HuangMZ .PreparingandcharacteristicsofSiO2-TiO2-ZrO2 coating[J].Mater.Prot.,2002,35(5):7-9(李澄,周一扬,黄明珠.SiO2-TiO2-ZrO2系涂层的制备及其特性[J].材料保护,2002,35(5):7-9)
[5]ZhouXF ,ZhuDB ,LinCJ.NanocrystallineTiO2 coatingforstainlessanditscorrosionresistance[J].Mater.Prot.,2002,35(7):4-5(周幸福,诸道葆,林昌健.不锈钢表面纳米TiO2膜的制备及其耐蚀性能[J].材料保护,2002,35(7):4-5)
[6]FanEH .Preparationofnoncrystallinecoatingforthesurfaceofmetalmaterialbysol-gel[J].Corros.Prot.,1996,(5):217(范恩华.用溶胶-凝胶法制备金属材料表面非晶涂层[J].腐蚀与防护,1996,(5):217)
[7]YuB ,LiangKM ,GuSR ,etal.Studyonanti-corrosionperfor manceofthinsol-gel-derivedfilmsonthesurfaceofcopperalloy[J].Mater.Prot.,2001,34(12):12-13(俞冰,梁开明,顾守仁等.铜合金表面溶胶-凝胶涂层抗腐蚀性能的研究[J].材料保护,2001,34(12):12-13)
[8]HarizanovO ,IvanovaT ,HarizanovaA .Studyofsol-gelTiO2 andTiO2-MnOobtainedfromapeptizedsolution[J].Mater.Lett.,2001,49:165-171
[9]ToshikazuNishide,FujioMizukami.PreparationandpropertiesofTiO2-SiO2(1:1)filmspreparedbyacomplexingagent-assistedsol-gelprocess[J].ThinSolidFilms,1997,298:89-91
[10]SureshC ,BijuV ,MukundanP ,etal.Anatasetorutiletransforma tioninsol-geltitaniabymodificationofprecursor[J].Polyhedron,1998,(17,18):3231-3135

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[3]	施远,金洙吉,姜冠楠,刘作涛,周忠正,王泽北. YG15硬质合金电化学腐蚀机理研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 253-259.
[4]	王凯, 易耀勇, 卢清华, 易江龙, 江泽新, 马金军, 张宇. 基于窄间隙焊接的热模拟峰值温度对Q690高强钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(5): 447-454.
[5]	宋博强,陈旭,马贵阳,刘睿. SRB对X70管线钢在近中性pH溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(3): 212-218.
[6]	汪家梅,陆辉,段振刚,张乐福,孟凡江,徐雪莲. 模拟压水堆二回路水环境中温度对690合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(2): 113-120.
[7]	睢文杰,赵文杰,张星,秦立光,彭叔森,乌学东,薛群基. 铜合金表面巯基官能有机硅溶胶-凝胶涂层中TEOS含量对其防腐性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(1): 52-58.
[8]	张山,周丽娜,简璐,王煦. 聚苯胺/TiO₂/环氧涂层的制备及耐蚀性研究[J]. 中国腐蚀与防护学报, 2016, 36(1): 59-66.
[9]	张宁,孙虎元,孙立娟,刘栓. X80管线钢在滨海滩涂土壤模拟液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(4): 339-344.
[10]	尹成勇, 李澄, 彭晓燕, 王加余, 王艳慧, 郑顺丽, 李敏, 胡玮. 溶胶-凝胶法制备超疏水性纳米复合防腐涂层[J]. 中国腐蚀与防护学报, 2014, 34(3): 257-264.
[11]	刘光明, 杨晓东, 林继月, 田继红. Al₂O₃/有机硅/SiO₂杂化涂层电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2013, 33(6): 527-531.
[12]	梁平, 王莹. 覆有短期腐蚀产物膜的X80钢的电化学行为[J]. 中国腐蚀与防护学报, 2013, 33(5): 371-376.
[13]	张雨，王均，石树坤，王院生. 时效对2205双相不锈钢在硫环境下的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2012, 32(6): 496-500.
[14]	林继月, 刘光明,陈刚. DDS含量对有机硅/SiO₂杂化涂层性能的影响[J]. 中国腐蚀与防护学报, 2011, 31(2): 116-120.
[15]	鲍玉胜; 王玮; 尹衍升; 赵文元; 张玥; 房晶瑞; 梁亮; 王敏 . TiO2薄膜在海水中的耐腐蚀性能[J]. 中国腐蚀与防护学报, 2008, 28(5): 287-290 .

Viewed

Full text

Abstract

Cited

Shared

Discussed