含稀土元素的Mg-Al合金在NaCl溶液中腐蚀产物膜的研究

中国腐蚀与防护学报

2002, Vol. 22

Issue (3): 167-171

研究报告

本期目录 | 过刊浏览

含稀土元素的Mg-Al合金在NaCl溶液中腐蚀产物膜的研究

黄亮;黄元伟;王晨

上海市中科院上海冶金所

STUDY ON CORROSION PRODUCT FILM OF MAGNESIUM-ALUMINUM ALLOYS CONTAININGRARE-EARTH ELEMENT IN NaCl SOLUTION

Liang Huang;Yuanwei` Huang;Chen Wang

上海市中科院上海冶金所

全文: PDF(170 KB)

摘要: 利用多种表面分析手段比较研究了纯Mg和Mg-8Al、Mg-8Al-R E等镁铝合金在Mg(OH )2饱和的35％NaCl溶液中的腐蚀产物膜的形貌及结构.发现Al元素的加入使镁合金表面形成含Mg、Al的复杂氧化物，有利于提高镁合金耐腐蚀性.稀土元素RE的加入有利于提高Al 元素在氧化膜中的含量，形成具有三层结构的产物膜，进一步提高了Mg-Al合金的耐腐蚀性.

关键词 ： Mg-Al合金, NaCl溶液, 腐蚀产物膜, 稀土元素

Abstract：The corrosion resistance of magnesium-aluminum allo ys is closely related to the corrosion product film formed on the alloy's surfac e.The morphology and structure of the corrosion product film on pure Mg,Mg-Al  and Mg-Al-RE alloys in the solution containing Cl\+- were examined by the var ious sur face analysis techniques including EMPA,EDS,SEM,TEM,XRD,AES etc.The results indi cated that the elemental aluminum is conducive to the corrosion resistance of al loys,but its beneficial effect is limited and unstable.The RE addition can obvi ously increase the Al concentration in corrosion product film.Also,the distribut i on of Al in corrosion product film of Mg-Al-RE alloys was broadened due to the a dd ition of RE.It indicated that the RE element promoted the formation of protectiv e film containing elemental Al.

Key words： Mg-Al alloy NaCl solution corrosion product film rare earth element

收稿日期: 2000-11-03

ZTFLH:

TG174

通讯作者: 黄亮

Corresponding author: Liang Huang

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	黄亮
	黄元伟
	王晨
44.8K

引用本文:

黄亮; 黄元伟; 王晨 . 含稀土元素的Mg-Al合金在NaCl溶液中腐蚀产物膜的研究[J]. 中国腐蚀与防护学报, 2002, 22(3): 167-171 .
Liang Huang, Yuanwei` Huang, Chen Wang. STUDY ON CORROSION PRODUCT FILM OF MAGNESIUM-ALUMINUM ALLOYS CONTAININGRARE-EARTH ELEMENT IN NaCl SOLUTION. J Chin Soc Corr Pro, 2002, 22(3): 167-171 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I3/167

[1]OttoLunder,MavianneVidern,KemalNisancioglu.CorrosionRe sistantMagnesiumAlloys[A].950428,MagnesiuminVehicleDesign,SAEInternationalSP -1096[C].1995
[2]OttoLunder,LeinJE ,AuneTKr,NisanciogluKemal.TheroleofMg17Al12 phaseinthecorrosionofMgalloyAZ91[J].Corrosion,1989,45(9):741-748
[3]MercerWE ,HillsJE .ThecriticalcontaminantlimitandsaltwatercorrosionperformanceofmagnesiumAE42alloy[A].SAETechni calpaper.No.920073[C].1992
[4]NakatsugawaI ,KamadoS ,KojimaY ,NinomiyaR ,KubotaK .Cor rosionofmagnesiumalloyscontainingrareearthelements[J].Cor rosionReviews,1998,139-158
[5]LunderO ,NisanciogluK ,HansenRS .Corrosionofdiecastmagne siumaluminumalloys[A].SAETechnicalpaperNo.930755[C].SocietyofAutomotiveEngineers,1993
[6]JanHalvorNordlien,SachilkoOno,NoburoMasuko.Morphologyandstructureofoxidefilmsformedonmagnesiumbyexposuretoairandwater[J].J.Electrochem.Soc.,1995,142(10):3320-3322

[1]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[2]	黄博博,刘平,刘新宽,梅品修,陈小红. 新型HSn70-1铜网衣两年期海水腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
[3]	王海媛, 卫英慧, 杜华云, 刘宝胜, 郭春丽, 侯利锋. 绿色缓蚀剂SDDTC对AZ31B镁合金的缓蚀作用及吸附行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 62-67.
[4]	鲍明昱, 任呈强, 胡静思, 刘博, 李佳蒙, 王丰, 刘丽, 郭小阳. 油气管材应力诱导腐蚀电化学行为探讨[J]. 中国腐蚀与防护学报, 2017, 37(6): 504-512.
[5]	陈振宁,陈日辉,潘金杰,滕艳娜,雍兴跃. L921A钢在3.5%NaCl溶液中的有机/无机复配缓蚀剂研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.
[6]	朱敏,袁永锋,刘俊,聂轮,周健. Incoloy825合金在不同温度3.5%NaCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(6): 631-636.
[7]	张弟,梁平,张云霞,史艳华,秦华. 库尔勒土壤模拟溶液中形成的腐蚀产物膜对X80钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(4): 313-320.
[8]	董洋洋, 黄峰, 程攀, 胡骞, 刘静. X65 MS耐酸管线钢在H₂S环境中腐蚀产物膜的演变[J]. 中国腐蚀与防护学报, 2015, 35(5): 386-392.
[9]	杨海, 陆卫中, 李京, 孙超. 环氧粉末涂层在1.5 mol/L NaCl溶液中的失效行为[J]. 中国腐蚀与防护学报, 2014, 34(4): 382-388.
[10]	梁平, 王莹. 覆有短期腐蚀产物膜的X80钢的电化学行为[J]. 中国腐蚀与防护学报, 2013, 33(5): 371-376.
[11]	苏义祥,鲍艳东,廖乃飞,侯凤刚,代英秋. Te-Ni-Cr合金在3.5%NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2011, 31(6): 462-466.
[12]	俞芳高克玮路民旭. 流动状态下X65管线钢CO₂腐蚀产物膜结构和力学性能的评价[J]. 中国腐蚀与防护学报, 2009, 29(6): 401-404.
[13]	李桐; 高克玮; 路民旭 . X65钢CO2腐蚀产物膜形成机理研究[J]. 中国腐蚀与防护学报, 2007, 27(6): 338-341 .
[14]	马文海; 裴晓含; 高飞; 高纯良 . N80钢在模拟深层气井水溶液中的CO2腐蚀行为[J]. 中国腐蚀与防护学报, 2007, 27(1): 8-13 .
[15]	张卫国; 李; 林; 姚素薇; 郑国钦 . 纳米炭黑改性涂料在NaCl溶液中的耐蚀机理研究[J]. 中国腐蚀与防护学报, 2005, 25(6): 351-355 .

Viewed

Full text

Abstract

Cited

Shared

Discussed