预污染处理对碳钢大气腐蚀的影响

万晔;严川伟;史志明

中科院金属腐蚀与防护研究所

INVESTIGATION OF ATMOSPHERIC CORROSION OF CARBON STEELS PRE-CORRODED BY DIFFERENT POLLUTANTS

Ye Wan;Chuanwei Yan;Zhiming Shi

中科院金属腐蚀与防护研究所

全文: PDF(159 KB)

摘要: 通过对北京和江津曝露站3个钢种的预污染样品大气腐蚀失重数据及北京曝露站腐蚀产物组成的分析，讨论了不同污染预处理对碳钢大气腐蚀的影响. 结果表明：曝露1年和2年的碳钢在江津地区的腐蚀速率均远远高于北京的腐蚀速率；不同污染预处理对3种碳钢后期腐蚀的影响有所差异，但差别不大，其中NO2预污染处理对这3种碳钢的影响最大；尽管预污染气氛不同，曝露时间不同，但腐蚀产物具有相似的结构，而且主要都由α型羟基氧化铁和γ型羟基氧化铁组成.

关键词 ：污染物, 预处理, 碳钢, 大气腐蚀, 腐蚀产物

Abstract：The atmospheric corrosion data of three kinds of pr e-corroded carbon steels at Beijing and Jiangjin exposure sites are studied.The characterizations of the corrosion products formed on the samples at Beijing exp osure site have been studied by FTIR and XRD.The results show that the corrosion rates of carbon steels at Jiangjin site are much greater than that at Beijing s ite under the same condition; the pre-corroded means have made some small differ ences to the kinetics behaviors of three kinds of carbon steels，but they have n o difference to the corrosion phases of carbon steels after exposure over one ye ar.The effects of different pre-corroded means on the atmospheric corrosion of c arbon steels are analyzed.

Key words： pollutant pre-corrosion carbon steel atmospheric co rrosion corrosion product

收稿日期: 2002-01-10

ZTFLH:

TG172.3

通讯作者: 万晔

Corresponding author: Ye Wan

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	万晔
	严川伟
	史志明
44.8K

引用本文:

万晔; 严川伟; 史志明 . 预污染处理对碳钢大气腐蚀的影响[J]. 中国腐蚀与防护学报, 2003, 23(4): 227-230 .
Ye Wan, Chuanwei Yan, Zhiming Shi. INVESTIGATION OF ATMOSPHERIC CORROSION OF CARBON STEELS PRE-CORRODED BY DIFFERENT POLLUTANTS. J Chin Soc Corr Pro, 2003, 23(4): 227-230 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I4/227

[1]RickettBI ,PayerJH .Compositionofcoppertarnishproductsformedinmoistairwithtracelevelsofpollutantgas:sulfurdioxideandsulfurdioxide/nitrogendioxide[J].J.Electrochem.Soc.,1995,142(11):3713-3719
[2]AilorWH .AtmosphericCorrosion[M ].NewYork:JohnWileyandSons,1982.8
[3]BalbaudF ,SanchezG ,FauvetP ,SantariniG ,etal.MechanismofcorrosionofAISI 304Lstainlesssteelinthepresenceofnitricacidcondensates[J].Corros.Sci.,2000,42:1685-1707
[4]ShastryCR ,FrielJJ ,TownsndHE .Degradationofmetalsinat mosphere[J].ASTMSTP965,1988.5
[5]WanYe,ShiZM ,YanCW ,CaoCN .Effectofthedifferentpre-rustedmethodsontheatmosphericcorrosionbehaviorofcarbonsteel[J].Chin.J.Mater.Res.,2002,16(1):27-30(万晔,史志明,严川伟,曹楚南.预处理对碳钢大气腐蚀的影响[J].材料研究学报,2001,16(1):27-30)
[6]MisawaT ,AsamiK ,HshimotoK ,etal.Themechanismofatmo sphericrustingandtheprotectiveamorphousrustonlowalloysteel[J].Corros.Sci.,1974,14:279-285
[7]YamashitaM ,MiyukiH ,MatsudaY ,etal.Thelongtermgrowthoftheprotectiverustlayerformedonweatheringsteelbyatmo sphericcorrosionduringaquarterofacentury[J].Corros.Sci.,1994,36(2):288-299
[8]RamanA ,KubanB ,RazvanA .Theapplicationofinfraredspec troscopytothestudyofatmosphericrustsystems-I.standardspectraandillustrativeapplicationstoidentifyrustphasesinnaturalatmosphericcorrosionproducts[J].Corros.Sci.,1991,32(12):1295-1306
[9]WuJG .TechniquesandApplicationsofInfraredFourierTrans formSpectroscopy[M ].Beijing:ScienceandTechnologyInforma tionPress,SecondVolume,1994:271(吴瑾光.近代傅立叶变换红外光谱技术及应用[M ].北京:科学技术文献出版社(下卷),1994:271)
[10]NyquistRA ,KagelRO .InfraredSpectraofInorganicCompounds[M].NewYorkandLondon:AcademicPress,1971:219
[11]MarcoJF ,GraciaM ,GancedoJR ,etal.Characterizationofthecorrosionproductsformedoncarbonsteelafterexposuretotheopenatmosphereintheantarcticandeasterisland[J].Corros.Sci.,2000,42:753-771
[12]NishimuraT ,KatayamaH ,NodaK ,etal.Electrochemicalbehaviorofrustformedoncarbonsteelinawet/dryenvironmentcontainingchlorideions[J].Corrosion,2000,56(9):935-941
[13]TianYE ,JinL ,WangXH .Changingregulationsofmeteorologi calfactorsoftheatmosphericcorrosiontestsitesinChina[J].Cor ros.Sci.Prote.Technol.,1995,7(3):196(田月娥,金蕾,汪学华.我国大气腐蚀实验站气象因数变化规律[J].腐蚀科学与防护技术,1995,7(3):196)
[14]LiuGR ,LuZX ,LiuGB .TheHandbookofCorrosionandProtec tion[M ].Beijing:ChemicalIndustryPress,1987,66(刘国瑞,陆志兴,刘桂彬.腐蚀与防护手册[M ].北京:化学工业出版社,1987,66)

[1]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[2]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[3]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[4]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[5]	邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[6]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[7]	许萍,张硕,司帅,张雅君,汪长征. EPS的主要成分-蛋白质、多糖抑制碳钢腐蚀机理研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 176-184.
[8]	钟显康,扈俊颖. 恒定的pH值和Fe²⁺浓度下X65碳钢的CO₂腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[9]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[10]	乔越, 朱志平, 杨磊, 刘志峰. 高温状态下锅炉给水氧化还原电位监测与模拟实验研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[11]	彭晚军, 丁纪恒, 陈浩, 余海斌. 生物基缓蚀剂糠醇缩水甘油醚的缓蚀性能及机理[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[12]	钱备, 刘成宝, 宋祖伟, 任俊锋. 纳米容器改性环氧涂层对Q235碳钢的防腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.
[13]	偶国富, 赵露露, 王凯, 王宽心, 金浩哲. 10^#碳钢在HCl-H₂O环境中的露点腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[14]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[15]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.

Viewed

Full text

Abstract

Cited

Shared

Discussed