丙烯酸聚氨酯涂料防腐蚀性能研究

中国腐蚀与防护学报

2003, Vol. 23

Issue (2): 89-91

研究报告

本期目录 | 过刊浏览

丙烯酸聚氨酯涂料防腐蚀性能研究

刘斌;李瑛;林海潮;曹楚南

中国科学院金属研究所;金属腐蚀与防护国家重点实验室

STUDY ON THE ANTI-CORROSION PERFORMANCE OF ACRYLIC-POLYURETHANE COATINGS BY EIS

Bin Liu;Ying Li;Haichao Lin;Chunan Cao

中国科学院金属研究所;金属腐蚀与防护国家重点实验室

全文: PDF(125 KB)

摘要: 利用电化学阻抗谱(EIS)，研究了对添加不同颜料体积浓度( PVC)TiO2的丙烯酸聚氨酯涂料的防腐蚀性能.实验结果表明，PVC为40%的涂层具有最优的防腐蚀性能.

关键词 ：丙烯酸聚氨酯涂料, 防腐蚀性能, EIS

Abstract：Acrylic-polyurethane coatings have been successfull y used in many places,such as marine environment and automobile industry for the ir excellent protective property.The anti-corrosion performance of acrylic-polyu rethane coatings with TiO2 at different pigment volume concentration(PVC) has been studied by electrochemical impedance spectroscopy(EIS).Experimental results showed that,PVC of TiO2 had remarkable effect on the anti-corrosion propertie s of acrylic-polyurethane coatings.Within the PVC value that had been studied,40 % PVC coating had the best anti-corrosion performance.

Key words： acrylic-polyurethane coatings anti-corrosion performan ce EIS

收稿日期: 2002-01-13

ZTFLH:

TG174.41

通讯作者: 刘斌

Corresponding author: Bin Liu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘斌
	李瑛
	林海潮
	曹楚南
44.8K

引用本文:

刘斌; 李瑛; 林海潮; 曹楚南 . 丙烯酸聚氨酯涂料防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2003, 23(2): 89-91 .
Bin Liu, Ying Li, Haichao Lin, Chunan Cao. STUDY ON THE ANTI-CORROSION PERFORMANCE OF ACRYLIC-POLYURETHANE COATINGS BY EIS. J Chin Soc Corr Pro, 2003, 23(2): 89-91 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I2/89

[1]　LiuBin,LiYing,LinHaichao,CaoChu′nan.EffectofPVConthediffusingbehaviorofwaterthroughalkydcoatings[J].ActaPhysi co-ChimicaSinica,2001,17(3):241(刘斌,李瑛,林海潮,曹楚南.颜料体积浓度对水在醇酸涂层中传输行为的影响[J].物理化学学报,2001,17(3):241)
[2]　LiuBin,LiYing,LinHaichao,CaoChu′nan.Studyonthediffus ingbehaviorofwaterthroughepoxycoatingsbyEIS[J].J.Chi neseSocietyforCorrosionandProtection,2002,22(3):172-175(刘斌,李瑛,林海潮,曹楚南.用EIS研究水在环氧涂层中的传输行为[J].中国腐蚀与防护学报,2002,22(3):172-175)
[3]　HaruyamaS ,AsariM ,TsuruT .Corrosionprotectionbyorganiccoatings[A].KendingMW ,LeidheiserH .TheElectrochemicalSocietySoftboundProceedingsSeries[C].Pennington,NJ :1987,197.
[4]　HackHP ,ScullyJR .Defectareadeterminationoforganiccoatedsteelsinseawaterusingthebreakpointfrequencymethod[J].J .Electrochem.Soc.,1991,138(1):33
[5]　ZhangJianqing,MansfeldF .EvaluationoforganiccoatingsbyEIS[J].Corros.Sci.Prote.Technol.,1989,1(3):15(张鉴清,MansfeldF .交流阻抗评价有机涂层[J].腐蚀科学与防护技术,1989,1(3):15)
[6]　LiuHongwei,LiangFeng,ZhangJiangqing,etal.Investigationofeffectofaluminum powderonperformanceofepoxycoatingsbybreakpointfrequencymethod[J].Corros.Sci.Prote.Technol.,1992,4(3):144(刘宏伟,梁峰,张鉴清等.交流阻抗特征频率法评价添加铝粉对有机涂层防护性能的影响[J].腐蚀科学与防护技术,1992,4(3):144)

[1]	常亮, 师超, 邵亚薇, 王艳秋, 刘斌, 孟国哲. 植酸转化膜对环氧清漆防腐性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 265-273.
[2]	蔡光义,王浩伟,赵苇杭,董泽华. 添加纳米CeO₂对聚氨酯涂层防腐性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(5): 411-420.
[3]	郝永胜,Luqman Abdullahi SANI,宋立新,徐国宝,葛铁军,方庆红. 中性和酸性溶液中Q235碳钢表面沉积植酸转化膜的耐蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.
[4]	刘艳洁,王振尧,柯伟. 纯Al在3种典型沿海,工业和乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(1): 47-51.
[5]	周兵, 唐囡, 张颖君, 毛亮, 王艳秋, 邵亚薇, 孟国哲. 镀锌钢表面高附着环氧清漆的研究[J]. 中国腐蚀与防护学报, 2015, 35(5): 455-460.
[6]	杨霜,唐囡,闫茂成,赵康文,孙成,许进,于长坤. 温度对X80管线钢酸性红壤腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2015, 35(3): 227-232.
[7]	郑敏聪, 李建华, 聂新辉, 李博文, 台闯. 镀锌钢接地材料在酸性土壤中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(1): 27-32.
[8]	元辛, 岳珠峰, 温世峰, 李磊. 铝合金表面有机硅环氧涂层的腐蚀电化学行为[J]. 中国腐蚀与防护学报, 2014, 34(4): 375-381.
[9]	朱敏, 杜翠薇, 李晓刚, 刘智勇, 李月强, 黄亮. Cu在北京土壤环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2013, 33(4): 306-310.
[10]	苏景新白云关庆丰邹阳. 飞机蒙皮结构表面涂层失效的电化学阻抗分析[J]. 中国腐蚀与防护学报, 2013, 33(3): 251-256.
[11]	朱敏杜翠薇李晓刚刘智勇姚文涛黄亮. Q235钢在北京土壤环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2013, 33(3): 199-204.
[12]	李喜明金哲刘五铸孙成张洪伟许进闫茂成于长坤王振尧. 尿素对土壤中Q235钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2013, 33(3): 216-220.
[13]	金伟良,岳增国,许晨,李志远. 混凝土中钢筋脱钝氯离子阈值的快速测定[J]. 中国腐蚀与防护学报, 2012, 32(3): 223-227.
[14]	蔡健平,刘明,安英辉. 铝合金防护涂层老化动力学研究[J]. 中国腐蚀与防护学报, 2012, 32(3): 256-261.
[15]	闫瑞霞,杜翠薇,刘智勇,李晓刚. 敏化态00Cr12Ti的动电位电化学阻抗谱特征研究[J]. 中国腐蚀与防护学报, 2011, 31(6): 419-425.

Viewed

Full text

Abstract

Cited

Shared

Discussed